O OBJETIVO DESTE TRABALHO é ANALISAR A INCORPORAçãO DE GUIMBAS DE CIGARRO (GC) TRITURADAS EM TIJOLOS CONFORMADOS POR EXTRUSãO. FORAM UTILIZADAS ARGILAS TíPICAS DE CONFECçãO DE TIJOLOS E GC DE DIFERENTES TAMANHOS E MARCAS. A COMPOSIçãO QUíMICA DAS TRêS ARGILAS FOI DETERMINADA POR FLUORESCêNCIA DE RAIO-X (FRX). AS PEçAS FORAM FEITAS NAS COMPOSIçõES DE 0%, 2,5% E 5% EM RELAçãO à MASSA E QUEIMADOS A 700 ºC, 800 ºC, 900 ºC E 1000 ºC. O íNDICE DE ABSORçãO DE áGUA, RETRAçãO LINEAR DE QUEIMA E RESISTêNCIA à COMPRESSãO FORAM VERIFICADOS. O EFEITO DA INCORPORAçãO DE GC FOI O AUMENTO DA ABSORçãO DE áGUA, EM FUNçãO DA POROSIDADE GERADA DURANTE A QUEIMA. A RESISTêNCIA A COMPRESSãO AUMENTOU COM 2,5% PARA TEMPERATURAS DE QUEIMA ACIMA DE 800ºC, COM POSTERIOR QUEDA PARA MAIORES QUANTIDADES DE RESíDUO. ASSIM, OS RESULTADOS MOSTRARAM QUE O USO DE GC EM MATRIZ CERâMICA EM QUANTIDADES DE ATé 5% EM MASSA é CAPAZ DE FORMAR POROSIDADE NAS PEçAS, TORNANDO A PEçA MAIS LEVE, ALéM DE POSSIVELMENTE DIMINUIR A CONDUTIVIDADE TéRMICA E AUMENTAR O ISOLAMENTO ACúSTICO, SENDO UMA ALTERNATIVA ECONôMICA E SUSTENTáVEL PARA A DISPOSIçãO FINAL DAS GC.
THE AIM OF THIS WORK IS TO ANALYZE THE INCORPORATION OF SHREDDED CIGARETTE BUTTS (CBS) INTO BRICKS MAKING BY EXTRUSION. TYPICAL CLAYS USED FOR MAKING BRICKS AND CBS OF DIFFERENT SIZES AND BRANDS WERE USED. THE CHEMICAL COMPOSITION OF THE THREE CLAYS WAS DETERMINED BY X-RAY FLUORESCENCE (XRF). THE SAMPLES WERE MADE IN COMPOSITIONS OF 0%, 2.5% AND 5% WT AND FIRED AT 700 ºC, 800 ºC, 900 ºC AND 1000 ºC. THE WATER ABSORPTION, LINEAR FIRING SHRINKAGE AND COMPRESSIVE STRENGTH WERE PERFORMED. THE EFFECT OF CBS INCORPORATION WAS TO INCREASE WATER ABSORPTION, DUE TO THE POROSITY GENERATED AFTER FIRING. COMPRESSIVE STRENGTH INCREASED BY 2.5% FOR FIRING TEMPERATURES ABOVE 800ºC, WITH A DECREASE FOR LARGER AMOUNTS OF WASTE. THUS, THE RESULTS SHOWED THAT THE USE OF CBS IN FIRED CLAY BRICKS IN AMOUNTS OF UP TO 5% WT IS CAPABLE OF FORMING POROSITY IN THE SAMPLES, MAKING THE PART LIGHTER, IN ADDITION TO POSSIBLY REDUCING THERMAL CONDUCTIVITY AND INCREASING ACOUSTIC INSULATION, BEING A ECONOMICAL AND SUSTAINABLE ALTERNATIVE FOR THE FINAL DISPOSAL OF CBS.
Palavras-chave
Reciclagem; Tijolos cerâmicos; Cigarros.
Recycling; Fired clay bricks; Cigarette butts.
Como citar
PAULISTA, CÁSSIO RANGEL;
DELAQUA, GEOVANA CARLA GIRONDI;
GUIMARÃES, CARLOS ALBERTO DE OLIVEIRA;
FERREIRA, PAULA MUNIER;
SILVA, MARCELO GOMES DA;
VIEIRA, CARLOS MAURÍCIO FONTES.
UMA ALTERNATIVA INOVADORA PARA O DESCARTE DE CIGARROS: INCORPORAÇÃO EM TIJOLOS CERÂMICOS
,
p. 1852-1863.
In: 77º Congresso Anual da ABM - Internacional,
São Paulo, Brasil,
2024.
ISSN: 2594-5327
, DOI 10.5151/2594-5327-40965