A CRESCENTE DEMANDA DE INSUMOS NA CONSTRUçãO CIVIL E O MANEJO INADEQUADO DOS RESíDUOS AGROINDUSTRIAIS TEM RESULTADO UM IMPACTO AMBIENTAL SIGNIFICATIVO, CONSIDERANDO QUE A CONSTRUçãO FIGURA-SE ENTRE OS SETORES MAIS POLUENTES DO MUNDO, E OS RESíDUOS AGRíCOLAS AFETAM DIRETAMENTE O ECOSSISTEMA. AS FIBRAS LIGNOCELULóSICAS PROVENIENTES DESSES RESíDUOS, TORNAM-SE UMA ALTERNATIVA PARA REFORçOS EM MATRIZES CIMENTíCIAS. ENTRETANTO, ESSAS FIBRAS SãO HIDROFíLICAS, REDUZINDO A ADESãO ENTRE A FIBRA-MATRIZ. PARA MITIGAR ESSA CARACTERíSTICA, REALIZARAM-SE TRATAMENTOS PARA VIABILIZAR SUA INCORPORAçãO NESSAS MATRIZES. ANALISARAM-SE FIBRAS DE AçAí E COCO, TRATADAS COM áCIDO TâNICO, EM ARGAMASSAS DE REVESTIMENTO. A PROPORçãO DA MISTURA FOI: 1;1;6;1,4 (CIMENTO; CAL; AREIA; áGUA), COM ADIçãO DE 3% DE FIBRAS EM RELAçãO à MASSA DO CIMENTO TRATADAS COM 5% DE CONCENTRAçãO DE áCIDO TâNICO, ALéM DA ARGAMASSA DE REFERêNCIA (0%). AVALIARAM-SE TRABALHABILIDADE, íNDICE DE PENETRAçãO, DENSIDADE DE MASSA E TEOR DE AR INCORPORADO. AS ANáLISES INDICARAM REDUçãO NA FLUIDEZ NAS ARGAMASSAS REFORçADAS COM FIBRAS E MENOR DENSIDADE, CONSIDERANDO-SE FAVORáVEL, VISTO QUE, ARGAMASSAS COM ESSE ASPECTO RESULTAM EM ESTRUTURAS MAIS LEVES. DESSA FORMA, ARGAMASSAS INCORPORADAS COM FIBRAS DE AçAí E COCO POSSUEM POTENCIAL DE APLICAçãO, SENDO NECESSáRIOS ESTUDOS ADICIONAIS DE OUTROS PARâMETROS.
THE GROWING DEMAND FOR INPUTS IN CONSTRUCTION AND THE INADEQUATE MANAGEMENT OF AGRO-INDUSTRIAL WASTE HAS RESULTED IN A SIGNIFICANT ENVIRONMENTAL IMPACT, CONSIDERING THAT CONSTRUCTION IS AMONG THE MOST POLLUTING SECTORS IN THE WORLD, AND AGRICULTURAL WASTE DIRECTLY AFFECTS THE ECOSYSTEM. LIGNOCELLULOSIC FIBERS FROM THESE WASTES BECOME AN ALTERNATIVE FOR REINFORCEMENT IN CEMENTITIOUS MATRICES. HOWEVER, THESE FIBERS ARE HYDROPHILIC, REDUCING ADHESION BETWEEN THE FIBER-MATRIX. TO MITIGATE THIS CHARACTERISTIC, TREATMENTS WERE CARRIED OUT TO ENABLE ITS INCORPORATION INTO THESE MATRICES. AçAí AND COCONUT FIBERS, TREATED WITH TANNIC ACID, WERE ANALYZED IN COATING MORTARS. THE MIXTURE PROPORTION WAS: 1;1;6;1.4 (CEMENT; LIME; SAND; WATER), WITH ADDITION OF 3% FIBERS IN RELATION TO THE MASS OF CEMENT TREATED WITH 5% CONCENTRATION OF TANNIC ACID, IN ADDITION TO REFERENCE MORTAR (0%). WORKABILITY, PENETRATION INDEX, MASS DENSITY AND ENTRAINED AIR CONTENT WERE EVALUATED. THE ANALYZES INDICATED A REDUCTION IN FLUIDITY IN MORTARS REINFORCED WITH FIBERS AND LOWER DENSITY, WHICH IS CONSIDERED FAVORABLE, SINCE MORTARS WITH THIS ASPECT RESULT IN LIGHTER STRUCTURES. THEREFORE, MORTARS INCORPORATED WITH AçAí AND COCONUT FIBERS HAVE APPLICATION POTENTIAL, REQUIRING ADDITIONAL STUDIES OF OTHER PARAMETERS.
Palavras-chave
Argamassa de revestimento; Fibra de coco; Fibra de açaí; Ácido tânico.
Coating mortar; Coconut fiber; Açaí fiber; Tannic acid.
Como citar
JÚNIOR, JOSÉ ALEXANDRE TOSTES LINHARES; COUTO, RENAN DIAS; FONSECA, LARISSA MENDONÇA OSORIO; NATALLI, JULIANA FADINI; MONTEIRO, SERGIO NEVES; PEREIRA, IULLY DA SILVA AMARAL; AZEVEDO, AFONSO RANGEL GARCEZ.
ANÁLISE COMPARATIVA DAS ARGAMASSAS DE REVESTIMENTO REFORÇADAS COM FIBRAS DE COCO E AÇAÍ,
p. 1587-1598.
In: 77º Congresso Anual da ABM - Internacional,
São Paulo, Brasil,
2024.
ISSN: 2594-5327, DOI 10.5151/2594-5327-40881