Título

CORROSãO INTEGRANULAR EM AçOS INOXIDáVEIS AUSTENíTICOS (ABNT 304) E FERRíTICOS (ABNT 430) SOLDADOS

INTERGRANULAR CORROSION IN WELDED AUSTENITIC (ABNT 304) AND FERRITIC (ABNT 430) STAINLESS STEELS

Autoria

MOUSSA, THAYNARA MELO; CANDIDO, LUIZ CLAUDIO; OLIVEIRA, FERNANDA DO NASCIMENTO

MOUSSA, THAYNARA MELO

Eu sou esse autor

CANDIDO, LUIZ CLAUDIO

Eu sou esse autor

OLIVEIRA, FERNANDA DO NASCIMENTO

Eu sou esse autor

DOI

10.5151/2594-5327-40681

Downloads

Resumo

OS AçOS INOXIDáVEIS FERRíTICOS E AUSTENíTICOS SãO SUSCETíVEIS AO FENôMENO DE SENSITIZAçãO APóS SEREM EXPOSTOS A ALTAS TEMPERATURAS, O QUE PODE PROMOVER A CORROSãO INTERGRANULAR. NESSE CONTEXTO, ESSE TRABALHO VISOU ESTUDAR OS EFEITOS DA SOLDAGEM EM JUNTAS DE AçOS INOXIDáVEIS SOLDADAS PELO PROCESSO MIG (METAL INERT GAS), UTILIZANDO-SE UM ARAME DE ADIçãO DE ELETRODO AUSTENíTICO (ABNT 316LSI, %C £ 0,03% EM MASSA), COM ATMOSFERA DE PROTEçãO CONTENDO ARGôNIO DE ALTA PUREZA. VERIFICOU-SE A FORMAçãO DE MARTENSITA NA ZONA TERMICAMENTE AFETADA (ZTA) DO AçO ABNT 430 (FERRíTICO), BEM COMO CRESCIMENTO DE GRãOS SIGNIFICATIVO NESSA REGIãO. NA ZONA FUNDIDA (ZF) OS AçOS ABNT 430 E ABNT 304 APRESENTARAM MICROESTRUTURAS DUPLEX DE AUSTENITA E FERRITA. ALéM DISSO, AMBOS APRESENTARAM PRECIPITAçãO DE CARBONETOS DE CR DE FORMA SIGNIFICATIVA NO METAL BASE (MB) O QUE PODE INDICAR A NãO SOLUBILIZAçãO DESSES CARBONETOS DAS AMOSTRAS DESTES AçOS NO ESTADO DE ENTREGA. FORAM REALIZADOS ENSAIOS DE POLARIZAçãO POTENCIODINâMICA NOS AçOS ABNT 304 E ABNT 430 NO ESTADO DE ENTREGA, E FICOU EVIDENTE A MAIOR RESISTêNCIA à CORROSãO DO AçO INOXIDáVEL AUSTENíTICO EM SOLUçãO AQUOSA CONTENDO 3,5% EM MASSA DE NACL. ADEMAIS, FORAM REALIZADOS TRATAMENTOS TéRMICOS PARA AVALIAR O GRAU DE SENSITIZAçãO DOS AçOS. FOI POSSíVEL OBSERVAR QUE OS DOIS AçOS TRATADOS TERMICAMENTE EM FORNOS FORAM SUSCETíVEIS à CORROSãO INTERGRANULAR, E DE FORMA MAIS ACENTUADA, O AçO INOXIDáVEL FERRíTICO. NESTE TRABALHO FORAM UTILIZADAS NORMAS ASTM A262 E A763.

FERRITIC AND AUSTENITIC STAINLESS STEELS ARE SUSCEPTIBLE TO THE PHENOMENON OF SENSITIZATION AFTER BEING EXPOSED TO HIGH TEMPERATURES, WHICH CAN PROMOTE INTERGRANULAR CORROSION. IN THIS CONTEXT, THIS WORK AIMED TO STUDY THE EFFECTS OF WELDING ON STAINLESS STEEL JOINTS WELDED BY THE MIG PROCESS, USING AN AUSTENITIC ELECTRODE ADDITION WIRE (AISI 316LSI, %C ≤ 0.03% BY MASS), WITH A PROTECTIVE ATMOSPHERE CONTAINING HIGH PURITY ARGON. THE FORMATION OF MARTENSITE ISLANDS WAS OBSERVED IN THE HAZ OF AISI 430 (FERRITIC) STEEL, AS WELL AS SIGNIFICANT GRAIN GROWTH IN THIS REGION. AT THE FUSION ZONE, AISI 430 AND AISI 304 STEELS PRESENTED A DUPLEX MICROSTRUCTURE OF AUSTENITE AND FERRITE. FURTHERMORE, BOTH SHOWED SIGNIFICANT PRECIPITATION OF CR CARBIDES IN THE BASE METAL, WHICH MAY INDICATE THE NON-SOLUBILIZATION OF THESE CARBIDES IN THE SAMPLES OF THESE STEELS IN THE DELIVERY STATE. POTENTIODYNAMIC POLARIZATION TESTS WERE CARRIED OUT ON AISI 304 AND AISI 430 STEELS IN THE DELIVERY STATE, AND THE GREATER CORROSION RESISTANCE OF AUSTENITIC STAINLESS STEEL WAS CLEAR. FURTHERMORE, HEAT TREATMENTS WERE CARRIED OUT TO EVALUATE THE DEGREE OF SENSITIZATION OF THE STEELS. IT WAS POSSIBLE TO OBSERVE THAT THE TWO HEAT TREATED STEELS WERE SUSCEPTIBLE TO INTERGRANULAR CORROSION, AND IN A MORE PRONOUNCED WAY, THE FERRITIC STAINLESS STEEL. IN THIS WORK, ASTM A262 AND A763 STANDARDS WERE USED.

Palavras-chave

Aços Inoxidáveis; Soldagem; Sensitização; Corrosão Intergranular

Stainless Steels; Welding; Sensitization; Intergranular Corrosion.