Título

ANÁLISE E DETERMINAÇÃO DA MICROESTRUTURA E DUREZA DO MAGNÉSIO PURO 9980A E LIGA EZ33 PROCESSADOS POR ECAP

DETERMINATION AND ANALYSIS OF MICROSTRUCTURE AND HARDNESS OF COMMERCIALLY PURE MAGNESIUM 9980A AND MAGNESIUM ALLOY EZ33 PROCESSED BY ECAP

Autoria

Filho, José Amilton Cardoso de Oliveira; Saraiva, Breno Rabelo Coutinho; Neto, João Rodrigues de Barros; Gömes, Francisco Bruno Alexandre; Abreu, Hamilton Ferreira Gomes de; Leiva, Daniel Rodrigo; Silva, Wágner Batista

DOI

10.5151/2594-5327-34669

Downloads

Baixar Artigo 8 Downloads

Resumo

O INTERESSE NO MAGNÉSIO E SUAS LIGAS CRESCE EXPONENCIALMENTE, PRINCIPALMENTE POR SUAS MELHORES PROPRIEDADES MECÂNICAS ALIADAS À BAIXA DENSIDADE, SENDO AMPLAMENTE APLICADOS NA INDÚSTRIA AUTOMOBILÍSTICA. O PRESENTE TRABALHO VISA APRIMORAR AS PROPRIEDADES MECÂNICAS DO MAGNÉSIO PURO E LIGA EZ33 ATRAVÉS DO PROCESSAMENTO POR ECAP, COM O OBJETIVO DE ANALISAR O EFEITO DA TEMPERATURA NA DUREZA EM RELAÇÃO À MICROESTRUTURA. NO ECAP, UTILIZOU-SE UMA MATRIZ DE CANAL INTERNO DE 120º COM PARÂMETROS DE PROCESSO, POR AMOSTRA, DE: ROTA BC COM AS CONDIÇÕES DE 4 PASSES A 300ºC, A 250ºC E CONDIÇÃO M (1 PASSE A 300ºC, A 275ºC, A 250ºC E A 225ºC) A UMA VELOCIDADE DE PRENSAGEM DE 5 MM/MIN. FORAM, ENTÃO, REALIZADAS ANÁLISES DE MICROSCOPIA ÓPTICA, EDS E DUREZA EM TODAS AS AMOSTRAS. A LIGA DEMONSTROU RESULTADOS PROMISSORES, COM VALORES MAIORES DE DUREZA EM RELAÇÃO À COMO RECEBIDA, PRINCIPALMENTE NA CONDIÇÃO M, COM AUMENTO DE CERCA DE 15% E, PARA O MG PURO, 32%. A MICROESTRUTURA REVELOU A REDUÇÃO DE CERCA DE 57 VEZES NO TAMANHO DO GRÃO, E, NO MG PURO, CERCA DE 37 VEZES. POR CONSEGUINTE, AS LIGAS DE MAGNÉSIO PROCESSADAS POR ECAP SÃO EFICIENTEMENTE OTIMIZADAS ANALISANDO A DUREZA, CONTRIBUINDO PARA APLICAÇÕES DE MAIOR QUALIDADE NA INDÚSTRIA.

 

THE INTEREST IN MAGNESIUM ALLOYS HAS BEEN EXPONENTIALLY GROWN, DUE TO ITS BETTER MECHANICAL PROPERTIES BOUND TO LOW DENSITY COMPARED WITH OTHER METALS, BEING WIDELY QUALIFIED IN AUTOMOTIVE INDUSTRIES. THIS SCIENTIFIC WORK PURSUES TO IMPROVE THE MECHANICAL PROPERTIES OF PURE MAGNESIUM AND ITS ALLOY EZ33 THROUGH THE ECAP TECHNIQUE, CRUCIALLY AIMING TO ANALYSE THE TEMPERATURE’S EFFECT ON HARDNESS AND RELATE WITH THE MICROSTRUCTURE. THE ECAP PROCESS HAVE BEEN MADE USING A DIE WITH PROCESS PARAMETERS SUCH AS INTERNAL CHANNEL OF 120º AND USING THE BC ROUTE, FOLLOWING, EACH SAMPLE, THE EXTRUSION SEQUENCE CONDITIONS: 4 PASSES AT 300ºC, THEN AT 250ºC AND CONDITION M (1 PASS AT 300ºC, AT 275ºC, AT 250ºC AND 225ºC), WITH A PRESSING SPEED OF 5 MM/MIN. THEN, THE ANALYSES WERE MADE: MICROSTRUCTURE, EDS, AND HARDNESS. THE ALLOY SHOWED PROMISING RESULTS, PRESENTING HIGHER VALUES IN ITS MECHANICAL PROPERTIES, MAINLY ON M CONDITION, INCREASING APPROXIMATELY 15% IN HARDNESS, AND, FOR THE PURE MG, 32%. THE MICROSTRUCTURE REVEALED THE DIMINISHING OF ABOUT 57 AND 37 TIMES IN GRAIN SIZE FOR THE ALLOY AND PURE MG, RESPECTIVELY. HENCE, THE MAGNESIUM ALLOYS PROCESSED BY ECAP ARE CONSIDERABLY OPTIMIZED IN THEIR MECHANICAL AND MICROSTRUCTURAL PROPERTIES, CONTRIBUTING TO HIGHER QUALITY APPLICATIONS.

Palavras-chave

Magnésio Puro; Equal Channel Angular Pressing; Liga de magnésio EZ33; Caracterização Microestrutural

Pure Magnesium; Equal Channel Angular Pressing; Magnesium alloy EZ33; Hardness; Microstructural Char