ANÁLISE DA RESISTÊNCIA AO IMPACTO CHARPY EM MATERIAIS COMPÓSITOS POLIMÉRICOS DE FIBRAS DE PIASSAVA E MATRIZ EPÓXI

ANALYSIS OF RESISTANCE TO CHARPY IMPACT ON POLYMERIC COMPOSITE MATERIALS OF PIASSAVA FIBERS AND EPOXY MATRIX

Autoria

Carvalho, Juliana Peixoto Rufino Gazem de; Ribeiro, Amanda Mendes; Guimarães, Renan da Silva; Simonassi, Noan Tonini; Lopes, Felipe Perisse Duarte; Vieira, Carlos Maurício Fontes

DOI

10.5151/2594-5327-34491

Downloads

Baixar Artigo 10 Downloads

Resumo

AS FIBRAS NATURAIS LIGNOCELULÓSICAS, CADA VEZ MAIS, SÃO ESTUDAS COMO SUBSTITUIÇÃO DE FIBRAS DE ORIGEM SINTÉTICA. A VANTAGEM DESTA UTILIZAÇÃO É O FATO DAS FIBRAS NATURAIS SEREM RENOVÁVEIS, BIODEGRADÁVEIS E POSSUÍREM BOAS PROPRIEDADES MECÂNICAS. A PARTIR DISTO, ESTE TRABALHO VISOU O REAPROVEITAMENTO DE FIBRAS DE PIASSAVA DESCARTADAS COMO RESÍDUO INDUSTRIAL PARA A ANÁLISE EM MATERIAIS COMPÓSITOS. PARA ISTO, FORAM CRIADOS PLACAS DE MATRIZ POLIMÉRICA EPÓXI COM INCORPORAÇÃO DE 30% A 60% EM VOLUME DE FIBRA. EM SEGUIDA, AS PLACAS FORAM CORTADAS EM DIMENSÕES DETERMINADAS PELA NORMA PARA ENSAIO DE IMPACTO CHARPY. POR FIM, COMO RESULTADO, OBTEVE-SE QUE AS COMPOSIÇÕES COM 60% DE FIBRA ATINGIRAM OS MELHORES RESULTADOS, CHEGANDO A, APROXIMADAMENTE, 15KJ/M² DE RESISTÊNCIA.

 

NATURAL LIGNOCELLULOSIC FIBERS ARE INCREASINGLY BEING STUDIED AS REPLACEMENTS FOR FIBERS OF SYNTHETIC ORIGIN. THE ADVANTAGE OF THIS USE IS THAT THE NATURAL FIBERS ARE RENEWABLE, BIODEGRADABLE AND HAVE GOOD MECHANICAL PROPERTIES. FROM THIS, THIS WORK AIMED AT THE REUSE OF PIASSAVA FIBERS DISCARDED AS INDUSTRIAL WASTE FOR THE ANALYSIS IN COMPOSITE MATERIALS. FOR THIS, EPOXY POLYMER MATRIX PLATES WERE CREATED WITH INCORPORATION OF 30% TO 60% BY VOLUME OF FIBER. THEN, THE PLATES WERE CUT TO DIMENSIONS DETERMINED BY THE CHARPY IMPACT TEST STANDARD. FINALLY, AS A RESULT, IT WAS FOUND THAT COMPOSITIONS WITH 60% FIBER ACHIEVED THE BEST RESULTS, REACHING APPROXIMATELY 15KJ / M² OF RESISTANCE.

Palavras-chave

Fibra de piassava; resina epóxi; Charpy; materiais compósitos

Piassava fiber; epoxy resin; Charpy; composite materials.