APLICAÇÃO DE SOLUÇÃO ALCALINA EM CERÂMICA VERMELHA

APPLICATION OF ALKALINE SOLUTION IN RED CERAMICS

Autoria

Marvila, Markssuel Teixeira; Azevedo, Afonso Rangel Garcez de; Delaqua, Geovana Carla Girondi; Zanelato, Euzébio Bernabé; Barbosa, Victor de Souza; Lima, Thuany Espirito Santo; Monteiro, Sergio Neves; Xavier, Gustavo Castro; Aguiar, Niander Cerqueira; Vieira, Carlos Maurício Fontes

DOI

10.5151/2594-5327-34038

Downloads

Baixar Artigo 27 Downloads

Resumo

O PRINCIPAL MECANISMO RESPONSÁVEL PELA RESISTÊNCIA EM CERÂMICA VERMELHA É A FORMAÇÃO DE FASE LIQUIDA ATRAVÉS DA PRESENÇA DE ÓXIDOS FUNDENTES ALCALINOS. SABE-SE QUE AS ARGILAS DE CAMPOS DOS GOYTACAZES, RJ, APRESENTAM DEFICIÊNCIA DESSES COMPONENTES. POR ISSO O OBJETIVO DESSE TRABALHO É CORRIGIR OS TEORES ALCALINOS DA MATÉRIA PRIMA ATRAVÉS DA UTILIZAÇÃO DE UMA SOLUÇÃO ALCALINA. FORAM CONFECCIONADOS CORPOS DE PROVA POR PRENSAGEM COM 8% DE UMIDADE EM SOLUÇÃO ALCALINA 10M E QUEIMADOS A TEMPERATURA DE 400, 600 E 800ºC, TENDO SIDO PRODUZIDO TAMBÉM UMA CERÂMICA DE CONTROLE QUEIMADA A 800ºC. OS RESULTADOS DE RETRAÇÃO LINEAR, ABSORÇÃO DE ÁGUA, POROSIDADE E RESISTÊNCIA MECÂNICA COMPROVAM QUE A UTILIZAÇÃO DA SOLUÇÃO ALCALINA PERMITE A OBTENÇÃO DE COMPOSTOS MAIS RESISTENTES E COM MELHORES PROPRIEDADES EM 400ºC DO QUE OS MESMOS CORPOS DE PROVA UMEDECIDOS COM ÁGUA QUEIMADOS A 800ºC. ESSA CARACTERÍSTICA PERMITE UMA ECONOMIA AO SETOR CERÂMICO, UMA VEZ QUE ETAPA MAIS CUSTOSA PARA O SETOR É A ETAPA DE QUEIMA DOS CORPOS DE PROVA E REDUZIR A TEMPERATURA DE QUEIMA PELA METADE É UMA GRANDE VANTAGEM ECONÔMICA

 

THE MAIN MECHANISM RESPONSIBLE FOR THE RESISTANCE IN RED CERAMIC IS THE FORMATION OF A LIQUID PHASE THROUGH THE PRESENCE OF ALKALINE FLUXING OXIDES. IT IS KNOWN THAT THE CLAYS IN CAMPOS DOS GOYTACAZES, RJ, PRESENT DEFICIENCY OF THESE COMPONENTS. THEREFORE, THE OBJECTIVE OF THIS WORK IS TO CORRECT THE ALKALINE CONTENTS OF THE RAW MATERIAL THROUGH THE USE OF AN ALKALINE SOLUTION. TEST SPECIMENS WERE MADE BY PRESSING 8% MOISTURE IN A 10M ALKALINE SOLUTION AND FIRED AT 400, 600 AND 800ºC, AND A CONTROL CERAMIC BURNED AT 800ºC WAS ALSO PRODUCED. THE RESULTS OF LINEAR SHRINKAGE, WATER ABSORPTION, POROSITY AND MECHANICAL RESISTANCE PROVE THAT THE USE OF THE ALKALINE SOLUTION ALLOWS TO OBTAIN MORE RESISTANT COMPOUNDS WITH BETTER PROPERTIES AT 400ºC THAN THE SAME SPECIMENS MOISTENED WITH WATER BURNED AT 800ºC. THIS CHARACTERISTIC ALLOWS SAVINGS TO THE CERAMIC SECTOR, SINCE THE MOST EXPENSIVE STEP FOR THE SECTOR IS THE STAGE OF BURNING THE SPECIMENS AND REDUCING THE TEMPERATURE OF THE FIRING IN HALF IS A GREAT ECONOMIC ADVANTAGE

Palavras-chave

Cerâmica Vermelha; Solução Alcalina; Fase líquida

Red Ceramics; Alkaline Solution; Liquid phase