Título

ANÁLISE DO TEOR DE MANGANÊS E CROMO NO ENCRUAMENTO POR IMPACTO DOS AÇOS AUSTENÍTICOS AO MANGANÊS

ANALYSIS OF MANGANESE AND CHROMIUM CONTENTS ON HARDENING BY IMPACT OF AUSTENITIC MANGANESE STEELS

Autoria

Trindade, Adriel de Brito Maciel; Silva, Gilson Neves da; Rossino, Luciana Sgarbi

Trindade, Adriel de Brito Maciel

Eu sou esse autor

Silva, Gilson Neves da

Eu sou esse autor

Rossino, Luciana Sgarbi

Eu sou esse autor

DOI

10.5151/2594-5327-34264

Downloads

Resumo

DENTRE OS MATERIAIS FERROSOS DESENVOLVIDOS PARA A RESISTÊNCIA AO DESGASTE, ESTÃO OS AÇOS AUSTENÍTICOS AO MANGANÊS (HADFIELD). TAIS MATERIAIS POSSUEM ALTA TENACIDADE AO IMPACTO E RESISTÊNCIA AO DESGASTE POR ABRASÃO SIMULTANEAMENTE, FATOR QUE OS TORNARAM GRANDEMENTE ACEITOS NO SETOR DE MINERAÇÃO, FÉRREO E DE RECICLAGEM. COM FINALIDADE DE ANALISAR O EFEITO DOS TEORES DE MANGANÊS E CROMO NO ENCRUAMENTO POR IMPACTO DESSES MATERIAIS, FORAM ESTUDADAS TRÊS LIGAS COM COMPOSIÇÕES DISTINTAS, VARIANDO O PERCENTUAL DOS ELEMENTOS QUÍMICOS CITADOS. AS LIGAS FORAM CARACTERIZADAS POR ANÁLISE METALOGRÁFICA E PERFIL DE MICRODUREZA VICKERS. ENSAIOS DE ENCRUAMENTO POR IMPACTO FORAM UTILIZADOS PARA DETERMINAR A INFLUÊNCIA DOS ELEMENTOS DE LIGA CROMO E MANGANÊS NA CAPACIDADE DE ENCRUAMENTO DO MATERIAL ESTUDADO. OS RESULTADOS OBTIDOS DEMONSTRARAM QUE AS COMPOSIÇÕES POSSUINDO MAIORES PERCENTUAIS DE MANGANÊS E CROMO TENDEM A PRODUZIREM MAIOR DUREZA SUPERFICIAL APÓS ENCRUAMENTO, SENDO O MANGANÊS O ELEMENTO DE MAIOR RELEVÂNCIA PARA TAL. FOI DEMONSTRADO SIMULTANEAMENTE QUE AÇOS DE COMPOSIÇÃO PADRÃO DA ASTM A 128, CONTENDO BAIXO PERCENTUAL DE CROMO, APRESENTAM MAIOR DEFORMAÇÃO COM MENOR ENDURECIMENTO SUPERFICIAL, SENDO ESTE COMPORTAMENTO VINCULADO AO MECANISMO DE DEFORMAÇÃO PLÁSTICA E O TEOR DE CR CONTIDO.

AMONG FERROUS MATERIALS APPLIED FOR WEAR, IT’S THE HADFIELD MANGANESE STEELS. SUCH MATERIALS PRESENT HIGH TOUGHNESS AND WEAR ABRASION RESISTANCE SIMULTANEOUSLY, WHICH LEADS IT TO BECOME WELL ACCEPTED FOR MINING, RAIL AND RECYCLING BUSINESSES. THE TARGET IS TO EVALUATE THE EFFECTS OF MANGANESE AND CHROMIUM CONTENTS ON WORK HARDENING BY IMPACT OF THIS ALLOY. IT WAS EVALUATED THREE DIFFERENT CHEMICAL COMPOSITIONS, VARYING THE PERCENTAGE OF THE MENTIONED ELEMENTS. ALLOYS WERE CHARACTERIZED BY OPTICAL MICROSCOPY, SCANNING ELECTRONIC MICROSCOPY AND PROFILE OF VICKERS MICROHARDNESS. OBTAINED RESULTS EVIDENCED THE CHEMICAL COMPOSITIONS PRESENTING HIGHER PERCENTAGES OF MANGANESE AND CHROMIUM PRODUCE HIGHER SURFACE HARDNESS AFTER WORK HARDENING, BEING MANGANESE THE MORE RELEVANT ELEMENT FOR THAT. IT WAS DEMONSTRATED AT THE SAME TIME THAT STEELS WITH STANDARD CHEMICAL COMPOSITION, GIVEN BY ASTM A 128 PRESENTING LOWER CHROMIUM PERCENTAGE, PRESENTED HIGHER DEFORMATION WITH LOWER SURFACE WORK HARDENING, BEING THIS BEHAVIOR LINKED TO THE MECHANISM OF PLASTIC DEFORMATION AND CHROMIUM CONTENTS.

Palavras-chave

Aço hadfield; Cromo; Manganês; Encruamento;

Hadfield steel; Chromium; Manganese; Work Hardening;