CARACTERIZAÇÃO METALOGRÁFICA DE UMA LIGA MONOCRISTALINA Cu-Al-Ni

METALLOGRAPHIC CHARACTERIZATION OF THE MONOCRYSTALLINE Cu-Al- Ni ALLOY

Autoria

Cruz, Thiago de Oliveira; Matlakhov, Anatoliy Nikolaevich; Matlakhova, Lioudmila Aleksandrovna; Monteiro, Sérgio Neves

DOI

10.5151/2594-5327-0318

Downloads

Baixar Artigo 61 Downloads

Resumo

No presente trabalho, foi investigada uma liga monocristalina Cu-Al-Ni, com o efeito de memória de forma, no seu estado inicial, fabricada pela tecnologia desenvolvida pela empresa "Memory Crystals Group", na Universidade Técnica de São Petersburgo da Rússia, a fim de verificar sua estrutura, identificar a composição química e fásica, bem como medir a microdureza e densidade. Na caracterização estrutural da liga foram envolvidas a microscopia ótica e eletrônica de varredura, microanálise por EDS e a difração de raios-X. Os ensaios de microdureza Vickers foram realizados com o auxílio de um dispositivo MHP- 100 adaptado ao microscópio ótico. A densidade da liga foi medida por meio da pesagem hidrostática, bem como foi estimada com base na sua composição química, peso e tamanhos. Mostrou-se que a liga apresenta a estrutura martensítica, composta por uma série dos blocos com microdureza de 307

 

In the present work, a monocrystalline alloy of the Cu-Al-Ni system, which display shape memory effect in its initial state, was investigated. The alloy was fabricated using a technology developed by the firm “Memory Crystal Group” of the Technical University of Saint Petersburg, Russia. The investigation was carried out to evaluate the structure, to identify both the chemical and phase composition as well as to measure the microhardness and the density of the alloy. For the structural characterization of the alloy, optical and scanning electron microscopies as well as EDS microanalysis and X-ray diffraction tests were performed. Vickers microhardness was carried out in a MHP-100 device coupled with the optical microscope. The alloy density was measured by means of hydrostatic weighting and also estimated by the chemical analysis together with the size and weight of the alloy samples. It was shown that the alloy depicts a martensitic structure comprising a series of blocks with 307

Palavras-chave

Liga monocristalina Cu-Al-Ni; Estrutura; Composição; Densidade.

Monocrystalline Cu-Al-Ni alloy; Structure; Composition; Density.