USING THERMOCHEMICAL EQUILIBRIA TO STUDY SLAGS OF THE CaO-SiO2-CrOx-MgO SYSTEM

USANDO EQUILÍBRIOS TERMOQUÍMICOS PARA ESTUDAR ESCÓRIAS DO SISTEMA CaO-SiO2-CrOx-MgO

Autoria

Heck, Nestor Cezar; Klug, Jeferson Leandro; Vilela, Antônio Cezar Faria

DOI

10.5151/2594-5327-16387

Downloads

Baixar Artigo 36 Downloads

Resumo

Metallurgical slags may be used – and studied – under greatly different conditions: from that of atmospheric air to the strongly reducing conditions of smelting furnaces. For chromium-containing slags, changes in oxygen pressure noticeably affect its composition, because of the multivalent oxidation states of the Cr-ions. Aim of the current paper is to evaluate the addition of periclase into slags of the system CaO- SiO2-CrOx. In order to carry out the investigation, slags of the Ca-O-Cr-Si-Mg quinary system were studied with the help of computational thermodynamics, at 1.2 binary basicity and temperature of 1600oC. Two conditions were especially motivating: chromium oxide-saturated and non-saturated slags.

 

Escórias metalúrgicas podem ser utilizadas – e estudadas – sob condições muito diferentes: desde aquela ao ar, até as fortemente redutoras, utilizadas em fornos para redução de minérios. Para escórias contendo cromo, alterações na pressão de oxigênio afetam sensivelmente a sua composição, por causa dos múltiplos estados de oxidação dos íons do cromo. O objetivo do presente trabalho é avaliar a influência da adição de periclásio em escórias do sistema CaO-SiO2-CrOx. De ordem a executar esta investigação, escórias do sistema quinário Ca-O-Cr-Si-Mg foram estudadas com a ajuda da termodinâmica computacional, com basicidade binária 1,2 e temperatura de 1.600oC. Duas condições foram especialmente interessantes: escórias saturadas com óxido de cromo e escórias insaturadas.

Palavras-chave

Slags; Stainless steel; Computational thermodynamics.

Escórias; Aços inoxidáveis; Termodinâmica computacional.