OS RESíDUOS DE DEMOLIçãO SãO LIXOS COMPOSTOS POR DETRITOS, PROVENIENTES DE ELEMENTOS ESTRUTURAIS ESCOMBROS E REFORMAS. SEU POTENCIAL TEM SIDO OBJETO DE ESTUDO DE PESQUISADORES QUE OBSERVARAM QUE POR MEIO DE TRATAMENTO TéRMICO é POSSíVEL PROMOVER A DESIDRATAçãO, FORMANDO SILICATOS DE CáLCIO HIDRATADO, QUE QUANDO EM CONTATO NOVAMENTE COM A áGUA, SãO CAPAZES DE RECUPERAR PARCIALMENTE A RESISTêNCIA DA MATRIZ CIMENTICIA. POR ESTA RAZãO, ESTE TRABALHO ANALISOU AS CARACTERíSTICAS FíSICO-MECâNICAS DO RESíDUO CIMENTíCIO DE REBOCO (RCR) DESIDRATADO à 550°C E TRITURADO, POR MEIO DAS ANáLISES DE GRANULOMETRIA à LASER, DIFRAçãO DE RAIOS-X (DR-X) E CALORIMETRIA ISOTéRMICA. Já NO ESTADO ENDURECIDO, FORAM CONFECCIONADOS CORPOS DE PROVA PRISMáTICOS (4X4X16) PARA OS ENSAIOS DE DENSIDADE, RESISTêNCIA MECâNICA, íNDICE DE VAZIOS E ABSORçãO DE áGUA POR CAPILARIDADE E POR IMERSãO. O TRAçO DESENVOLVIDO FOI DE 1:6 (CIMENTO:AREIA), COM PROPORçõES DE SUBSTITUIçãO DE 0, 10, 20 E 30% DO AGREGADO MIúDO PELO RCR E UTILIZOU-SE O CIMENTO CPV ARI. OS RESULTADOS MOSTRARAM QUE A SUBSTITUIçãO DA AREIA PELO RCR PROMOVEU MELHORAS SIGNIFICATIVAS NAS PROPRIEDADES MECâNICAS E TECNOLóGICAS DA ARGAMASSA, AUMENTANDO A RESISTêNCIA MECâNICA, DIMINUINDO O íNDICE DE VAZIOS E ABSORçãO TANTO POR CAPILARIDADE, QUANTO POR IMERSãO.
DEMOLITION WASTE IS WASTE COMPOSED OF DEBRIS, COMING FROM STRUCTURAL ELEMENTS, RUBBLE AND RENOVATIONS. ITS POTENTIAL HAS BEEN THE SUBJECT OF STUDY BY RESEARCHERS WHO OBSERVED THAT THROUGH HEAT TREATMENT IT IS POSSIBLE TO PROMOTE DEHYDRATION, FORMING HYDRATED CALCIUM SILICATES, WHICH WHEN IN CONTACT WITH WATER AGAIN, ARE CAPABLE OF PARTIALLY RECOVERING THE STRENGTH OF THE CEMENT MATRIX. FOR THIS REASON, THIS WORK ANALYZED THE PHYSICAL-MECHANICAL CHARACTERISTICS OF PLASTER CEMENT RESIDUE (RCR) DEHYDRATED AT 550°C AND CRUSHED, THROUGH LASER GRANULOMETRY, X-RAY DIFFRACTION (X-RD) AND ISOTHERMAL CALORIMETRY ANALYSES. ONCE IN THE HARDENED STATE, PRISMATIC SPECIMENS (4X4X16) WERE MADE FOR TESTING DENSITY, MECHANICAL RESISTANCE, VOID INDEX AND WATER ABSORPTION BY CAPILLARITY AND IMMERSION. THE MIXTURE DEVELOPED WAS 1:6 (CEMENT:SAND), WITH REPLACEMENT PROPORTIONS OF 0, 10, 20 AND 30% OF THE FINE AGGREGATE BY RCR AND CPV ARI CEMENT WAS USED. THE RESULTS SHOWED THAT REPLACING SAND WITH RCR PROMOTED SIGNIFICANT IMPROVEMENTS IN THE MECHANICAL AND TECHNOLOGICAL PROPERTIES OF THE MORTAR, INCREASING MECHANICAL RESISTANCE, REDUCING THE VOID INDEX AND ABSORPTION BOTH BY CAPILLARITY AND IMMERSION.
Palavras-chave
Tratamento térmico; Desidratação; Resíduo de reboco; Reciclagem.
Heat treatment; Dehydration; Demolition waste; Recycling.
Como citar
NEVES, SÉRGIO; TAVARES, KARINE MIRANDA DE SOUZA; BARROSO, LAIMARA DA SILVA; PEREIRA, MARIA MARIANA DIAS; CHERENE, MARIANA GOMES PINTO; XAVIER, GUSTAVO DE CASTRO; SOUSA, SIDNEI JOSÉ GOMES; AZEVEDO, AFONSO RANGEL GARCEZ DE; SOUSA, LETÍCIA BARCELOS DE.
CARACTERÍSTICAS FÍSICO-MECÂNICAS DE RESÍDUO DE REBOCO TERMICAMENTE TRATADO,
p. 1712-1722.
In: 77º Congresso Anual da ABM - Internacional,
São Paulo, Brasil,
2024.
ISSN: 2594-5327, DOI 10.5151/2594-5327-40923