AVALIAÇÃO DA INFLUÊNCIA DA NITRETAÇÃO NA TEXTURA CRISTALOGRÁFICA APÓS A RECRISTALIZAÇÃO PRIMÁRIA DE UM AÇO ELÉTRICO DE GRÃO ORIENTADO

EVALUATION OF THE INFLUENCE OF NITRIDING ON CRYSTALLOGRAPHIC TEXTURE AFTER PRIMARY RECRYSTALLIZATION IN A GRAIN ORIENTED ELECTRICAL STEEL

DOI

10.5151/1516-392X-313

Downloads

Baixar Artigo 57 Downloads

Resumo

Com o crescimento da demanda energética mundial, faz-se necessário a implantação de recursos tecnológicos eficientes para reduzir o consumo de energia. Nesse contexto, os aços elétricos de grão orientado (GO) têm sido estudados com o objetivo de aperfeiçoar suas propriedades magnéticas, uma vez que sua principal aplicação é em núcleo de transformadores. As propriedades magnéticas desses aços estão condicionadas à orientação preferencial dos grãos, que, por sua vez, está relacionada aos precipitados, pois eles inibem o crescimento normal dos grãos durante a recristalização secundária. Neste trabalho estudou-se a influência do tratamento de nitretação na textura cristalográfica após a recristalização primária em um aço GO avaliando a condição de 0,30 Nm3/h de injeção de amônia em comparação ao processamento sem injeção de amônia. A textura cristalográfica foi determinada por difração de raios X. Alguns precipitados foram identificados na amostra nitretada e avaliados quanto ao tipo, forma e tamanho com o auxílio de um MET Jeol LaB6, foram obtidos figuras de difração e realizado análise qualitativa por EDS. Os resultados sugerem a precipitação de nitretos e um fortalecimento da componente de textura próxima a fibra γ do aço processado em atmosfera com amônia, após a descarbonetação.

 

With the growth of global energy demand, it is necessary to deploy efficient technological resources to reduce energy consumption. In this context, grain oriented electrical steels (GO) have been studied with the objective of improving their magnetic properties, since their main application is in transformers core. The magnetic properties of these steels are conditioned to the preferred orientation of the grains, which is related to the precipitates that inhibit normal grain growth during secondary recrystallization. This study investigated the influence of nitriding treatment in crystallographic texture after primary recrystallization from a GO steel evaluating the condition of 0.30 Nm3 / h of ammonia injection in comparison to the processing without ammonia injection. The crystallographic texture was determined by X-ray diffraction. Some nitride precipitates were identified in the sample and evaluated for the type, shape and size with the aid of a TEM JEOL LaB6, diffraction figures were obtained and qualitative analysis carried out by EDS. The results suggest the precipitation of nitrites and a strengthening of the texture component next to the γ fiber of the steel processed in atmosphere with ammonia, after decarburizing annealing.

Palavras-chave

Aço elétrico de grão orientado; precipitados; nitretação; textura cristalográfica.

grain oriented electrical steel; precipitate; nitriding; crystallographic texture.

Como citar

Oliveira, Marcelly Quintão; Cruz, Bruna Madeira Araújo da; Santana, Simone Izabel Vieira de; Brandão, Luíz Paulo Mendonça. AVALIAÇÃO DA INFLUÊNCIA DA NITRETAÇÃO NA TEXTURA CRISTALOGRÁFICA APÓS A RECRISTALIZAÇÃO PRIMÁRIA DE UM AÇO ELÉTRICO DE GRÃO ORIENTADO , p. 3100-3108. In: 73º Congresso Anual da ABM, São Paulo, 2018.