AVALIAÇÃO DE SOLDABILIDADE DOS AÇOS INOXIDÁVEIS FERRÍTICOS ABNT 430 E ABNT 409 AO PROCESSO GTAW: ESTRUTURA DE SOLIDIFICAÇÃO, PROPRIEDADES MECÂNICAS E ESTAMPABILIDADE

EVALUATION OF WELDABILITY OF ABNT 430 AND ABNT 409 FERRITIC STAINLESS STEELS TO THE GTAW PROCESS: SOLIDIFICATION STRUCTURE, MECHANICAL PROPERTIES AND STAMPING

Autoria

DOI

10.5151/2594-5327-40669

Downloads

2 Downloads

Resumo

ALGUNS MATERIAIS APRESENTAM LIMITAçõES EM RELAçãO à SOLDABILIDADE, COMO é O CASO DOS AçOS INOXIDáVEIS FERRíTICOS, QUE POSSUEM BOA RESISTêNCIA à CORROSãO ATMOSFéRICA E BOA FORMABILIDADE. A SOLDAGEM MODIFICA E PREJUDICA AS PROPRIEDADES MECâNICAS E ANTICORROSIVAS DO MATERIAL. AVALIOU-SE A SOLDAGEM PELO PROCESSO GTAW EM AçOS INOXIDáVEIS FERRíTICOS ABNT 409) (ESTABILIZADO) E ABNT 430 (NãO ESTABILIZADO), COM DIFERENTES CONDIçõES DE SOLIDIFICAçãO A PARTIR DA VARIAçãO DE PARâMETROS DE SOLDAGEM MECANIZADA. OS RESULTADOS MOSTRARAM QUE EM BAIXAS VELOCIDADES E BAIXA CORRENTE, FORAM GERADOS GRãOS EPITAXIAIS ENCURVADOS EM DIREçãO à POçA DE FUSãO. O AUMENTO DA VELOCIDADE E DA CORRENTE DE SOLDAGEM RESULTOU EM UMA MAIOR INSTABILIDADE DA POçA, FORMANDO UMA ESTRUTURA NO FORMATO DE GOTA, COM GRãO COLUNARES. OS EFEITOS DA VIBRAçãO MECâNICA TAMBéM FORAM AVALIADOS, O QUE RESULTOU EM UM REFINO DOS GRãOS E AUMENTO DA UNIFORMIDADE NO CENTRO DO CORDãO. A ANáLISE METALOGRáFICA MOSTROU QUE NO AçO ABNT 430 OCORREU A FRAGILIZAçãO DO MATERIAL COM FORMAçãO DE MARTENSITA NOS CONTORNOS DE GRãO, O QUE NãO ACONTECEU COM O AçO ABNT 409. AS JUNTAS OBTIDAS FORAM CARACTERIZADAS EM RELAçãO AO SEU COMPORTAMENTO EM ENSAIOS DE TRAçãO E ENSAIO DE ESTAMPAGEM ERICHSEN, NO QUAL O AçO ABNT 409 APRESENTOU MELHORES CARACTERíSTICAS

 

SOME MATERIALS HAVE WELDABILITY ISSUES, SUCH AS FERRITIC STAINLESS STEELS, WHICH HAVE GOOD RESISTANCE TO ATMOSPHERIC CORROSION AND GOOD FORMABILITY. WELDING MODIFIES AND IMPAIRS THE MECHANICAL AND ANTI-CORROSION PROPERTIES OF THE MATERIAL. WELDING USING THE GTAW PROCESS WAS EVALUATED ON FERRITIC STAINLESS STEELS ABNT 409) (STABILIZED) AND ABNT 430 (NON-STABILIZED), WITH DIFFERENT SOLIDIFICATION CONDITIONS BASED ON THE VARIATION OF MECHANIZED WELDING PARAMETERS. THE RESULTS SHOWED THAT AT LOW SPEEDS AND LOW CURRENT, CURVED EPITAXIAL GRAINS WERE GENERATED TOWARDS THE WELD POOL. THE INCREASE IN WELDING SPEED AND CURRENT RESULTED IN GREATER INSTABILITY OF THE POOL, FORMING A DROP-SHAPED STRUCTURE, WITH COLUMNAR GRAINS. THE EFFECTS OF MECHANICAL VIBRATION WERE ALSO EVALUATED, WHICH RESULTED IN GRAIN REFINEMENT AND INCREASED UNIFORMITY IN THE CENTER OF THE BEAD. THE METALLOGRAPHIC ANALYSIS SHOWED THAT IN THE ABNT 430 STEEL THE MATERIAL WEAKENED WITH THE FORMATION OF MARTENSITE AT THE GRAIN BOUNDARIES, WHICH DID NOT HAPPEN WITH THE ABNT 409 STEEL. THE JOINTS OBTAINED WERE CHARACTERIZED IN RELATION TO THEIR BEHAVIOR IN TENSILE TESTS AND THE ERICHSEN STAMPING TEST, IN WHICH ABNT 409 STEEL PRESENTED BETTER CHARACTERISTICS

Palavras-chave

GTAW; Aços Inoxidáveis Ferríticos; Modos de Solidificação; Parâmetros de Soldagem;

GTAW; Ferritic Stainless Steels; Solidification Modes; Welding Parameters.

Como citar

PORCARO, RODRIGO RANGEL; RAMOS, DANIELA MAGALHÃES; FARIA, GEOVANE DE ASSIS. AVALIAÇÃO DE SOLDABILIDADE DOS AÇOS INOXIDÁVEIS FERRÍTICOS ABNT 430 E ABNT 409 AO PROCESSO GTAW: ESTRUTURA DE SOLIDIFICAÇÃO, PROPRIEDADES MECÂNICAS E ESTAMPABILIDADE, p. 1069-1079. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.