Título

ZrO2 ADDITION IN MOULD POWDERS: EFFECT ON HORIZONTAL HEAT TRANSFER RATE AND SEN EROSION RATE

ZrO2 ADDITION IN MOULD POWDERS: EFFECT ON HORIZONTAL HEAT TRANSFER RATE AND SEN EROSION RATE

DOI

10.5151/1982-9345-26491

Downloads

Baixar Artigo 175 Downloads

Resumo

Durante o lingotamento contínuo de aço, partículas de ZrO2 adicionadas na escória de molde facilitam a nucleação heterogênea de cristais devido à sua limitada solubilidade. A adição de ZrO2 promove a cristalização da fase cuspidina, o que auxilia na redução da transferência horizontal de calor no molde, amenizando desta forma o problema das trincas longitudinais. Outro benefício da adição de ZrO2 em pós fluxantes é reduzir a taxa de desgaste da válvula submersa (SEN) na interface metal/escória; a erosão da SEN é um problema sério. Através de testes de laboratório e de testes industriais concluiu-se que a adição de ZrO2 em pós fluxantes reduz a taxa de transferência de calor horizontal no molde durante o lingotamento contínuo de aço, considerando os dois tipos de pós fluxantes que foram analisados no presente trabalho. Além disso, observou-se que a adição de ZrO2 reduz a taxa de desgaste da válvula submersa na interface metal/escória.

 

During continuous casting of steel, it is accepted that ZrO2 particles in the mould slag act as heterogeneous nucleation sites due to its limited solubility. ZrO2 addition promotes crystallisation of cuspidine and consequently reduces horizontal heat transfer, alleviating in this way problems associated with longitudinal cracking. Another benefit when adding ZrO2 in mould powders is to reduce erosion of SENs at the slag/metal interface; SEN erosion is a serious problem. Through laboratory tests and industrials tests it was concluded that ZrO2 addition in mould powders can reduce horizontal heat transfer rate for the mould during continuous casting of steel, considering two particular mould powders which were studied in the present work. Besides, it was observed that ZrO2 addition reduces erosion of SEN at the slag/metal interface.

Palavras-chave

Lingotamento contínuo, Pó fluxante, Erosão da válvula submersa, Trinca longitudinal

Continuous casting, Mould powder, SEN erosion, Longitudinal crack

Como citar

Pereira, Márcia Maria da Silva Monteiro; Lima, Marco Túlio Dias; Filho, Carlos Berlini; Mendes, Sebastião Garcia; Ferreira, Gérson Tolentino; Jung, Detlef; Klug, Jeferson Leandro. ZrO2 ADDITION IN MOULD POWDERS: EFFECT ON HORIZONTAL HEAT TRANSFER RATE AND SEN EROSION RATE , p. 281-288. In: 46º Seminário de Aciaria - Internacional, Rio de Janeiro, 2015.
ISSN: 2594-5300 , DOI 10.5151/1982-9345-26491