TIJOLOS TEMPERADOS DE MAGNéSIA CROMO: RESULTADO DE TESTES EM CLIENTES

TEMPERED MAGNESIA CHROME REFRACTORY BRICK: CUSTOMERS TRIALS PERFORMANCE

DOI

10.5151/2594-5300-34685

Downloads

Baixar Artigo 12 Downloads

Resumo

O DESGASEIFICADOR RH VEM SENDO UTILIZADO PARA A PRODUÇÃO DE AÇOS DE ULTRA-BAIXO CARBONO. REAÇÕES COMPLEXAS ENTRE AÇO, GÁS, ESCORIA E INCLUSÕES DOS REFRATARIOS ESTÃO ENVOLVIDAS NO PROCESSO. AS CONDIÇÕES OPERACIONAIS CRÍTICAS AUMENTARAM A DEMANDA DE PRODUTOS REFRATÁRIOS COM DESEMPENHO SUPERIOR. GERALMENTE AS DIFERENTES PARTES DO DESGASEIFICADOR RH SÃO REVESTIDAS COM DIFERENTES LINHAS DE TIJOLOS DE MAGNÉSIA CROMO (MGO-CR2O3). OS TIJOLOS DE LIGA DIRETA SÃO OS MAIS UTILIZADOS DESDE 1960 E SÃO CONHECIDOS POR SUA RESISTÊNCIA À CORROSÃO, ESTABILIDADE VOLUMÉTRICA E ELEVADAS PROPRIEDADES MECÂNICAS. A LIGAÇÃO DIRETA ENTRE OS GRÃOS AUMENTA COM A PRESENÇA DE SIO2 ABAIXO DE 3WT.% E TEMPERATURAS ATÉ 1700 ° C. A BUSCA DE NOVAS ROTAS TECNOLÓGICAS MAIS SUSTENTÁVEIS COM REDUÇÃO DE ENERGIA E EMISSÕES DE GASES POLUENTES É A FORÇA MOTRIZ DA INDÚSTRIA. PORTANTO, UM NOVO SISTEMA LIGANTE PARA TIJOLOS DE MGO-CR2O3 FOI DESENVOLVIDO PARA ATENDER ÀS SEVERAS DEMANDAS DO DESGASEIFICADOR RH, MAS APENAS TEMPERADO A 200 ° C. A CAPACIDADE DE SINTERIZAÇÃO RÁPIDA PERMITE QUE ESTA TECNOLOGIA SEJA SEMELHANTE AO PRODUTO QUEIMADO. ESTE TRABALHO TEM COMO OBJETIVO A AVALIAÇÃO COMPARATIVA DE PROPRIEDADES FÍSICAS, MECÂNICAS, CORROSÃO E RESISTÊNCIA A CHOQUE TÉRMICO DOS NOVOS TIJOLOS DE MGO-CR2O3 TEMPERADOS COM O PRODUTO QUEIMADO. O DESEMPENHO DOS TESTES EM CLIENTE TAMBÉM SÃO APRESENTADOS.

 

RH DEGASSER HAS BEEN WIDELY USED TO PRODUCE ULTRA-LOW CARBON STEEL. IT INVOLVES COMPLEX REACTIONS BETWEEN MOLTEN STEEL, GAS, SLAG AND INCLUSIONS FROM REFRACTORY. THE CRITICAL OPERATIONAL CONDITIONS HAVE BEEN INCREASED THE DEMAND FOR REFRACTORY PRODUCTS WITH SUPERIOR PERFORMANCE. USUALLY VARIOUS PARTS OF THE RH DEGASSER ARE LINED WITH DIFFERENT GRADES OF MAGNESIA CHROME (MGO-CR2O3) BRICKS. DIRECT BONDED BRICKS ARE MOSTLY USED SINCE 1960S AND THEY ARE KNOWN TO THEIR CORROSION RESISTANCE, VOLUME STABILITY AND HIGH MECHANICAL PROPERTIES. THE BONDING BETWEEN THE GRAINS IS ENHANCED WITH SIO2 CONTENT BELOW 3WT.% AND TEMPERATURES UP TO 1700°C. THE SEARCH FOR NEW ENVIRONMENTALLY FRIENDLY PROCESS WITH LESS ENERGY DEMANDS AND A REDUCTION IN POLLUTION EMISSIONS IS THE DRIVING FORCE OF THE INDUSTRY. SO, A NEW BINDER SYSTEM FOR MGO-CR2O3 BRICKS WAS DEVELOPED TO ATTEND THE SEVERE DEMANDS FOR RH DEGASSERS BUT JUST DELIVERED TEMPERED AT 200°C. FAST SINTERING CAPABILITY ALLOW THIS TECHNOLOGY PERFORMING SIMILAR TO THE FIRED PRODUCT. THIS WORK PRESENTS THE COMPARATIVE EVALUATION OF PHYSICAL AND MECHANICAL PROPERTIES, CORROSION AND THERMAL SHOCK RESISTANCE OF THE NOVEL TEMPERED MGO-CR2O3 BRICKS WITH THE HIGH TEMPERATURE FIRED PRODUCTS. CUSTOMERS’ PERFORMANCES IN FIELD TRIALS ARE ALSO HIGHLIGHTED.

Palavras-chave

Desgaseificador RH, ULTRA-BAIXO CARBONO, RH Degasser; Ultra-low carbon; MgO-Cr2O3; TEMPERADO

RH Degasser; Ultra-low carbon; RH Degasser; Ultra-low carbon; MgO-Cr2O3; Tempered

Como citar

Melo, Barbara Luiza Borges; Neto, Carlos Pagliosa; Campos, Adão Adelcio; Santos, Marcelo Borges; Avila, Haylander Coelho De; Verona, Mauro Lucio Resende; Madalena, Vanderlúcio Geraldo. TIJOLOS TEMPERADOS DE MAGNéSIA CROMO: RESULTADO DE TESTES EM CLIENTES , p. 517-530. In: 51° Seminário de Fusão, Refino e Solidificação de Metais, São Paulo, 2022.