ANÁLISE ESTATÍSTICA DA INFLUÊNCIA DAS VARIÁVEIS DO PROCESSO DE SOLDAGEM DE BOBINAS LAMINADAS A FRIO NO DESEMPENHO MECÂNICO DAS UNIÕES PRODUZIDAS: STATISTICAL ANALYSIS OF WELDING PROCESS VARIABLES’ INFLUENCE ON MECHANICAL PERFORMANCE OF UNIONS AMONG COLD ROLLED STRIP STEEL COILS

Silva, Antonio Marlon; Litz, Andrés; Solé, Rubén; Domingues, Ricardo

doi:10.5151/2594-5297-20704

Anais do Seminário de Laminação, Conformação de Metais e Produtos

ISSN 2594-5297

48º Seminário de Laminação, Processos e Produtos Laminados e Revestidos — vol. 48, num.48 (2011)

Título

ANÁLISE ESTATÍSTICA DA INFLUÊNCIA DAS VARIÁVEIS DO PROCESSO DE SOLDAGEM DE BOBINAS LAMINADAS A FRIO NO DESEMPENHO MECÂNICO DAS UNIÕES PRODUZIDAS

STATISTICAL ANALYSIS OF WELDING PROCESS VARIABLES’ INFLUENCE ON MECHANICAL PERFORMANCE OF UNIONS AMONG COLD ROLLED STRIP STEEL COILS

Autoria

Silva, Antonio Marlon; Litz, Andrés; Solé, Rubén; Domingues, Ricardo

10.5151/2594-5297-20704

Downloads

Baixar Artigo 97 Downloads

Resumo

Este trabalho, realizado na empresa Ternium Siderar, San Nicolás, Argentina, objetivou o estudo da influência da corrente, da pressão, do tempo de aplicação da corrente e da velocidade de soldagem na carga máxima de ruptura da solda feita em chapas laminadas a frio que seguirão para o processo de limpeza eletrolítica. Para o cálculo da importância de cada variável e das interações entre elas, analisaram-se k os resultados dos ensaios de tração das soldas com o projeto de experimento, 2 , o que possibilitou escolher as combinações que fornecessem os resultados mais relevantes. Ensaios de tração realizados em três amostras retiradas dos cordões de solda permitiram medir a carga de ruptura. Foram observadas a microestrutura e a ocorrência de trincas na zona de fusão da solda. Para as chapas de 0,20mm, a velocidade, corrente e a interação corrente-pressão são as variáveis de maior peso. Para a espessura de 0,45mm o maior peso recai na velocidade, no tempo e nas interações velocidade-tempo e pressão-tempo. Este estudo permitirá reduzir o atraso no processo de limpeza eletrolítica e evitará a exposição de operários ao risco de acidentes durante o reposicionamento da chapa dentro do tanque.

This work, performed at Ternium Siderar, San Nicolás, Argentina, has aimed the study of the influence of current, pressure, current application interval and welding speed on the maximum rupture load of welded cold rolled sheets to be sent to electrolytic cleaning process. For the calculation of the importance of each variable and the interactions between them, results of tension tests made on the welds had been analyzed with the experimental design technique, 2k, that made possible choosing the combinations that supplied the most relevant results. Tension tests made on three samples of weld seam had allowed measuring the rupture load. The microstructure and cracking occurrence in the weld fusion zone had been observed. For 0,20mm thick sheets, speed, current and interaction current-pressure are the most significant variables. For 0,45mm thick sheets, the greatest significance is on speed, time and interactions speed-time and pressure-time. This study will allow reducing the delay in electrolytic cleaning process and will prevent the exposition of workers to the risk of accidents during the repositioning of sheets inside the tank.

Palavras-chave

Soldagem por costura a ponto; análise estatística; laminação a frio.

Seam-spot welding; statistical analysis; cold rolling.

Como citar

Silva, Antonio Marlon; Litz, Andrés; Solé, Rubén; Domingues, Ricardo. ANÁLISE ESTATÍSTICA DA INFLUÊNCIA DAS VARIÁVEIS DO PROCESSO DE SOLDAGEM DE BOBINAS LAMINADAS A FRIO NO DESEMPENHO MECÂNICO DAS UNIÕES PRODUZIDAS , p. 796-806. In: 48º Seminário de Laminação, Processos e Produtos Laminados e Revestidos, Santos, 2011.