UTILIZAÇÃO DE RESÍDUOS DE QUARTZITO NA FORMULAÇÃO DE LIGANTES ATIVADOS ALCALINAMENTE: UTILIZATION OF QUARTZITE WASTE IN THE FORMULATION OF ALKALI

O APROVEITAMENTO SUSTENTáVEL DE RESíDUOS NOS PROCESSOS PRODUTIVOS MOTIVA O SEGUINTE ESTUDO QUE OBJETIVA A CARACTERIZAçãO DE UM RESíDUO FINO PROVENIENTE DA ETAPA DE CORTE DE BLOCOS DE QUARTZITO ORNAMENTAL, VISANDO SUA POSTERIOR UTILIZAçãO COMO FILLER NA PRODUçãO DE MATERIAIS ATIVADOS ALCALINAMENTE, E DETERMINAR A PROPORçãO IDEAL DA INCORPORAçãO DESSE FINO NA MISTURA DO MATERIAL A FIM DE MAXIMIZAR SUAS PROPRIEDADES MECâNICAS. REALIZOU-SE ENSAIOS DE CARACTERIZAçãO FíSICA, QUíMICA E MINERALóGICA DO MATERIAL, POSTERIORMENTE, MOLDOU-SE OS CORPOS DE PROVA UTILIZANDO A SOLUçãO ATIVADORA, COM A CONCENTRAçãO DE 6 MOLARES DE HIDRóXIDO DE SóDIO, JUNTO à UMA MISTURA DO QUARTZITO COM A ESCóRIA DE FERRO-LIGA DE MANGANêS, SENDO A MISTURA REALIZADA UTILIZANDO A METODOLOGIA ONE-PART E TWO-PART. EM SEGUIDA, FORAM REALIZADOS OS ENSAIOS DE RESISTêNCIA à COMPRESSãO E ABSORçãO A áGUA EM DIFERENTES TEMPOS DE CURA. O QUARTZITO é COMPOSTO PELOS MINERAIS MAJORITáRIOS QUARTZO, CIANITA E MUSCOVITA, SENDO 88% DE SIO₂ E 11% DE AL2O3. APRESENTA DENSIDADE ESPECíFICA DE 2,8G/CM3 E 80% DAS PARTíCULAS MENORES DO QUE 43µM. FOI POSSíVEL OBSERVAR A INFLUêNCIA DO AUMENTO DO TRAçO DE QUARTZITO, E A SUA PROPORçãO IDEAL DE 5% NA MISTURA, CONSIDERANDO A INFLUêNCIA DAS METODOLOGIAS E DOS TEMPOS DE CURA EM ENSAIOS.

THE SUSTAINABLE UTILIZATION OF WASTE IN PRODUCTION PROCESSES MOTIVATES THE FOLLOWING STUDY, WHICH AIMS TO CHARACTERIZE A FINE RESIDUE FROM THE CUTTING STAGE OF ORNAMENTAL QUARTZITE BLOCKS, WITH THE SUBSEQUENT INTENTION OF ITS USE AS A FILLER IN THE PRODUCTION OF ALKALI-ACTIVATED MATERIALS. THE STUDY ALSO SEEKS TO DETERMINE THE OPTIMAL PROPORTION FOR INCORPORATING THIS FINE RESIDUE INTO THE MATERIAL MIXTURE TO MAXIMIZE ITS MECHANICAL PROPERTIES. PHYSICAL, CHEMICAL, AND MINERALOGICAL CHARACTERIZATION TESTS OF THE MATERIAL WERE CONDUCTED, FOLLOWED BY THE MOLDING OF SPECIMENS USING AN ACTIVATING SOLUTION CONTAINING A CONCENTRATION OF 6 MOLAR SODIUM HYDROXIDE, ALONG WITH A MIXTURE OF QUARTZITE AND MANGANESE FERROALLOY SLAG. THE MIXING PROCESS WAS CARRIED OUT USING BOTH THE ONE-PART AND TWO-PART METHODOLOGIES. SUBSEQUENTLY, COMPRESSION STRENGTH AND WATER ABSORPTION TESTS WERE PERFORMED AT VARIOUS CURING TIMES. THE QUARTZITE CONSISTS PREDOMINANTLY OF QUARTZ, KYANITE, AND MUSCOVITE MINERALS, WITH 88% SIO₂ AND 11% AL2O3. IT EXHIBITS A SPECIFIC DENSITY OF 2.8G/CM3 AND 80% OF PARTICLES SMALLER THAN 43µM. THE STUDY OBSERVED THE INFLUENCE OF INCREASING THE QUARTZITE RATIO, WITH THE IDEAL PROPORTION BEING 5% IN THE MIXTURE, TAKING INTO ACCOUNT THE METHODOLOGIES AND CURING TIMES IN THE TESTS

Palavras-chave

Quartzito; Escória; Materiais ativados alcalinamente

Quartzite; Slag; Alkaline activated materials.

Como citar

BESERRA, LEONARDO HENRIQUE MENDES; COTA, TIANY GUEDES; REIS, ÉRICA LINHARES. UTILIZAÇÃO DE RESÍDUOS DE QUARTZITO NA FORMULAÇÃO DE LIGANTES ATIVADOS ALCALINAMENTE , p. 41-52. In: 1º Seminário de Economia Circular e Sustentabilidade, São Paulo, Brasil, 2024.
ISSN: - , DOI 10.5151/2594-5327-40729