DEVIDO AO CRESCIMENTO DOS INVESTIMENTOS NO SETOR DE ENERGIA EóLICA, HOUVE UM AVANçO SIGNIFICATIVO NA UTILIZAçãO DOS MATERIAIS COMPóSITOS, O PRESENTE TRABALHO OBJETIVOU ANALISAR AS PROPRIEDADES MECâNICAS DE LAMINADOS DE MATRIZ DE RESINA EPóXI REFORçADOS COM TECIDOS DE FIBRA DE VIDRO. PARA ISSO, FORAM PRODUZIDAS PLACAS LAMINADAS DE MATRIZ DE RESINA EPóXI REFORçADOS COM TECIDOS UNIDIRECIONAIS (UD) E BIDIRECIONAIS (BIAX), UTILIZANDO O PROCESSO MODELAGEM POR TRANSFERêNCIA DE RESINA ASSISTIDA à VáCUO (VARTM). POR MEIO DE ENSAIOS DE TRAçãO A 0° E 90°, VISOU-SE AVALIAR A INFLUêNCIA DA ORIENTAçãO DO TECIDO DE FIBRA DE VIDRO NA MATRIZ DE RESINA EPóXI NO COMPORTAMENTO MECâNICO DOS LAMINADOS FABRICADOS E DETERMINAR SUAS PROPRIEDADES. OS RESULTADOS DOS ENSAIOS MOSTRARAM UMA INTENSA QUEDA NA RESISTêNCIA, EM TERMOS DO LIMITE DE RESISTêNCIA à TRAçãO (LRT) E DA TENSãO DE RUPTURA, QUANDO OS CORPOS DE PROVA DOS LAMINADOS UD FORAM SUBMETIDOS A ESFORçOS TRATIVOS NA DIREçãO PERPENDICULAR à ORIENTAçãO DAS FIBRAS. OS CORPOS DE PROVA BIAX REFORçADOS COM FIBRA DE VIDRO APRESENTARAM UM VALOR MéDIO DE LRT MUITO MENOR DO QUE AQUELES VERIFICADOS PARA AS PLACAS UD E VALORES INTERMEDIáRIOS DE TENSãO DE RUPTURA.
DUE TO THE GROWTH OF INVESTMENTS IN THE WIND ENERGY SECTOR, THERE HAS BEEN A SIGNIFICANT ADVANCE IN THE USE OF COMPOSITE MATERIALS, THE PRESENT WORK AIMED TO ANALYZE THE MECHANICAL PROPERTIES OF EPOXY RESIN MATRIX LAMINATES REINFORCED WITH FIBERGLASS FABRICS. FOR THIS, LAMINATED PLATES OF EPOXY RESIN MATRIX REINFORCED WITH UNIDIRECTIONAL (UD) AND BIDIRECTIONAL (BIAX) FABRICS WERE PRODUCED, USING THE VACUUM ASSISTED RESIN TRANSFER MODELING (VARTM) PROCESS. BY MEANS OF TENSILE TESTS AT 0° AND 90°, THE AIM WAS TO EVALUATE THE INFLUENCE OF THE ORIENTATION OF THE FIBERGLASS FABRIC IN THE EPOXY RESIN MATRIX ON THE MECHANICAL BEHAVIOR OF THE FABRICATED LAMINATES AND TO DETERMINE ITS PROPERTIES. THE RESULTS OF THE TESTS SHOWED AN INTENSE DROP IN STRENGTH, IN TERMS OF THE TENSILE STRENGTH LIMIT (LRT) AND THE TENSILE STRENGTH, WHEN THE SPECIMENS OF THE UD LAMINATES WERE SUBJECTED TO TRACTIVE FORCES IN THE DIRECTION PERPENDICULAR TO THE ORIENTATION OF THE FIBERS. THE GLASS-FIBER-REINFORCED BIAX SPECIMENS SHOWED A MUCH LOWER MEAN LRT VALUE THAN THOSE VERIFIED FOR THE UD PLATES AND INTERMEDIATE VALUES OF BREAKDOWN STRESS.
Palavras-chave
compósito laminado; fibra de vidro; ensaio de tração.
laminated composite; fiberglass; tensile test
Como citar
SANTOS, LARAH EVELY BELARMINO DOS; Caio Ramos de Menezes; SAYMON MADEIRO; BARBOSA, BRUNO DOUGLAS RODRIGUES; LIMA, FRANCISCO VICTOR ROSA DE.
ANÁLISE COMPARATIVA DE LAMINADOS DE MATRIZ DE RESINA EPÓXI REFORÇADOS COM FIBRA DE VIDRO E A INFLUÊNCIA DA ORIENTAÇÃO DA FIBRA NA RESISTÊNCIA À TRAÇÃO,
p. 3842-3854.
In: 77º Congresso Anual da ABM - Internacional,
São Paulo, Brasil,
2024.
ISSN: 2594-5327, DOI 10.5151/2594-5327-41644