A SíLICA TEM DESEMPENHADO UM PAPEL FUNDAMENTAL NO DESENVOLVIMENTO DE MATERIAIS COMPóSITOS DEVIDO àS SUAS PROPRIEDADES úNICAS E VERSATILIDADE COMO INéRCIA QUíMICA, ALTO PONTO DE FUSãO, ENTRE OUTROS, O QUE FAZ COM QUE TENHA VáRIAS POSSIBILIDADES DE APLICAçãO. ESTE ARTIGO APRESENTA UMA ANáLISE DO COMPORTAMENTO DA SíLICA NA UTILIZAçãO COMO FASE DISPERSA, COM O INTUITO DE MELHORAR SUAS PROPRIEDADES MECâNICAS PARA QUE POSSA CONTRIBUIR PARA A MELHORIA DO DESEMPENHO DOS COMPóSITOS POLIMéRICOS. ALéM DISSO, SERá DISCUTIDO O MéTODO UTILIZADO PARA A PREPARAçãO DOS CORPOS DE PROVA, INCORPORANDO DE SíLICA COMERCIAL NA FORMA DE PARTICULADOS NA MATRIZ DE EPóXI E SUA IMPLICAçãO E COMPORTAMENTO MECâNICO. FORAM CONFECCIONADOS 8 CORPOS DE PROVA DE CADA FORMULAçãO INTEGRADO A RESINA EPóXI COM UM SISTEMA DGEBA/DETA COM O PHR DE 16, O VOLUME INCORPORADO DE PARTICULADOS DE SíLICA FORAM DE 5%,10%,15% E 20%, PARA QUE SE OBTIVESSE UMA CONSISTêNCIA PASTOSA PARA POSSíVEIS APLICAçõES COMO REVESTIMENTO EM ESTRUTURAS METáLICAS. UTILIZAMOS A NORMA ASTM D790 COMO SUPORTE PARA O ENSAIO, A UMA TAXA DE 1,3 MM/MIN.
SILICA HAS PLAYED A KEY ROLE IN THE DEVELOPMENT OF COMPOSITE MATERIALS DUE TO ITS UNIQUE PROPERTIES AND VERSATILITY SUCH AS CHEMICAL INERTNESS, HIGH MELTING POINT, AMONG OTHERS, WHICH MAKES IT HAVE SEVERAL APPLICATION POSSIBILITIES. THIS ARTICLE PRESENTS AN ANALYSIS OF THE BEHAVIOR OF SILICA WHEN USED AS REINFORCEMENT, HIGHLIGHTING ITS MECHANICAL PROPERTIES TO CONTRIBUTE TO THE ENHANCEMENT OF COMPOSITE PERFORMANCE. ADDITIONALLY, THE METHOD USED FOR SAMPLE PREPARATION, THE INCORPORATION OF SILICA INTO THE POLYMERIC MATRIX, AND ITS IMPLICATIONS ON MECHANICAL BEHAVIOR WILL BE DISCUSSED. EIGHT SPECIMENS WERE FABRICATED FOR EACH FORMULATION INTEGRATED WITH EPOXY RESIN USING A DGEBA/DETA SYSTEM WITH A PHR OF 16, WITH SILICA INCORPORATION LEVELS OF 5%, 10%, 15%, AND 20%. THE ASTM D790 STANDARD WAS EMPLOYED FOR THE TEST, AT A RATE OF 1,3 MM/MIN.
Palavras-chave
Sílica; Ensaio de Flexão; Compósitos; Resina epóxi; Resistência a flexão.
Silica; Flexural test; Composites; Epoxy resin, resistance flexural.
Como citar
OLIVEIRA, JAQUELINE MOREIRA DE.
ANÁLISE COMPARATIVA EM FLEXÃO DE COMPÓSITOS EPOXÍDICOS COM PARTICULADOS DE SÍLICA,
p. 3363-3369.
In: 77º Congresso Anual da ABM - Internacional,
São Paulo, Brasil,
2024.
ISSN: 2594-5327, DOI 10.5151/2594-5327-41432