CARACTERIZAÇÃO MICROESTRUTURAL DAS CAMADAS PROTETIVAS DE ÓXIDOS FORMADOS NAS SUPERFÍCIES DE UM AÇO INOXIDÁVEL AUSTENITICO LAMINADO (253 MA®) OXIDADO A ALTAS TEMPERATURAS AO AR

MICROSTRUCTURAL CHARACTERIZATION OF PROTECTIVE OXIDES LAYERS FORMED ON THE SURFACES OF A ROLLED AUSTENITIC STAINLESS (253 MA®) AT HIGH TEMPERATURES IN AIR

DOI

10.5151/1516-392X-30090

Downloads

Baixar Artigo 385 Downloads

Resumo

Foram estudadas as camadas de óxidos formadas nas superfícies de um aço inoxidável austenítico laminado do tipo 22.12, após oxidação ao ar a 800, 900, 1000 e 1100 °C, dentro de um projeto que visava uma melhor compreensão da oxidação a altas temperaturas ao ar de aços inoxidáveis resistentes a altas temperaturas. Utilizou-se o aço inoxidável austenítico microligado ao cério (253 MA®), que é um aço projetado para trabalhos a altas temperaturas. Várias técnicas complementares de análise microestrutural foram utilizadas, tais como difração de raios X e microscopia eletrônica de varredura com EDS acoplado. Observou-se a formação de uma camada não protetora de óxidos de ferro (Fe2O3, Fe3O4 e FeO) e posterior formação de uma camada protetora mais espessa de crômia (Cr2O3). Mais internamente observou-se a formação de SiO2.

 

The oxide layers formed on the surfaces of an austenitic stainless steel type 22.12, after oxidation in air at 800, 900, 1000 and 1100 °C, within a project that aimed at a better understanding of the oxidation at high temperatures in the air of stainless steels resistant to high temperatures. The austenitic stainless steel microalloyed to cerium (253 MA®), that is a steel designed for works at high temperatures, was used. Several complementary techniques of microstructural analysis were used, such as X-ray diffraction and scanning electron microscopy with coupled EDS. A formation of a non-protective layer of iron oxides (Fe2O3, Fe3O4 and FeO) and subsequent formation of a thicker protective layer of chromia (Cr2O3) was observed. More internally, SiO2 formation was observed.

Palavras-chave

Aço Inoxidável, 253 MA®, Oxidação a Altas Temperaturas, Óxidos.

Stainless Steel, 253 MA®, High Temperatures Oxidation, Oxides.

Como citar

Vicente, André de Albuquerque; Cabral, Débora Arruda; Marques, Igor Jordão; Santos, Tiago Felipe de Abreu; Espinosa, Denise Crocce Romano; Tenório, Jorge Alberto Soares. CARACTERIZAÇÃO MICROESTRUTURAL DAS CAMADAS PROTETIVAS DE ÓXIDOS FORMADOS NAS SUPERFÍCIES DE UM AÇO INOXIDÁVEL AUSTENITICO LAMINADO (253 MA®) OXIDADO A ALTAS TEMPERATURAS AO AR , p. 54-65. In: 72nd ABM Annual Congress, São Paulo, 2017.