COMPORTAMENTO AO IMPACTO DOS AÇOS SAE 4140 E SAE O1 SOB DIFERENTES CONDIÇÕES DE TRATAMENTO TÉRMICO: TEMPERADO E REVENIDO (COM E SEM BANHO CRIOGÊNICO) E AUSTEMPERADO: BEHAVIOR IMPACT OF SAE 4140 AND SAE O1 STEEL UNDER DIFFERENT CONDITIONS OF HEAT TREATMENT: QUENCHED AND TEMPERED (WITH AND WITHOUT BATH CRYOGENIC) AND AUSTEMPERED

Nucci, José Eduardo; Vatavuk, Jan; Canale, Lauralice de Campos Franceschini

doi:10.5151/2594-5327-23534

Anais do Congresso Anual da ABM

ISSN 2594-5327

68º Congresso da ABM — vol. 68, num.68 (2013)

Título

COMPORTAMENTO AO IMPACTO DOS AÇOS SAE 4140 E SAE O1 SOB DIFERENTES CONDIÇÕES DE TRATAMENTO TÉRMICO: TEMPERADO E REVENIDO (COM E SEM BANHO CRIOGÊNICO) E AUSTEMPERADO

BEHAVIOR IMPACT OF SAE 4140 AND SAE O1 STEEL UNDER DIFFERENT CONDITIONS OF HEAT TREATMENT: QUENCHED AND TEMPERED (WITH AND WITHOUT BATH CRYOGENIC) AND AUSTEMPERED

Autoria

Nucci, José Eduardo; Vatavuk, Jan; Canale, Lauralice de Campos Franceschini

Canale, Lauralice de Campos Franceschini

Eu sou esse autor

DOI

10.5151/2594-5327-23534

Downloads

Baixar Artigo 688 Downloads

Resumo

Estudos disponíveis na literatura sobre microestruturas martensítica e bainítica relatam que a microestrutura bainítica comparativamente à martensita revenida, apresenta melhores propriedades de impacto. No presente trabalho foi proposto o estudo de comportamento ao impacto de aços SAE 4140 e SAE O1 (VND) sob diferentes condições de tratamento térmico. Ao todo foram feitos 57 corpos Charpy de prova para cada tipo de aço divididos em 3 lotes que foram então: temperados e revenidos, com e sem banho criogênico e austemperados. A dureza final após tratamento térmico foi similar nos diferentes tratamentos térmicos. Os resultados obtidos para os dois tipos de aço mostram que os corpos de provas que passaram pelo tratamento térmico de têmpera, revenido e banho criogênico apresentaram melhor tenacidade ao impacto.

Studies available in the literature about bainitic and martensitic microstructure report that bainitic microstructure compared to tempered martensite has better impact properties. In this paper was proposed the study of the impact performance of steel SAE 4140 and SAE O1 (VND) under different conditions of heat treatment. Altogether 57 were made Charpy specimens divided into 3 batches which were then: quenched and tempered, with and without cryogenic bath and austemperados. The final hardness after heat treatment was similar in the different heat treatments. The results obtained for the two kinds of steel show that the test samples that passed through the heat treatment of quenching, tempering and cryogenic bath had better impact toughness.

Palavras-chave

Austêmpera; Têmpera; Revenido; Criogênico; Charpy.

Austemperd; Quenched; Tempered; Charpy