TRATAMENTO BIOTECNÓLOGICO DO RESÍDUO DE BAUXITA: AVALIAÇÃO  COMO MATERIAL CIMENTÍCIO SUPLEMENTAR: TREATMENT OF BAUXITE WASTE FROM FILTER PRESS VIA BIOGEN SULFURIC ACID FOR USE AS SUPPLEMENTARY CEMENTITIVE MATERIAL

A CRESCENTE GERAçãO DE RESíDUOS INDUSTRIAIS é UM DESAFIO GLOBAL, EXIGINDO SOLUçõES INOVADORAS. SETORES, COMO CONSTRUçãO CIVIL E MINERAçãO NECESSITAM DE ESTRATéGIAS PARA O REUSO DE SUBPRODUTOS. NA CONSTRUçãO CIVIL, A PRODUçãO DE CIMENTO PORTLAND, EM SEU PROCESSO DE CLINQUERIZAçãO Há EMISSãO DE DIóXIDO DE CARBONO (CO2), CONTRIBUINDO PARA O EFEITO ESTUFA. NA MINERAçãO, Há UMA URGêNCIA EM REDUZIR A QUANTIDADE DE RESíDUOS SUBUTILIZADOS. PORTANTO, PROPõE-SE O USO RESíDUO DE BAUXITA (RB) PóS-TRATAMENTO VIA ROTA BIOTECNOLóGICA, PARA APLICá-LO COMO MATERIAL CIMENTíCIO SUPLEMENTAR. O PRé-TRATAMENTO DO RB EMPREGOU ÁCIDO SULFúRICO BIOGêNICO, PRODUZIDO POR BACTéRIAS DO GêNERO ACIDITHIOBACILLUS THIOOXIDANS. OS RESULTADOS OBTIDOS INDICARAM UMA REDUçãO DO PH DO RB DE 11 PARA 7,4 COM USO DE áCIDO BIOGêNICO, COM PERMANêNCIA DOS MINERAIS. NA AVALIAçãO DO MATERIAL CIMENTíCIO SUPLEMENTAR, ONDE UTILIZOU-SE 25% DO RB TRATADO COM áCIDO BIOGêNICO EM SUBSTITUIçãO AO CLíNQUER, OBSERVOU-SE UM AUMENTO DA RESISTêNCIA à COMPRESSãO DE 9% NO PRIMEIRO DIA EM COMPARAçãO COM A REFERêNCIA, ATINGINDO 35MPA AOS 28 DIAS. CONCLUI-SE, PORTANTO, QUE O USO DESTE PRODUTO TEM POTENCIAL DE UTILIZAçãO EM ESTRUTURAS DE BAIXA NECESSIDADE DE CARGA, ALéM DE RESULTAR NA REDUçãO DE UMA PARCELA SIGNIFICATIVA DOS RESíDUOS SUBUTILIZADOS E DE EMISSãO DE DIóXIDO DE CARBONO.

THE INCREASING GENERATION OF INDUSTRIAL WASTE IS A GLOBAL CHALLENGE, REQUIRING INNOVATIVE SOLUTIONS. SECTORS SUCH AS CONSTRUCTION AND MINING NEED STRATEGIES FOR REUSING BY-PRODUCTS. IN CONSTRUCTION, THE PRODUCTION OF PORTLAND CEMENT DURING THE CLINKERIZATION PROCESS EMITS CARBON DIOXIDE (CO2), CONTRIBUTING TO THE GREENHOUSE EFFECT. IN MINING, THERE IS AN URGENT NEED TO REDUCE UNDERUTILIZED WASTE. THEREFORE, USING POST-TREATMENT BAUXITE RESIDUE (BR) VIA A BIOTECHNOLOGICAL ROUTE IS PROPOSED AS A SUPPLEMENTARY CEMENTITIOUS MATERIAL. THE PRE-TREATMENT OF BR WAS DONE USING BIOGENIC SULFURIC ACID, PRODUCED BY ACIDITHIOBACILLUS THIOOXIDANS BACTERIA. THE RESULTS SHOWED A REDUCTION IN BR PH FROM 11 TO 7.4 WITH BIOGENIC ACID, WHILE MINERALS REMAINED INTACT. IN EVALUATING THE SUPPLEMENTARY CEMENTITIOUS MATERIAL, USING 25% BR TREATED WITH BIOGENIC ACID, A 9% INCREASE IN COMPRESSIVE STRENGTH WAS OBSERVED ON THE FIRST DAY COMPARED TO THE REFERENCE, REACHING 35MPA AT 28 DAYS. IT IS CONCLUDED THAT THIS PRODUCT IS FEASIBLE FOR STRUCTURES WITH LOW LOAD REQUIREMENTS, SIGNIFICANTLY REDUCING UNDERUTILIZED WASTE AND CO2 EMISSIONS.

Palavras-chave

Cimento Portland; Resíduo de Bauxita; Ácido Sulfúrico Biogênico; Material Cimentício Suplementar

Portland Cement; Bauxite Residue; Biogenic Sulfuric Acid; Additional Cementitious Material.

Como citar

GOMES, FERNANDO GAMA; SILVA, PATRICIA MAGALHÃES PEREIRA; CARMO, ANDRE LUIZ DO; MONTEIRO, DAVID MIRANDA; BARATA, MÁRCIO SANTOS; LUCHETA, ADRIANO REIS. TRATAMENTO BIOTECNÓLOGICO DO RESÍDUO DE BAUXITA: AVALIAÇÃO COMO MATERIAL CIMENTÍCIO SUPLEMENTAR , p. 273-287. In: 1º Seminário de Economia Circular e Sustentabilidade, São Paulo, Brasil, 2024.
ISSN: - , DOI 10.5151/2594-5327-41423