ANÁLISE DE CORROSÃO EM JUNTAS SOLDADAS PELO PROCESSO SMAW NO AÇO API 5L X70 EM MEIO SALINO

CORROSION ANALYSIS IN WELDS WELDED BY THE SMAW PROCESS IN API 5L X70 STEEL IN SALINE

DOI

10.5151/1516-392X-30950

Downloads

Baixar Artigo 390 Downloads

Resumo

Este trabalho visa as análises metalograficas qualitativas da região de solda e a análises qualitativas e semi- quantitativa da corrosão em juntas soldadas pelo processo SMAW em tubos do aço API 5L X-70, em solução de NaCl; afim de simular um eventual ambiente de trabalho do aço em questão, conhecer seu comportamento para consequentemente prever e evitar danos corrosivos e diminuição de custos. Para realização do trabalho um tubo de Aço API 5L X70 foi cortado, soldado e dividido em corpos de prova e então imersos em solução de NaCl nas concentrações de 1,5% e 4,5%, os corpos de prova foram imersos em soluções estáticas e em agitação. As amostras foram devidamente preparadas de acordo com a norma ASTM G31 para o ensaio de imersão e ficaram imersos por 75 dias. Foi feito o cálculo de perda de massa, taxa de corrosão e micrografias. As amostras apresentaram corrosão do tipo generalizada e por pites, comprovando a teoria de que as amostras com maior concentração e agitadas tiveram uma maior taxa de corrosão, e um maior número de pites. Através das micrografias, foram observadas uma maior concentração de pites na zona termicamente afetada, e também na zona fundida nas amostras que tiveram uma maior concentração de pites. No metal de base houve a presença de pites em menor proporção. No geral pode-se dizer que a junta apresentou uma tolerância à corrosão razoável neste meio.

 

This work aims at the qualitative metallographic analyzes of the weld region and the qualitative and semi-quantitative analyzes of the corrosion in welds welded by the SMAW process in API 5L X-70 steel tubes in NaCl solution; In order to simulate a possible working environment of the steel in question, to know its behavior in order to anticipate and avoid corrosive damages and cost reduction. To perform the work, a tube of API 5L X70 Steel was cut, welded and divided into test pieces and then immersed in NaCl solution at concentrations of 1.5% and 4.5%, the specimens were immersed in static solutions And stirring. The samples were duly prepared according to ASTM G31 for the immersion test and were immersed for 75 days. Mass loss, corrosion rate and micrographs were calculated. The samples showed generalized and pitting corrosion, confirming the theory that the higher concentration and agitated samples had a higher corrosion rate and a higher number of pits. Through the micrographs, a higher concentration of pites was observed in the thermally affected area, and also in the melted zone in the samples that had a higher concentration of pites. In the base metal there was the presence of pites in a smaller proportion. In general it can be said that the joint exhibited a reasonable corrosion tolerance in this medium.

Palavras-chave

Aço API 5L X70. Metalurgia da Soldagem. Corrosão

Steel API 5L X70. Welding Metallurgy. Corrosion

Como citar

Almeida, Matheus Jorge de; Chilque, Angel Rafael Arce; Silva, Letícia Barbosa; Souza, Franciele Vieira de; Freitas, Filipe Menezes de; Camilo, Carla de Araújo. ANÁLISE DE CORROSÃO EM JUNTAS SOLDADAS PELO PROCESSO SMAW NO AÇO API 5L X70 EM MEIO SALINO , p. 3593-3603. In: 72nd ABM Annual Congress, São Paulo, 2017.