Samples of spray formed AISI M2 high-speed steel were hot rolled at 50% and 72% reduction rates. The hot rolling was done at 1150 °C with sample reheating between steps. The samples were characterised by optical microscopy, scanning electron microscopy and x-ray diffraction. The obtained results were compared with commercial and as fabricated samples. The results are presented and discussed in terms of microstructure refinement, size and carbides distribution.
Samples of spray formed AISI M2 high-speed steel were hot rolled at 50% and 72% reduction rates. The hot rolling was done at 1150 °C with sample reheating between steps. The samples were characterised by optical microscopy, scanning electron microscopy and x-ray diffraction. The obtained results were compared with commercial and as fabricated samples. The results are presented and discussed in terms of microstructure refinement, size and carbides distribution.
Palavras-chave
spray forming, AISI M2 high-speed steel, hot rolling
spray forming, AISI M2 high-speed steel, hot rolling
Como citar
Jesus, E. R. B.; Schroer, G.; Filho, E. S. Jesus; Serna, M. M.; Galego, E.; Rossi, J. L..
MICROSTRUCTURAL CHARACTERISATION OF SPRAY FORMED AISI M2 HIGH-SPEED STEEL AFTER HOT ROLLING,
p. 4377-4385.
In: 59º Congresso anual,
São Paulo, Brasil,
2004.
ISSN: 2594-5327, DOI 10.5151/2594-5327-4379