EFEITO DA ELETRODEPOSIÇÃO DE NÍQUEL-NIÓBIO NO COMPORTAMENTO EM FADIGA DE UM AÇO SAE 1020

EFFECT OF NICKEL-NIOBIUM COATING BY ELECTRODEPOSITION IN THE FATIGUE BEHAVIOR OF A SAE 1020 STEELL

Autoria

DOI

10.5151/1516-392X-27597

Downloads

852 Downloads

Resumo

O objetivo deste trabalho é estudar o efeito do recobrimento de níquel-nióbio por eletrodeposição na resistência à fadiga de um aço carbono SAE 1020. Os corpos de prova para os ensaios de fadiga foram extraídos de barras de diâmetro igual a 7,94 mm (5/16’’). Os ensaios de fadiga foram realizados por flexão rotativa com carregamento em balanço. Foi empregada uma velocidade de rotação de aproximadamente 1500rpm. Foram realizados ensaios de dureza do aço e da camada depositada de Ni-Nb. Análises microestruturais do aço e das fraturas de fadiga foram realizadas através de microscopia eletrônica de varredura (MEV). Os ensaios de fadiga foram realizados de forma a se obter curvas S-N (curvas de Whöler). Foram realizados três ensaios para cada carregamento. Foi observado que o recobrimento de Ni-Nb proporcionou tendência ao aumento do limite de resistência à fadiga do aço.

 

The objective of this work is to study the effect of coating nickel-niobium by electrodeposition on the fatigue strength of a carbon steel SAE 1020. The samples for fatigue testing were carried out from bars diameter 7.94mm. The fatigue tests were performed by bending with rotary loading balance. The tests were performed with 1500rpm. Hardness tests were conducted on the steel and deposited Ni-Nb coating. Microstructural analysis of the steel and fatigue fractures were performed by scanning electron microscopy (SEM). The fatigue tests were performed to obtain Whöler curves. Three tests were performed for each loading. It was observed that Ni-Nb coating provided a small increase on the fatigue strength of the steel.

Palavras-chave

Resistência à fadiga, Curva S-N, Eletrodeposição de Ni-Nb.

Fatigue strength, S-N curves, Electrodeposition of Ni-Nb