Título

TRATAMENTOS ALTERNATIVOS À CROMATIZAÇÃO COM CROMO HEXAVALENTE E SEUS EFEITOS NA RESISTÊNCIA À CORROSÃO DO ALUMÍNIO 1050

ALTERNATIVE TREATMENTS FOR CROMATIZATION WITH HEXAVALENT CHROMIUM AND ITS EFFECTS ON THE CORROSION RESISTANCE OF ALUMINUM 1050

Autoria

Santos, Wagner Izaltino Alves dos; Yoshikawa, Daniel Sierra; Assis, Sergio Luiz de; Costa, Isolda

DOI

10.5151/2594-5327-18374

Downloads

Baixar Artigo 42 Downloads

Resumo

O objetivo deste trabalho foi investigar a potencialidade de alguns pré-tratamentos para substituição do cromo hexavalente. Foi avaliada a resistência à corrosão de cinco tratamentos da superfície do alumínio 1050: (1) passivação à base de Cr VI, (2) passivação à base de Cr III, (3) crescimento de óxido seguido por tratamento com moléculas auto-organizáveis (SAM), (4) crescimento de óxido associado com partículas cerâmicas de zircônio e (5) crescimento de óxido associado com partículas cerâmicas de zircônio, seguido por tratamento com SAM. A resistência à corrosão das amostras tratadas foi avaliada por ensaios eletroquímicos e ensaios de névoa salina. As amostras submetidas aos ensaios de névoa salina foram divididas em três grupos: (a) amostras sem revestimento orgânico (verniz poliéster), (b) amostras com revestimento orgânico e (c) amostras com revestimento orgânico e com risco para expor o substrato. A caracterização da resistência à corrosão associada com os vários tratamentos permitiu observar que os tratamentos para crescimento de óxido seguido por tratamento com SAM e o tratamento de passivação à base de Cr III tratamentos mostraram-se alternativas em potencial para substituição do tratamento de passivação com Cr VI.

 

The objective of this study was to investigate the potentiality of some pre-treatments for replacement of hexavalent chromium. The 1050 aluminum surface was prepared by five types of surface treatments, specifically: (1) passivation based on Cr VI solution, (2) passivation based on Cr III solution (3) immersion in boiling water to favor oxide growth followed by treatment with self-assembling molecules (SAM), (4) treatment specified in (3) associated with ceramic particles of zirconium and (5) immersion in boiling water to favor oxide growth associated with ceramic particles of zirconium followed by treatment with SAM. The corrosion resistance of the surface treated samples was evaluated by electrochemical tests and salt spray tests. The samples exposed to salt spray tests were divided into three groups: (a) samples without organic coating (varnish polyester), (b) samples with organic coating and (c) samples with organic coating and scratch to expose the substrate to the corrosive environment. The characterization of the corrosion resistance associated to the various surface treatments tested showed that two of these treatments could be used for replacement of passivation with hexavalent chromium. These treatments were passivation with trivalent chromium and the treatment of immersion in boiling water for oxide growth followed by immersion in solution with self-assembling molecules.

Palavras-chave

Alumínio; Corrosão; Passivação; Tratamentos superficiais.

Aluminum; Corrosion; Passivation; Surface treatments.