EVOLUÇÃO MICROESTRUTURAL NA LIGA 718 PARA DIFERENTES CONDIÇÕES DE SOLUBILIZAÇÃO E ENVELHECIMENTO

MICROSTRUCTURAL EVOLUTION OF 718 ALLOY UNDER DIFFERENT SOLUBILIZATION AND AGING CONDITIONS

Autoria

DOI

10.5151/2594-5327-40652

Downloads

2 Downloads

Resumo

AS PROPRIEDADES MECâNICAS DAS SUPERLIGAS A BASE DE NíQUEL, EM PARTICULAR DA LIGA 718, SãO MELHORADAS PRINCIPALMENTE PELO MECANISMO DE PRECIPITAçãO. A PRECIPITAçãO DE FASES COMO γ’ E γ” PROMOVE UM SUBSTANCIAL AUMENTO DAS PROPRIEDADES MECâNICAS, O QUE PODE SER VERIFICADO PELA DUREZA DO MATERIAL. NO ENTANTO, TAIS FASES SãO METAESTáVEIS O QUE EM DETERMINADAS CONDIçõES PODE DAR ORIGEM AS FASES ESTáVEIS, EM PARTICULAR à FASE d. ESSA FASE TEM EFEITO DELETéRIO NAS LIGAS 718 E IMPACTA DIRETAMENTE NAS PROPRIEDADES MECâNICAS DESSAS LIGAS. O OBJETIVO DO PRESENTE TRABALHO FOI VERIFICAR A VARIAçãO DE DUREZA DA LIGA 718, PARA DIFERENTES TEMPERATURAS DE SOLUBILIZAçãO E DIFERENTES TEMPOS DE ENVELHECIMENTO, A FIM DE SE DETERMINAR A CONDIçãO DE MELHORES PROPRIEDADES MECâNICAS. MEDIDAS DE MICRODUREZA VICKERS ALéM DAS CARACTERIZAçõES DE MICROSCOPIA óPTICA E DIFRAçãO DE RAIOS X (DRX) FORAM EMPREGADAS PARA VERIFICAR A EVOLUçãO DESSAS LIGAS AO LONGO DOS TRATAMENTOS ESCOLHIDOS. FOI OBSERVADO QUE A MAIOR TEMPERATURA DE SOLUBILIZAçãO FOI CAPAZ DE DISSOLVER OS PRECIPITADOS d DA LIGA COMO RECEBIDA, MAS POR OUTRO LADO PROMOVEU O CRESCIMENTO DE GRãO O QUE FEZ COM QUE A DUREZA FOSSE DIMINUíDA. O MáXIMO DE DUREZA OBSERVADO FOI PARA O TEMPO DE ENVELHECIMENTO DE 15H PARA AS DUAS CONDIçõES DE SOLUBILIZAçãO.

 

THE MECHANICAL PROPERTIES OF NICKEL-BASED SUPERALLOYS, PARTICULARLY 718 ALLOY, ARE MAINLY IMPROVED BY PRECIPITATION MECHANISM. PRECIPITATION OF PHASES SUCH AS γ ’AND γ” PROMOTES A SUBSTANTIAL INCREASE IN MECHANICAL PROPERTIES, WHICH CAN BE VERIFIED BY THE HARDNESS OF THE MATERIAL. HOWEVER, SUCH PHASES ARE METASTABLE WHICH, UNDER CERTAIN CONDITIONS, CAN GIVE RISE TO STABLE PHASES, THE d PHASE. THIS PHASE HAS A DELETERIOUS EFFECT ON 718 ALLOY AND DIRECTLY IMPACTS THE MECHANICAL PROPERTIES. THE OBJECTIVE OF THE PRESENT WORK WAS TO VERIFY THE VARIATION IN HARDNESS OF THE 718 ALLOY, FOR DIFFERENT SOLUBILIZATION TEMPERATURES AND DIFFERENT AGING TIMES, TO DETERMINE THE CONDITION OF BETTER MECHANICAL PROPERTIES. VICKERS MICROHARDNESS MEASUREMENTS AND CHARACTERIZATION OF THE MICROSTRUCTURE BY OPTICAL MICROSCOPY AND X-RAY DIFFRACTION (XRD) WERE USED TO VERIFY THE EVOLUTION OF THESE ALLOYS OVER THE CHOSEN TREATMENTS. IT WAS OBSERVED THAT THE HIGHEST SOLUBILIZATION TEMPERATURE WAS ABLE TO DISSOLVE THE d PRECIPITATES OF THE AS-RECEIVED CONDITION, BUT ON THE OTHER HAND, IT PROMOTED GRAIN GROWTH, WHICH CAUSED A DECREASE IN HARDNESS. THE MAXIMUM HARDNESS WAS OBSERVED FOR 15H AGING TIME FOR SOLUBILIZATION CONDITIONS.

Palavras-chave

Endurecimento por precipitação; liga 718; Evolução microestrutural

Precipitation hardening; 718 alloy; Microstructural evolution.

Como citar

SOUSA, LAURA SETTI DE; FILHO, FABIO DA COSTA GARCIA; CÊA, BERNARDO SOARES AVILA DE; MONTEIRO, SERGIO NEVES; BRASILEIRO, ROBERTO MATIAS GUIMARÃES; OLIVEIRA, JOÃO LUCAS SANTOS LIMA DE. EVOLUÇÃO MICROESTRUTURAL NA LIGA 718 PARA DIFERENTES CONDIÇÕES DE SOLUBILIZAÇÃO E ENVELHECIMENTO , p. 1017-1024. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.