Título

ANÁLISE COMPARATIVA DO PROCESSO DE FABRICAÇÃO DE FACAS ARTESANAIS EM AÇO SAE 1070

COMPARATIVE ANALYSIS OF THE PROCESS OF MANUFACTURING ARTISANAL KNIVES IN STEEL SAE 1070

Autoria

Almeida, Yuri Freitas da Silva; Murro, Tiago Homero; Souza, Victor Barbosa de; Júnior, Aloísio Costa Vieira; Lima, Amanda Camerini; Gallo, Daniel Passos; Azevedo, Afonso Rangel Garcez de; Marvila, Markssuel Teixeira; Monteiro, Sergio Neves; Miguel, Thais Pirovane

DOI

10.5151/2594-5327-34050

Downloads

Baixar Artigo 11 Downloads

Resumo

O AÇO SAE 1070, É UM AÇO COM ALTO TEOR DE CARBONO, UTILIZADO NA FABRICAÇÃO DE PEÇAS PLANAS QUE EXIGEM PROPRIEDADES MECÂNICAS ONDE O PROCESSO IRÁ SOFRER BAIXO GRAU DE CONFORMAÇÃO. A CUTELARIA E OS PRODUTOS ARTESANAIS VÊM GANHANDO GRANDE ESPAÇO NA ECONOMIA, MOVIMENTANDO O MERCADO DOS MICROEMPREENDEDORES, AUMENTANDO A PROCURA PELO APERFEIÇOAMENTO DOS CUTELEIROS. A PRESENTE PESQUISA BUSCA ANALISAR AS PROPRIEDADES OBTIDAS DAS LÂMINAS FORJADAS E USINADAS, VARIANDO O PROCESSO DE TÊMPERA. POR MEIO DA REVISÃO BIBLIOGRÁFICA, ESTUDOU-SE SOBRE A HISTÓRIA DAS LÂMINAS E A MÍSTICA QUE ENVOLVE SEU PROCESSO DE FABRICAÇÃO. FORAM REALIZADOS ENSAIOS PRELIMINARES DE TRAÇÃO, FLEXÃO E METALOGRÁFICO PARA A OBTENÇÃO DAS CARACTERÍSTICAS PARA COMPARAÇÃO DAS AMOSTRAS FINALIZADAS. UM TOTAL DE OITO LÂMINAS FORAM FORJADAS E OITO LÂMINAS FORAM USINADAS, APÓS A FABRICAÇÃO ELAS FORAM PARA OS TRATAMENTOS TÉRMICOS DE NORMALIZAÇÃO, TÊMPERA E REVENIMENTO. FEZ-SE O USO DAS NORMAS REGULAMENTADORAS PARA A EXECUÇÃO DOS ENSAIOS DE DUREZA E DE FLEXÃO DAS DEZESSEIS LÂMINAS. OS RESULTADOS OBTIDOS COMPROVARAM QUE O PROCESSO DE FABRICAÇÃO E O TRATAMENTO TÉRMICO INFLUENCIAM DIRETAMENTE NO RESULTADO FINAL DO PRODUTO DE MODO QUE AS LÂMINAS FORJADAS UTILIZANDO A TÊMPERA INTEGRAL SÃO SUPERIORES EM RESISTÊNCIA À FLEXÃO QUE AS LÂMINAS USINADAS.

 

SAE 1070 STEEL IS A STEEL WITH A HIGH CARBON CONTENT, USED IN THE MANUFACTURE OF FLAT PARTS THAT REQUIRE MECHANICAL PROPERTIES WHERE THE PROCESS WILL UNDERGO A LOW DEGREE OF CONFORMATION. CUTLERY AND ARTISANAL PRODUCTS HAVE BEEN GAINING GREAT SPACE IN THE ECONOMY, MOVING THE MICROENTREPRENEURS MARKET, INCREASING THE DEMAND FOR THE IMPROVEMENT OF CUTLERY. THIS RESEARCH SEEKS TO ANALYZE THE PROPERTIES OBTAINED FROM THE FORGED AND MACHINED BLADES, VARYING THE TEMPERING PROCESS. THROUGH BIBLIOGRAPHIC REVIEW, IT WAS STUDIED THE HISTORY OF THE BLADES AND THE MYSTIQUE THAT INVOLVES THEIR MANUFACTURING PROCESS. PRELIMINARY TESTS OF TRACTION, FLEXION AND METALLOGRAPHY WERE PERFORMED TO OBTAIN THE CHARACTERISTICS FOR COMPARISON OF THE FINISHED SAMPLES. A TOTAL OF EIGHT BLADES WERE FORGED AND EIGHT BLADES WERE MACHINED, AFTER MANUFACTURE THEY WENT TO NORMALIZATION, TEMPERING AND TEMPERING HEAT TREATMENTS. REGULATORY STANDARDS WERE USED TO PERFORM THE HARDNESS AND BENDING TESTS OF THE SIXTEEN BLADES. THE RESULTS OBTAINED PROVED THAT THE MANUFACTURING PROCESS AND THE HEAT TREATMENT DIRECTLY INFLUENCE THE FINAL RESULT OF THE PRODUCT, SO THAT THE BLADES FORGED USING INTEGRAL TEMPERING ARE SUPERIOR IN FLEXURAL STRENGTH THAN THE BLADES MACHINED.

Palavras-chave

Facas Artesanais; Forjamento; Desbaste; Têmpera

Handcrafted Knives; Forging; Thinning; Hardening