ANÁLISE DA RELAÇÃO DIAMETRAL NAS PROPRIEDADES MECÂNICAS EM TRAÇÃO DA FIBRA DE MALVA: ANALYSIS OF THE DIAMETER RATIO IN THE MECHANICAL PROPERTIES OF MALVA FIBER IN TENSION

A UTILIZAçãO DE FIBRAS NATURAIS COMO REFORçO EM MATERIAIS COMPóSITOS, TEM SE TORNADO UMA ALTERNATIVA SUSTENTáVEL E EFICIENTE EM SUBSTITUIçãO AOS REFORçOS SINTéTICO, DE ALTO VALOR DE PRODUçãO. DESSA FORMA, OBJETIVA-SE ESTUDAR AS PROPRIEDADES MECâNICA DA FIBRA DE MALVA EM RELAçãO A DIFERENçA DIAMETRAL DAS FIBRAS NATURAIS DE MALVA. A CARACTERíSTICA DIMENSIONAL FOI REALIZADA AVALIANDO A DENSIDADE E QUANTIDADE RELATIVA DA FIBRA EM CADA INTERVALO. PARA AVALIAR AS PROPRIEDADES MECâNICAS FOI REALIZADO O ENSAIO DE RESISTêNCIA à TRAçãO SEGUINDO A NORMA ASTM C1557. OS RESULTADOS APRESENTARAM A RESISTêNCIA à TRAçãO DA FIBRA E O MóDULO DE YOUNG PARA CADA INTERVALO. AS FIBRAS NATURAIS DE MALVA APRESENTARAM RESISTêNCIA à TRAçãO MéDIA IGUAL 273,2 MPA E MóDULO DE YOUNG IGUAL A 24,80 GPA. AS FIBRAS NATURAIS DE MALVA APRESENTARAM UM EXCEPCIONAL COMPORTAMENTO MECâNICO, QUANDO COMPARADAS AS OUTRAS FIBRAS LIGNOCELULóSICAS. DESSA FORMA, A VARIAçãO DE ESPESSURA DAS FIBRAS NATURAIS PODE INFLUENCIAR NA PROPRIEDADE MECâNICA FINAL DO COMPóSITO PRODUZIDOS A PARTIR DAS FIBRAS DE MALVA.

THE USE OF NATURAL FIBERS AS REINFORCEMENT IN COMPOSITE MATERIALS HAS BECOME A SUSTAINABLE AND EFFICIENT ALTERNATIVE TO REPLACING SYNTHETIC REINFORCEMENTS, WHICH HAVE A HIGH PRODUCTION VALUE. THUS, THE OBJECTIVE IS TO STUDY THE MECHANICAL PROPERTIES OF MALVA FIBER IN RELATION TO THE DIAMETRICAL DIFFERENCE OF NATURAL MALVA FIBERS. THE DIMENSIONAL CHARACTERISTIC WAS PERFORMED BY EVALUATING THE DENSITY AND RELATIVE QUANTITY OF THE FIBER IN EACH INTERVAL. TO EVALUATE THE MECHANICAL PROPERTIES, THE TENSILE STRENGTH TEST WAS CARRIED OUT FOLLOWING THE ASTM C1557 STANDARD. THE RESULTS PRESENTED THE FIBER'S TENSILE STRENGTH AND YOUNG'S MODULUS FOR EACH INTERVAL. MALVA'S NATURAL FIBERS SHOWED AN AVERAGE TENSILE STRENGTH OF 273.2 MPA AND YOUNG'S MODULUS OF 24.80 GPA. MALVA'S NATURAL FIBERS SHOWED EXCEPTIONAL MECHANICAL BEHAVIOR WHEN COMPARED TO OTHER LIGNOCELLULOSIC FIBERS. THEREFORE, THE VARIATION IN THICKNESS OF NATURAL FIBERS CAN INFLUENCE THE FINAL MECHANICAL PROPERTY OF THE COMPOSITE PRODUCED FROM MALVA FIBERS.

Palavras-chave

Caracterização mecânica; Relação Diamentral; Fibra de Malva

Mechanical characterization; Diamental relationship; Malva fiber.

Como citar

NASCIMENTO, DAMARES DA CRUZ BARBOSA; SOUZA, SARAH GABRIELLY BRANDÃO DE; SOUSA, PALOMA SUELLEN LIMA DE; NASCIMENTO, JOELLY VERA; MONTEIRO, SÉRGIO NEVES; SILVA, ALISSON CLAY RIOS DA; CANDIDO, VERÔNICA SCARPINI. ANÁLISE DA RELAÇÃO DIAMETRAL NAS PROPRIEDADES MECÂNICAS EM TRAÇÃO DA FIBRA DE MALVA , p. 364-372. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-40512