AVALIAÇÃO MICROESTRUTURAL DO AÇO AISI 310 SUBMETIDO A ENSAIOS DE FLUÊNCIA : MICROSTRUCTURAL EVALUATION OF AISI 310 STEEL SUBMITTED TO CREEP TESTS

NESSE ESTUDO FOI FEITA A AVALIAÇÃO DA MICROESTRUTURA DO AÇO AISI 310 PREVIAMENTE SUBMETIDO A ENSAIOS DE FLUÊNCIA, EM TEMPERATURA E TEMPO DE RUPTURA, ENTRE 650 °C A 700° E 2 A 1.231H, FORAM AVALIADOS. A EVOLUÇÃO MICROESTRUTURAL FOI ESTUDADA ATRAVÉS DE ENSAIOS DE DIFRAÇÃO DE RAIOS X, MICROSCOPIA ÓPTICA E ELETRÔNICA DE VARREDURA E MICRODUREZA VICKERS. FOI VERIFICADO A PRECIPITAÇÃO DE CARBONETOS, FASE SIGMA E LAVES, VARIANDO AO LONGO DO TEMPO DE EXPOSIÇÃO, VISTO PELOS PICOS DO DIFRATOGRAMA ACOMPANHADOS DA VISUALIZAÇÃO EM MICROSCOPIA. A MICRODUREZA DEMONSTROU UMA TENDENCIA DE ACRÉSCIMO SUCEDIDA DE DECRESCIMENTO, SEGUINDO A TRANSFORMAÇÃO DA FASE SIGMA NA MATRIZ, DEMONSTRANDO BOAS RELAÇÕES ENTRE AS TEMPERATURAS E TEMPOS DE RUPTURA COM A MICROESTRUTURA E O TEMPO DE ENVELHECIMENTO E, EM ESPECIAL, COM A FASE LAVES PARA AUMENTO DA RESISTÊNCIA A FLUÊNCIA DO MATERIAL, SENDO IMPORTANTE FONTE DE OTIMIZAÇÃO DA SUA APLICAÇÃO E MANUTENÇÃO.

IN THIS STUDY, THE MICROSTRUCTURE OF AISI 310 STEEL, PREVIOUSLY CREEP TESTED UNTIL RUPTURE, WAS EVALUATED. IN TEMPERATURE AND TIME CONDITIONS BETWEEN 650 °C AND 700 °C AND 2 TO 1,231 H, RESPECTIVELY. TO EVALUATE THE MICROSTRUCTURAL EVOLUTION, X-RAY DIFFRACTION, OPTICAL AND SCANNING ELECTRON MICROSCOPY AND VICKERS MICRO-HARDNESS TESTS WERE PERFORMED. CARBIDE, SIGMA PHASE AND LAVES PHASES HAVE BEEN OBSERVED, VARYING OVER TIME OF EXPOSURE, AS SEEN BY THE DIFFRACTOGRAM PEAKS ACCOMPANIED BY MICROSCOPIC VISUALIZATION. MICROHARDNESS INCREASES PURSUED BY A DECREASING, FOLLOWING THE TRANSFORMATION OF THE SIGMA PHASE IN THE MATRIX, DEMONSTRATING GOOD RELATIONSHIPS BETWEEN THE RUPTURE TEMPERATURES AND TIMES WITH THE MICROSTRUCTURE AND AGEING TIME OF THE MATERIAL AND, SPECIALLY, WITH THE LAVES PHASE TO INCREASE THE CREEP RESISTANCE OF THE MATERIAL, BEING, AN IMPORTANT POINT TO OPTIMIZE ITS APPLICATION AND MAINTENANCE.

Palavras-chave

Envelhecimento por fluência; M23 C6; Fase sigma; Fase Laves.

Ageing by creep; M23 C6; Sigma phase; Laves phase.

Como citar

Garcia, Julianna Magalhães; Monteiro, Ana Carolina Accioly; Casanova, Andréy de Moraes Barcelos; Carvalho, Iana Costa; Brandao, Luiz Paulo. AVALIAÇÃO MICROESTRUTURAL DO AÇO AISI 310 SUBMETIDO A ENSAIOS DE FLUÊNCIA , p. 436-449. In: 75° Congresso Anual da ABM, São Paulo, 2022.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-34572