Título

UTILIZAÇÃO DE UM SIMULADOR TERMOMECÂNICO PARA A AVALIAÇÃO DE DIFERENTES ESTRATÉGIAS DE LAMINAÇÃO DE UM AÇO MICROLIGADO AO NIÓBIO

USE OF A THERMALMECHANICAL SIMULATOR FOR EVALUATION OF DIFFERENT ROLLING STRATEGIES OF A NIOBIUM MICROALLOYED STEEL

Autoria

Paula, Gustavo Sales de; Souza, Altair Lucio de; Faria, Geraldo Lúcio de

Paula, Gustavo Sales de

2 Artigos, Baixados 32 Vezes

Souza, Altair Lucio de

Eu sou esse autor

Faria, Geraldo Lúcio de

Eu sou esse autor

DOI

10.5151/2594-5297-34945

Downloads

Resumo

ESTE TRABALHO TEVE COMO OBJETIVO AVALIAR O DESEMPENHO DE DIFERENTES ESTRATéGIAS DE LAMINAçãO TERMOMECâNICA DE UM AçO MICROLIGADO AO NB LAMINADO NA ESPESSURA DE 4,75 MM EM UM LAMINADOR DO TIPO STECKEL, UTILIZANDO O SOFTWARE MICROSIM®. TRêS ESTRATéGIAS DE LAMINAçãO FORAM EXECUTADAS EXPLORANDO A REDUçãO DO INTERVALO DE ESPERA ENTRE AS ETAPAS DE DESBASTE E DE ACABAMENTO, ASSIM COMO A DEFORMAçãO MáXIMA APLICADA NOS PASSES DE DESBASTE. APóS AS LAMINAçõES, SIMULAçõES COMPUTACIONAIS FORAM EXECUTADAS NO MICROSIM® E ENSAIOS MECâNICOS E ANáLISES METALOGRáFICAS FORAM REALIZADAS PARA AVALIAçãO DOS PRODUTOS OBTIDOS A PARTIR DE CADA ESTRATéGIA. FOI POSSíVEL OBSERVAR UMA BOA CORRELAçãO ENTRE OS VALORES OBTIDOS PELAS SIMULAçõES E OS RESULTADOS DAS LAMINAçõES EXPERIMENTAIS. ESTE ESTUDO MOSTROU QUE POR MEIO DA APLICAçãO DA METODOLOGIA UTILIZADA E DE UMA REDUçãO BEM PLANEJADA NO TEMPO DE ESPERA, FOI POSSíVEL AUMENTAR A PRODUTIVIDADE DO LAMINADOR EM 18% SEM PREJUíZOS à QUALIDADE DOS PRODUTOS LAMINADOS EM TERMOS MICROESTRUTURAIS E DE PROPRIEDADES MECâNICAS.

THIS WORK AIMS TO EVALUATE THE PERFORMANCE OF DIFFERENT THERMOMECHANICAL ROLLING STRATEGIES OF A NB MICROALLOYED STEEL ROLLED AT A THICKNESS OF 4.75 MM IN A STECKEL MILL USING THE MICROSIM® SOFTWARE. THREE ROLLING STRATEGIES WERE EXECUTED, EXPLORING THE REDUCTION OF THE WAITING INTERVAL BETWEEN THE STAGES OF ROUGHING AND FINISHING, AS WELL AS THE MAXIMUM DEFORMATION APPLIED IN THE ROUGHING PASSES. AFTER THE ROLLINGS, COMPUTATIONAL SIMULATIONS WERE PERFORMED IN MICROSIM® AND MECHANICAL TESTS AND METALLOGRAPHIC ANALYZES WERE MADE TO EVALUATE EACH STRATEGY. THIS STUDY SHOWED THAT BY APPLYING THE METHODOLOGY USED AND A WELL-PLANNED REDUCTION IN WAITING TIME, IT WAS POSSIBLE TO INCREASE THE MILL'S PRODUCTIVITY BY 18% WITHOUT COMPROMISING THE QUALITY OF THE ROLLED PRODUCTS IN TERMS OF MICROSTRUCTURAL AND MECHANICAL PROPERTIES.

Palavras-chave

Laminação Termomecânica; Nióbio; Simulador Termomecânico; Laminador Steckel

Thermomechanical Process; Niobium; Thermomechanical Simulator; Steckel-Mill