ANáLISE TERMO E DINâMICO MECâNICAS DAS FIBRAS DE JUNCO-SETE-ILHAS (CYPERUS MALACCENSIS) REVESTIDAS COM ÓXIDO DE GRAFENO REFORçANDO UMA MATRIZ EPóXI

THERMAL MECHANICAL AND DYNAMIC MECHANICAL ANALYSIS OF SEDGE FIBERS (CYPERUS MALACCENSIS) COATED BY GRAPHENE OXIDE AS A REINFORCEMENT FOR EPOXY MATRIX ABSTRACT

Autoria

DOI

10.5151/2594-5327-40556

Downloads

4 Downloads

Resumo

OS COMPóSITOS COM FIBRAS NATURAIS LIGNOCELULóSICAS (FNLS) TêM ATUALMENTE APLICAçõES EXTREMAMENTE DIVERSIFICADAS, INCLUSIVE NAS INDúSTRIAS DE ENGENHARIA, DEVIDO AO SEU MENOR CUSTO E DENSIDADE, BEM COMO à FACILIDADE DE PROCESSAMENTO. OUTRO MATERIAL NOTáVEL, O óXIDO DE GRAFENO VEM ATRAINDO CONSIDERáVEL ATENçãO POR SUAS PROPRIEDADES, PRINCIPALMENTE COMO REVESTIMENTO PARA MELHORAR A ADESãO INTERFACIAL EM COMPóSITOS POLIMéRICOS. PORTANTO, ESSA PESQUISA FOCA EM INVESTIGAR A ANáLISE DINâMICO-MECâNICA (DMA) E TERMOMECâNICA (TMA) PARA COMPóSITOS DE MATRIZ EPóXI CONTENDO 30% EM VOLUME DE FIBRA DE JUNCO CM INCORPORADA COM óXIDO DE GRAFENO. EM COMPARAçãO AO GRUPO CONTROLE (EPóXI SEM TRATAMENTO) O FATOR DE AMORTECIMENTO (TAN δ), SENDO A RAZãO DO MóDULO DA PERDA SOB O ARMAZENAMENTO, é AUMENTADA SIGNIFICATIVAMENTE DE (0.55-0.75) PARA OS COMPóSITOS REFORçADOS COM 30% DE FIBRAS DE JUNCO CM INCORPORADA COM óXIDO DE GRAFENO. A TG ENCONTRADA NO VALOR DE 127°C PARA A CONDIçãO 30 FJGO/EP APRESENTOU-SE SUPERIOR AS DEMAIS CONDIçõES DE EP, 30 FJ/EP E 30 FJ/EP-GO, ASSIM COMO O COEFICIENTE DE EXPANSãO TéRMICA (208.52 PARA 248.95 X 10−6/°C). A PERDA DE MASSA PARA A CONDIçãO 30 FJGO/EP NO PRIMEIRO ESTáGIO FOI UM POUCO SUPERIOR A CONDIçãO EP (1.63%). ESSES RESULTADOS DE DMA E TMA REVELAM SER PROMISSORES

 

COMPOSITES WITH NATURAL LIGNOCELLULOSIC FIBERS (NLFS) CURRENTLY HAVE EXTREMELY DIVERSE APPLICATIONS, INCLUDING IN ENGINEERING INDUSTRIES, DUE TO THEIR LOWER COST AND DENSITY, AS WELL AS EASE OF PROCESSING. ANOTHER NOTABLE MATERIAL, GRAPHENE OXIDE, HAS ATTRACTED CONSIDERABLE ATTENTION FOR ITS PROPERTIES, MAINLY AS A COATING TO IMPROVE INTERFACIAL ADHESION IN POLYMER COMPOSITES. THEREFORE, THIS RESEARCH FOCUSES ON INVESTIGATING THE DYNAMIC MECHANICAL (DMA) AND THERMOMECHANICAL ANALYSIS (TMA) FOR EPOXY MATRIX COMPOSITES CONTAINING 30% BY VOLUME OF CM REED FIBER INCORPORATED WITH GRAPHENE OXIDE. COMPARED TO THE CONTROL GROUP (UNTREATED EPOXY) THE DAMPING FACTOR (TAN δ), BEING THE RATIO OF THE LOSS MODULUS UNDER STORAGE, IS SIGNIFICANTLY INCREASED FROM (0.55-0.75) FOR THE COMPOSITES REINFORCED WITH 30% OF CM REED FIBERS INCORPORATED WITH GRAPHENE OXIDE. THE TG FOUND AT 127°C FOR CONDITION 30 FJGO/EP WAS HIGHER THAN THE OTHER EP CONDITIONS, 30 FJ/EP AND 30 FJ/EP-GO, AS WELL AS THE COEFFICIENT OF THERMAL EXPANSION (208.52 TO 248.95 X 10−6/°C). THE MASS LOSS FOR THE 30 FJGO/EP CONDITION IN THE FIRST STAGE WAS SLIGHTLY HIGHER THAN THE EP CONDITION (1.63%). THESE DMA AND TMA RESULTS PROVE TO BE PROMISING.

Palavras-chave

Fibra de junco-sete-ilhas; Compósitos epóxi; Análise dinâmico-mecânica; Análise termomecânica

Sedge Fiber; Epoxy composites; Dynamic mechanical analysis; Thermomechanical analysis.

Como citar

NEUBA, LUCAS DE MENDONÇA; SILVA, DOUGLAS SANTOS; BENTES, ELIAS MATIAS; REIS, LUCAS MOURA MONTENEGRO; SILVA, THUANE TEIXEIRA DA; MONTEIRO, SERGIO NEVES; JUNIO, RAÍ FELIPE PEREIRA. ANáLISE TERMO E DINâMICO MECâNICAS DAS FIBRAS DE JUNCO-SETE-ILHAS (CYPERUS MALACCENSIS) REVESTIDAS COM ÓXIDO DE GRAFENO REFORçANDO UMA MATRIZ EPóXI, p. 653-664. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.