Título

CARACTERIZAÇÃO DAS PROPRIEDADES ELETROMAGNÉTICAS NA BANDA X DE COMPÓSITOS EPOXIDICOS REFORÇADOS COM TECIDO DE JUTA E NEGRO DE FUMO

CHARACTERIZATION OF X-BAND ELECTROMAGNETIC PROPERTIES OF EPOXY COMPOSITES REINFORCED WITH JUTE FABRIC AND CARBON BLACK

Autoria

ENGENHARIA), RAPHAEL HENRIQUE MORAIS REIS (IME MILITAR DE

ENGENHARIA), RAPHAEL HENRIQUE MORAIS REIS (IME MILITAR DE

Eu sou esse autor

DOI

10.5151/2594-5327-41445

Downloads

Resumo

A CRESCENTE DEMANDA POR MATERIAIS COMPóSITOS EFICIENTES EM BLINDAGEM ELETROMAGNéTICA IMPULSIONA O DESENVOLVIMENTO DE COMPóSITOS EPóXICOS REFORçADOS COM TECIDO DE JUTA E NEGRO DE FUMO (NF) PARA APLICAçõES NA BANDA X. A DESGASEIFICAçãO DA RESINA EPóXI EVITA BOLHAS DE AR, CRUCIAL PARA A EFICáCIA DA BLINDAGEM. PRODUZIDOS COM 30% VOL. DE JUTA E 5% VOL. DE NF, OS COMPóSITOS FORAM MOLDADOS VIA COMPRESSãO HIDRáULICA E TESTADOS QUANTO à CONDUçãO ELéTRICA, TRANSMITâNCIA DE INFRAVERMELHO E EFICIêNCIA DE BLINDAGEM (SE). A DESGASEIFICAçãO NãO ALTEROU A PERMEABILIDADE MAGNéTICA, MANTENDO OS MATERIAIS NãO MAGNéTICOS. A PERMISSIVIDADE ELéTRICA VARIOU ENTRE 3 E 7, INDICANDO BOA EFICIêNCIA DE BLINDAGEM POR REFLEXãO. A RESISTIVIDADE ELéTRICA REVELOU MATERIAIS ALTAMENTE RESISTIVOS, OTIMIZANDO A BLINDAGEM ELETROMAGNéTICA, E A TRANSMITâNCIA DE INFRAVERMELHO MOSTROU ABSORçãO COMPLETA DE LUZ ENTRE 500 E 3000 NM, INDICANDO ALTA FURTIVIDADE CONTRA EQUIPAMENTOS óPTICOS. CONCLUI-SE QUE OS COMPóSITOS DOPADOS MANTêM PROPRIEDADES NãO MAGNéTICAS E APRESENTAM POTENCIAL PARA BLINDAGEM ELETROMAGNéTICA VIA REFLEXãO, COM ALTA RESISTIVIDADE ELéTRICA E EFICáCIA CONTRA RADIAçõES DE INFRAVERMELHO.

: Compósitos Epóxicos, Tecido de Juta, Negro de Fumo, Blindagem Eletromagnética, Banda X

Palavras-chave

THE GROWING DEMAND FOR EFFICIENT COMPOSITE MATERIALS IN ELECTROMAGNETIC SHIELDING DRIVES THE DEVELOPMENT OF EPOXY COMPOSITES REINFORCED WITH JUTE FABRIC AND CARBON BLACK (CB) FOR X-BAND APPLICATIONS. DEGASSING THE EPOXY RESIN PREVENTS AIR BUBBLES, CRUCIAL FOR SHIELDING EFFECTIVENESS. PRODUCED WITH 30% VOL. JUTE AND 5% VOL. CB, THE COMPOSITES WERE MOLDED VIA HYDRAULIC COMPRESSION AND TESTED FOR ELECTRICAL CONDUCTION, INFRARED TRANSMITTANCE, AND SHIELDING EFFECTIVENESS (SE). DEGASSING DID NOT ALTER MAGNETIC PERMEABILITY, KEEPING THE MATERIALS NON-MAGNETIC. THE ELECTRIC PERMITTIVITY RANGED BETWEEN 3 AND 7, INDICATING GOOD SHIELDING EFFICIENCY BY REFLECTION. ELECTRICAL RESISTIVITY REVEALED HIGHLY RESISTIVE MATERIALS, OPTIMIZING ELECTROMAGNETIC SHIELDING, AND INFRARED TRANSMITTANCE SHOWED COMPLETE LIGHT ABSORPTION BETWEEN 500 AND 3000 NM, INDICATING HIGH STEALTH AGAINST OPTICAL EQUIPMENT. IT IS CONCLUDED THAT THE DOPED COMPOSITES MAINTAIN NON-MAGNETIC PROPERTIES AND PRESENT POTENTIAL FOR ELECTROMAGNETIC SHIELDING

Epoxy Composites; Jute Fabric; Carbon Black; Electromagnetic Shielding; X-Band.