AVALIAÇÃO DAS PROPRIEDADES MECÂNICAS DE UMA ARGAMASSA GEOPOLIMÉRICA REFORÇADA COM FIBRAS DE AÇAÍ: EVALUATION OF THE MECHANICAL PROPERTIES OF A GEOPOLYMER MORTAR REINFORCED WITH AÇAÍ FIBERS

AS FIBRAS NATURAIS LIGNOCELULóSICAS (FNL) APRESENTAM POTENCIAL DE SEREM UTILIZADOS COMO MATERIAIS SUSTENTáVEIS NA INDúSTRIA DA CONSTRUçãO CIVIL EM GEOPOLíMEROS DEVIDO AS SUAS MELHORIAS EM PROPRIEDADES COMO RESISTêNCIA à TRAçãO, FLEXãO E POR TORNAR OS COMPOSTOS MAIS LEVES. NESSE CONTEXTO, ESTãO AS FIBRAS DE AçAí, QUE SãO OBTIDAS APóS APROVEITAMENTO DA POLPA, A QUAL REQUER DESTINAçãO FINAL E, GERALMENTE, ACABA EM ATERRO SANITáRIO. ASSIM, O OBJETIVO DESSE TRABALHO FOI DE PRODUZIR COMPOSTOS GEOPOLIMéRICOS REFORçADOS COM FIBRAS DE AçAí E AVALIAR AS PROPRIEDADES DA ARGAMASSA QUANDO A ADIçãO DE FIBRAS DE AçAí EM 1 E 2% (EM MASSA?) SEM TRATAMENTO E TRATADAS COM NAOH COM A CONCENTRAçãO DE 5 E 10% POR MEIO DOS ENSAIOS DE RESISTêNCIA à COMPRESSãO E RESISTêNCIA à FLEXãO, ALéM DA ABSORçãO DE áGUA DAS FIBRAS. OS RESULTADOS MOSTRARAM QUE A ADIçãO DE 2% DE FIBRAS AçAí TRATADAS COM 5% DE NAOH APRESENTOU OS MELHORES RESULTADOS DE RESISTêNCIA à COMPRESSãO E TRAçãO, INDICANDO QUE O TRATAMENTO ALCALINO FOI EFICAZ PARA REMOVER OS COMPONENTES AMORFOS QUAIS? E CONSEQUENTEMENTE MELHORAR A INTERAçãO FIBRA-MATRIZ GEOPOLIMéRICA. ASSIM, O GEOPOLíMERO COM ADIçãO DE FIBRAS DE AçAí APRESENTA UM POTENCIAL DE APLICAçãO NO SEGMENTO DA CONSTRUçãO CIVIL COMO UM MATERIAL SUSTENTáVEL.

NATURAL LIGNOCELLULOSIC FIBERS HAVE THE POTENTIAL TO BE USED AS SUSTAINABLE MATERIALS IN THE CONSTRUCTION INDUSTRY IN GEOPOLYMERS DUE TO THEIR IMPROVEMENTS IN PROPERTIES SUCH AS TENSILE STRENGTH, FLEXION AND FOR MAKING THE COMPOUNDS LIGHTER. IN THIS CONTEXT, THERE ARE AçAí FIBERS, WHICH ARE OBTAINED AFTER USING THE PULP AND REQUIRE FINAL DISPOSAL AND GENERALLY END UP IN LANDFILLS. THUS, THE OBJECTIVE OF THIS WORK WAS TO PRODUCE GEOPOLYMERIC COMPOUNDS REINFORCED WITH AçAí FIBERS AND EVALUATE THE PROPERTIES OF GEOPOLYMERIC MORTAR REINFORCED WITH THE ADDITION OF AçAí FIBERS AT 1 AND 2% WITHOUT TREATMENT AND TREATED WITH NAOH AT A CONCENTRATION OF 5 AND 10% PER THROUGH COMPRESSION RESISTANCE AND FLEXURAL RESISTANCE TESTS, IN ADDITION TO WATER ABSORPTION OF THE FIBERS. THE RESULTS SHOWED THAT THE ADDITION OF 2% AçAí FIBERS TREATED WITH 5% NAOH PRESENTED THE BEST RESULTS IN COMPRESSIVE AND TENSILE STRENGTH, INDICATING THAT THE ALKALINE TREATMENT WAS EFFECTIVE IN REMOVING AMORPHOUS COMPONENTS AND CONSEQUENTLY IMPROVING THE FIBER-GEOPOLYMERIC MATRIX INTERACTION. THUS, THE GEOPOLYMER WITH THE ADDITION OF AçAí FIBERS HAS POTENTIAL FOR APPLICATION IN THE CIVIL CONSTRUCTION SEGMENT AS A SUSTAINABLE MATERIAL.

Palavras-chave

Fibras de açaí; Geopolímero; Tratamento alcalino; Propriedades mecânicas.

Açaí fibers, Geopolymer, Alkaline treatment, Mechanical Properties.

Como citar

OLIVEIRA, LEANDRO BARBOSA DE; BARRAZA, MADELEING TABORDA; MARVILA, MARKSSUEL TEIXEIRA; MONTEIRO, SÉRGIO NEVES; VIEIRA, CARLOS MAURÍCIO FONTES; AZEVEDO, AFONSO RANGEL GARCEZ DE. AVALIAÇÃO DAS PROPRIEDADES MECÂNICAS DE UMA ARGAMASSA GEOPOLIMÉRICA REFORÇADA COM FIBRAS DE AÇAÍ , p. 937-946. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-40614