CARACTERIZAÇÃO MICROSESTRUTURAL DO AÇO PHS 1500 E 2000 POR METALOGRAFIA COLORIDA

MICROSTRUCTURAL CHARACTERIZATION OF PHS 1500 AND 2000 STEEL BY COLOR METALLOGRAPHY

Autoria

DOI

10.5151/2594-5327-40759

Downloads

4 Downloads

Resumo

OS AçOS ENDURECIDOS POR PRENSAGEM (PHS, DO INGLêS "PRESS HARDENED STEEL”) DESEMPENHAM UM PAPEL CRUCIAL NA INDúSTRIA AUTOMOTIVA, SENDO EMPREGADOS NA FABRICAçãO DAS CARROCERIAS DOS VEíCULOS DEVIDO à SUA RESISTêNCIA MECâNICA ELEVADA. ESSA RESISTêNCIA é ALCANçADA POR MEIO DO PROCESSO DE ESTAMPAGEM A QUENTE, QUE TRANSFORMA AS ESTRUTURAS FERRíTICAS/PERLíTICAS PARA MARTENSíTICAS. NO ENTANTO, OUTRAS FASES PODEM SE FORMAR E A MICROESTRUTURA FINAL PODE APRESENTAR REGIõES COM DIFERENTES TIPOS DE BAINITAS, REVENIMENTO DA MARTENSITA E ATé AUSTENITA RETIDA. A QUANTIFICAçãO DESSAS FASES APóS A ESTAMPAGEM A QUENTE NãO é UMA TAREFA FáCIL, UMA VEZ QUE AS TéCNICAS APRESENTAM DIFICULDADES NA DIFERENCIAçãO DE MICROESTRUTURAS REFINADAS. O USO DO ATAQUE COLORIDO SURGE COMO UMA ALTERNATIVA POUCO EXPLORADA PARA CARACTERIZAR ESSES AçOS, OFERECENDO UM CONTRASTE SELETIVO NA MICROESTRUTURA. ESTE ESTUDO DESCREVE A CARACTERIZAçãO MICROESTRUTURAL POR METALOGRAFIA COLORIDA EM QUATRO ETAPAS DE ATAQUE, SOB TRêS CONDIçõES DIFERENTES. OS RESULTADOS REVELARAM UMA DISTINçãO CLARA ENTRE AS DIVERSAS CONDIçõES, FORNECENDO INFORMAçõES VALIOSAS SOBRE A MICROESTRUTURA DOS AçOS ANALISADOS.

 

THE PRESS-HARDENED STEELS (PHS), PLAY A CRUCIAL ROLE IN THE AUTOMOTIVE INDUSTRY, BEING USED IN THE MANUFACTURING OF VEHICLE BODIES DUE TO THEIR HIGH MECHANICAL STRENGTH. THIS STRENGTH IS ACHIEVED THROUGH HOT STAMPING, WHICH TRANSFORMS FERRITIC/PEARLITIC STRUCTURES INTO MARTENSITIC STRUCTURES. HOWEVER, OTHER PHASES CAN FORM AND THE FINAL MICROSTRUCTURE CAN PRESENT REGIONS WITH DIFFERENT TYPES OF BAINITE, MARTENSITE TEMPERING AND EVEN RETAINED AUSTENITE. QUANTIFYING THESE PHASES AFTER HOT STAMPING IS NOT AN EASY TASK, SINCE THE TECHNIQUES PRESENT DIFFICULTIES IN DIFFERENTIATING REFINED MICROSTRUCTURES. THE USE OF COLOR ETCHING EMERGES AS A LITTLE EXPLORED ALTERNATIVE TO CHARACTERIZE THESE STEELS, PROVIDING SELECTIVE CONTRAST IN THE MICROSTRUCTURE. THIS STUDY DESCRIBES THE MICROSTRUCTURAL CHARACTERIZATION THROUGH COLORED METALLOGRAPHY IN FOUR ETCHING STEPS, UNDER THREE DIFFERENT CONDITIONS. THE RESULTS REVEALED A CLEAR DISTINCTION BETWEEN THE VARIOUS CONDITIONS, PROVIDING VALUABLE INFORMATION ABOUT THE MICROSTRUCTURE OF THE ANALYZED STEELS.

Palavras-chave

Estampagem a quente; Aços endurecidos por prensagem; Metalografia colorida.

Hot stamping; Press-hardened steels; Color metallography.