Título

CARACTERIZAÇÃO DE AÇOS DA CLASSE COMPLEX-PHASE POR MICROSCOPIA DE FORÇA ATOMICA

CHARACTERIZATION OF COMPLEX-PHASE (CP) STEEL USING ATOMIC FORCE MICROSCOPY(AFM)

DOI

10.5151/2594-5327-34984

Downloads

Baixar Artigo 15 Downloads

Resumo

A DEMANDA POR AÇOS AVANÇADOS DE ALTA RESISTÊNCIA (AHSS) CONTINUA ELEVADA NA INDÚSTRIA AUTOMOTIVA. ENTRES OS AÇOS DE PRIMEIRA GERAÇÃO AHSS OS COMPLEX-PHASE (CP) VÊM RECEBENDO ATENÇÃO COMO POSSÍVEIS SUBSTITUTOS PARA OS DUAL-PHASE (DP) POR APRESENTAREM MAIOR LIMITE DE ESCOAMENTO E MENOR PROPENSÃO A NUCLEAÇÃO DE VAZIOS. UM ASPECTO IMPORTANTE E DESAFIADOR NA PRODUÇÃO DE AÇOS CP É A CARACTERIZAÇÃO MICROESTRUTURAL. ESSES AÇOS PODEM APRESENTAR EM SUA MICROESTRUTURA FERRITA, BAINITA, MARTENSITA, AUSTENITA RETIDA E PERLITA. A COMBINAÇÃO DE TÉCNICAS DE CARACTERIZAÇÃO COMO MICROSCOPIA ÓTICA (LOM) COM ATAQUES COLORIDOS E DIFRAÇÃO DE ELÉTRONS RETROESPALHADOS (EBSD) VEM SENDO UTILIZADAS COM SUCESSO PARA QUANTIFICAÇÃO MICROESTRUTURAL. PORÉM, TÉCNICAS COM EBSD DEPENDEM DE PROCESSOS DE PREPARAÇÃO DE AMOSTRAS MINUCIOSOS E LONGOS PERÍODOS DE COLETA DE DADOS. UMA POSSÍVEL ALTERNATIVA PARA O EBSD SERIA O USO DE MICROSCOPIA DE FORÇA ATÔMICA (AFM). NESTE TRABALHO, DOIS AÇOS DA CLASSE CP RECENTEMENTE PRODUZIDOS E CUJA MICROESTRUTURA FOI QUANTIFICADA POR LOM E EBSD FORAM CARACTERIZADOS POR AFM. OS RESULTADOS DA QUANTIFICAÇÃO MOSTRAM QUE O AFM PODE SER UTILIZADO PARA COMPLEMENTAR OS DADOS OBTIDOS PELAS OUTRAS TÉCNICAS.

 

THE DEMAND FOR ADVANCED HIGH STRENGTH STEELS (AHSS) REMAINS HIGH IN THE AUTOMOTIVE INDUSTRY. AMONG THE FIRST GENERATION AHSS COMPLEX-PHASE (CP) STEELS HAVE BEEN RECEIVING ATTENTION AS POSSIBLE SUBSTITUTES FOR DUAL-PHASE (DP) ONES DUE TO A HIGHER YIELD STRENGTH AND BEING LESS PRONE TO VOID NUCLEATION. AN IMPORTANT AND CHALLENGING ASPECT IN THE PRODUCTION OF CP STEELS IS THE MICROSTRUCTURAL CHARACTERIZATION. THESE STEELS CAN PRESENT IN THEIR MICROSTRUCTURE FERRITE, BAINITE, MARTENSITE, RETAINED AUSTENITE AND PEARLITE. THE COMBINATION OF CHARACTERIZATION TECHNIQUES SUCH AS LIGHT OPTICAL MICROSCOPY (LOM) WITH COLOR ETCHING AND ELECTRON BACKSCATTER DIFFRACTION (EBSD) HAS BEEN SUCCESSFULLY USED FOR MICROSTRUCTURAL QUANTIFICATION. HOWEVER, EBSD TECHNIQUES RELY ON COMPLICATED AND LONG SAMPLE PREPARATION PROCESSES AS WELL AS LONG COLLECTION TIMES. A POSSIBLE ALTERNATIVE TO EBSD WOULD BE THE USE OF ATOMIC FORCE MICROSCOPY (AFM). IN THIS WORK, TWO RECENTLY PRODUCED CP CLASS STEELS WHOSE MICROSTRUCTURE WAS QUANTIFIED BY LOM AND EBSD WERE CHARACTERIZED BY AFM. THE QUANTIFICATION RESULTS SHOW THAT THE AFM CAN BE USED TO COMPLEMENT THE DATA OBTAINED BY THE OTHER TECHNIQUES.

Palavras-chave

Aços multifásicos, Aços Complex-Phase, Caracterização microestrutural, Microscopia de força atômica

Multi-phase Steel, Complex Phase Steel, Microstructural characterization, Atomic force microscopy