ANÁLISE DAS PROPRIEDADES MECÂNICAS DO CONCRETO ESTRUTURAL SUBSTITUINDO AGREGADO MIÚDO POR RESÍDUO DE FUNDIÇÃO

ANALYSIS OF THE MECHANICAL PROPERTIES OF THE STRUCTURAL CONCRETE REPLACING FINE AGGREGATE FOR CASTING WASTE

Autoria

Coutinho, Guilherme Moura Reis; Silva, Lucas Xavier Pereira da; Souza, Victor Barbosa de; Davila, Maksuell; Azevedo, Afonso Rangel Garcez de; Marvila, Markssuel Teixeira; Monteiro, Sergio Neves; Miguel, Thais Pirovane

DOI

10.5151/2594-5327-34051

Downloads

Baixar Artigo 9 Downloads

Resumo

O BRASIL É UM PAÍS EM ACESSÃO, E COM ISSO VÁRIOS SETORES DA ECONOMIA VÊM CRESCENDO JUNTAMENTE COM ESSE AVANÇO. A ÁREA DA FUNDIÇÃO ACOMPANHA ESTA ASCENSÃO, SENDO O BRASIL O SÉTIMO MAIOR PRODUTOR DE FUNDIDOS DO MUNDO, E ESTA ATIVIDADE GERA RESÍDUOS SÓLIDOS, SENDO A CHAMADA RESÍDUO O PRINCIPAL DELES. O OBJETIVO DESTE TRABALHO É A SUBSTITUIÇÃO DO AGREGADO MIÚDO DE CONCRETO PELO RESÍDUO DE FUNDIÇÃO. PARA A CONFECÇÃO DOS CORPOS DE PROVA FOI UTILIZADO O TRAÇO 3:2:1 (AREIA: BRITA: CIMENTO), RESPECTIVAMENTE. APÓS VERIFICADOS VALORES OBTIDOS EM UM ENSAIO COM CORPO DE PROVA SEM INCORPORAÇÃO, FORAM FEITOS TRAÇOS SUBSTITUINDO POR PORCENTAGENS DISTINTAS DE REJEITO DE FUNDIÇÃO. OS CORPOS DE PROVA FORAM CURADOS A TEMPERATURA AMBIENTE POR 7 E 28 DIAS, E LOGO APÓS FORAM SUBMETIDOS A ENSAIOS DE COMPRESSÃO ONDE TIVERAM UMA RUPTURA CISALHADA E DIFERENTES VALORES DE LIMITE DE RESISTÊNCIA (MPA). PODE-SE CONCLUIR COM ESTE ESTUDO QUE EXISTE A VIABILIDADE DA SUBSTITUIÇÃO PARCIAL DO AGREGADO MIÚDO DO CONCRETO PELO RESÍDUO DE FUNDIÇÃO.

 

BRAZIL IS A COUNTRY IN ACCESSION, AND WITH THAT SEVERAL SECTORS OF THE ECONOMY HAVE BEEN GROWING ALONG WITH THIS ADVANCE. THE FOUNDRY AREA IS FOLLOWING THIS RISE, WITH BRAZIL BEING THE SEVENTH LARGEST PRODUCER OF CASTINGS IN THE WORLD, AND THIS ACTIVITY GENERATES SOLID WASTE, THE SO-CALLED GREEN SAND BEING THE MAIN ONE. THE OBJECTIVE OF THIS WORK IS TO REPLACE THE FINE CONCRETE AGGREGATE WITH THE FOUNDRY WASTE. THE 3:2:1 LINE (SAND: GRAVEL: CEMENT) WAS USED TO MAKE THE SPECIMENS, RESPECTIVELY. AFTER VERIFYING VALUES OBTAINED IN A TEST WITH SPECIMEN WITHOUT INCORPORATION, DASHES WERE MADE REPLACING WITH DIFFERENT PERCENTAGES OF FOUNDRY TAILINGS. THE SPECIMENS WERE CURED AT ROOM TEMPERATURE FOR 7 AND 28 DAYS, AND IMMEDIATELY AFTERWARDS THEY WERE SUBJECTED TO COMPRESSION TESTS WHERE THEY HAD A SHEARED RUPTURE AND DIFFERENT VALUES OF RESISTANCE LIMIT (MPA). IT CAN BE CONCLUDED WITH THIS STUDY THAT THERE IS A FEASIBILITY OF PARTIALLY REPLACING THE FINE AGGREGATE OF THE CONCRETE WITH THE FOUNDRY WASTE.

Palavras-chave

Resíduo de Fundição; Concreto; Sustentabilidade.

Foundry Waste; Concrete; Sustainability