AVALIAÇÃO DA MICROESTRUTURA E TAXAS DE CORROSÃO DE CUPONS DE AÇO AISI 1020 SUBMETIDOS AO TRATAMENTO TÉRMICO DE NORMALIZAÇÃO: EVALUATION OF MICROSTRUCTURE AND CORROSION RATES OF AISI 1020 STEEL COUPONS SUBMITTED TO NORMALIZATION HEAT TREATMENT

CUPONS DE PERDA DE MASSA SãO EMPREGADOS NO MONITORAMENTO DE PROCESSOS CORROSIVOS E FORNECEM DOIS TIPOS DE INFORMAçãO, A CORROSIVIDADE DO AMBIENTE E O DANO QUE A INSTALAçãO SOFRE. AS EMPRESAS DE MONITORAMENTO ADQUIREM CUPONS DE DIFERENTES FORNECEDORES, E POUCO SE OBSERVA QUANTO AO TIPO DE PROCESSAMENTO, COMPOSIçãO, MICROESTRUTURA, TIPO DE TRATAMENTO TéRMICO ENTRE OUTROS PARâMETROS E O QUANTO, PODEM INFLUENCIAR NA CONFIABILIDADE DOS RESULTADOS. O PRESENTE TRABALHO TEM COMO OBJETIVO AVALIAR A INFLUêNCIA DO TRATAMENTO TéRMICO DE NORMALIZAçãO NA MICROESTRUTURA E NAS TAXAS DE CORROSãO UNIFORME E POR PITES EM CUPONS DE CORROSãO DE AçO AISI 1020, QUE FORAM SECCIONADOS DAS SEçõES LONGITUDINAL E TRANSVERSAL DE UM TARUGO. OS CUPONS FORAM ENSAIADOS EM LOOP DE CORROSãO TENDO COMO FLUIDO A áGUA POTáVEL. AS TAXAS DE CORROSãO UNIFORME E PUNTIFORME FORAM DETERMINADAS DE ACORDO COM A NORMA NACE RP0775. NA CARACTERIZAçãO MICROESTRUTURAL FORAM ENVOLVIDAS ANáLISES POR MICROSCOPIA óPTICA, OBSERVANDO O TAMANHO DE GRãO, ALéM DA MEDIçãO DE DUREZA VICKERS. OS CUPONS TRATADOS TERMICAMENTE APRESENTARAM TAMANHO DE GRãO E MORFOLOGIA DIFERENTES DOS CUPONS NO ESTADO COMO RECEBIDO. FOI OBSERVADA MAIOR DENSIDADE DE INCLUSõES NOS CUPONS SECCIONADOS DA SEçãO LONGITUDINAL, SENDO POSSíVEL ESTABELECER UMA RELAçãO DIRETA COM A TAXA DE CORROSãO POR PITES. QUANTO à CORROSãO UNIFORME, TODOS OS CUPONS TIVERAM A CLASSIFICAçãO QUALITATIVA COMO MODERADA. QUANTO à CORROSãO PUNTIFORME, TODOS OS CUPONS TIVERAM A CLASSIFICAçãO QUALITATIVA COMO SEVERA.

MASS LOSS COUPONS ARE USED IN MONITORING OF CORROSIVE PROCESSES AND PROVIDE TWO TYPES OF INFORMATION, THE CORROSITY OF THE ENVIRONMENT AND THE DAMAGE THAT THE INSTALLATION SUFFERS. MONITORING COMPANIES OBTAIN COUPONS FROM DIFFERENT SUPPLIERS, AND LITTLE NOTES ABOUT THE TYPE OF PROCESSING, COMPOSITION, MICROSTRUCTURE, TYPE OF HEAT TREATMENT, BETWEEN OTHER PARAMETERS AND HOW THEY CAN INFLUENCE IN THE CONFIABILITY OF THE RESULTS. THE PRESENT WORK AIMS TO EVALUATE THE INFLUENCE OF NORMALIZING HEAT TREATMENT ON MICROSTRUCTURE AND ON UNIFORM AND PITTING CORROSION RATES IN AISI 1020 STEEL CORROSION COUPONS, WHICH WERE SECTIONED FROM LONGITUDINAL AND TRANSVERSE SECTIONS OF A BILLET. THE COUPONS WERE TESTED FOR CORROSION LOOP HAVING AS FLUID POTABLE WATER. THE UNIFORM AND PUNTIFORM CORROSION RATES WERE DETERMINED ACCORDING TO THE STANDARD NACE RP0775. THE MICROSTRUCTURAL CHARACTERIZATION ANALYZES BY OPTICAL MICROSCOPY WERE INVOLVED, OBSERVING THE GRAIN SIZE, IN ADDITION TO THE MEASUREMENT OF VICKERS HARDNESS. HEAT-TREATED COUPONS HAVE DIFFERENT GRAIN SIZE AND MORPHOLOGY THAN COUPONS IN THE STATE AS RECEIVED. A HIGHER DENSITY OF INCLUSIONS WAS OBSERVED IN THE SECTIONED COUPONS OF THE LONGITUDINAL SECTION, BEING POSSIBLE TO ESTABLISH A DIRECT RELATIONSHIP WITH PITTING CORROSION RATE. AS FOR UNIFORM CORROSION, ALL COUPONS HAD THE QUALITATIVE RATING AS MODERATE. AS FOR PUNCTURE CORROSION, ALL COUPONS HAD THE QUALITATIVE CLASSIFICATION AS SEVERE.

Palavras-chave

Cupons; Tratamento térmico; corrosão uniforme; corrosão puntiforme.

Coupons; Heat treatment; Uniform corrosion; Puntiform corrosion.

Como citar

SOUZA, SHAYANA TAVARES DE; VIEIRA, WANDER PACHECO; MENDES, SILVIO GONÇALVES; GOMES, GUSTAVO DE AZEVEDO BARRETO; PEREIRA, ELAINE CRISTINA. AVALIAÇÃO DA MICROESTRUTURA E TAXAS DE CORROSÃO DE CUPONS DE AÇO AISI 1020 SUBMETIDOS AO TRATAMENTO TÉRMICO DE NORMALIZAÇÃO , p. 1257-1264. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-40733