EFEITO DE TRATAMENTOS ISOTÉRMICOS A 475°C E A 850ºC NA RESISTÊNCIA À FADIGA DE UM AÇO INOXIDÁVEL DUPLEX UNS S32304

EFFECT OF ISOTHERMAL TREATMENTS AT 475ºC AND 850ºC ON THE FATIGUE RESISTANCE OF A DUPLEX STAINLESS STEEL UNS S 32304

Autoria

DOI

10.5151/2594-5327-22962

Downloads

281 Downloads

Resumo

O objetivo deste trabalho foi avaliar o efeito de tratamentos isotérmicos nas propriedades mecânicas, principalmente fadiga, de um aço inoxidável duplex UNS S32304. Para tal, foram realizados tratamentos isotérmicos nas temperaturas de 475ºC e 850ºC. Em seguida foram realizados ensaios de tração, microdureza, tenacidade ao impacto e fadiga com controle de carga. A análise estrutural foi conduzida empregando as técnicas de microscopia ótica, microscopia eletrônica de varredura e de varredura por sonda mecânica. As análises microestruturais revelaram que ocorreu a formação de Cr2N e da fase σ após os tratamentos térmicos a 850ºC. A precipitação de Cr2N implicou no aumento da energia absorvida ao impacto e do percentual de alongamento em tração e diminuição na microdureza e na tensão limite de escoamento da liga. A resistência à fadiga e a resistência à tração não sofreram alterações significativas devido à presença de Cr2N. A fase σ se formou em pequena quantidade e seus efeitos não foram observados. Já os tratamentos térmicos a 475ºC levaram o material a apresentar redução na energia absorvida ao impacto, aumento na microdureza da fase α, na resistência à tração e na resistência à fadiga devido à precipitação de α’.

 

The aim of this work piece was to evaluate the effect of isothermal treatments on the mechanical properties, mainly fatigue, of a duplex stainless steel UNS S32304.For this purpose, it were carried out isothermal treatments at temperatures of 475ºC and 850ºC. Then were performed tests of tensile, microhardness, impact toughness and fatigue with control of load.The structural analysis was conducted employing the techniques of optical microscopy, scanning electronic microscopy and scanning probe microscopy. The microstructural analysis showed that occur the formation of Cr2N and of the σ phase after the heat treatments at 850ºC. The precipitation of Cr2N resulted in increased of the energy absorption in impact and percentage of elongation in tension and reduction at the microhardness and tension yield strength of the alloy. The fatigue resistance and the tensile strength have not significant changed due the presence of Cr2N. The σ phase formed in small amounts and their effects were not observed. Already the heat treatments at 475ºC led the material to present reduction in energy absorbed the impact, increase in microhardness of the α fase, the tensile strength and fatigue resistance due to precipitation of α’.

Palavras-chave

Aço inoxidável lean duplex; Resistência à fadiga; Fragilização à 475ºC; Fase σ; Cr2N.

Lean duplex stainless steel; Fatigue resistance; Embrittlement at 475ºC; σ phase; Cr2N.