Título

CARACTERIZAÇÃO MECÂNICA DE UM COMPÓSITO DE PP/SIC

MECHANICAL CHARACTERIZATION OF A PP/SIC COMPOSITE

Autoria

Dafe, Sara Silva Ferreira de

Dafe, Sara Silva Ferreira de

Eu sou esse autor

DOI

10.5151/2594-5327-34172

Downloads

Resumo

A PESQUISA POR NOVOS MATERIAIS VEM CADA VEZ MAIS SENDO O FOCO DA INDÚSTRIA. MATERIAIS MAIS LEVES, COM PROPRIEDADES MECÂNICAS MELHORES PARA SUBSTITUIR OS ATUALMENTE USADOS, VISANDO A REDUÇÃO DE PESO, E ASSIM MELHORES EFICIÊNCIAS ENERGÉTICAS. OS MATERIAIS COMPÓSITOS SÃO PROMISSORES NESSE CAMPO DE PESQUISA. A UTILIZAÇÃO DE UMA MATRIZ POLIMÉRICA COM A ADIÇÃO DE OUTRO MATERIAL PERMITE A CONFECÇÃO DE PEÇAS LEVES, COM BOAS PROPRIEDADES, E COM GEOMETRIAS COMPLEXAS. O POLIPROPILENO POSSUI BOAS PROPRIEDADES MECÂNICAS E UM FÁCIL PROCESSAMENTO. O CARBETO DE SILÍCIO POSSUI ELEVADA DUREZA E UMA BOA ESTABILIDADE TÉRMICA, SENDO, PORTANTO, UM PROMISSOR MATERIAL A SER ADICIONADO NA MATRIZ. NO TRABALHO FORAM UTILIZADAS DUAS GRANULOMETRIAS DE SIC E QUATRO DIFERENTES PORCENTAGENS DE PESO, E UMA AMOSTRA DE PP PURO COMO REFERÊNCIA. APÓS O PROCESSAMENTO DAS AMOSTRAS, FORAM REALIZADAS ANÁLISES TÉRMICAS, ENSAIOS DE TRAÇÃO E AFERIÇÕES DE DUREZA, E ENTÃO FOI OBSERVADO QUE A TEMPERATURA DE INÍCIO DE DEGRADAÇÃO DO COMPÓSITO FOI SUPERIOR EM MÉDIA 20ºC, E QUE AS TENSÕES DE ESCOAMENTO AUMENTARAM, EM MÉDIA, 2,5 MPA E A DUREZA AUMENTOU EM MÉDIA 10 SHORE D.

THE SEARCH FOR NEW MATERIALS IS INCREASINGLY BECOMING THE FOCUS OF THE INDUSTRIAL SECTOR. LIGHTER MATERIALS WITH BETTER MECHANICAL PROPERTIES TO REPLACE THOSE CURRENTLY USED, AIMING AT WEIGHT REDUCTION, AND THUS BETTER ENERGY EFFICIENCY. COMPOSITE MATERIALS ARE PROMISING IN THIS FIELD OF RESEARCH. THE USE OF A POLYMER MATRIX WITH THE ADDITION OF ANOTHER MATERIAL, ALLOWS FOR THE MANUFACTURING OF LIGHTER PARTS, WITH GOOD PROPERTIES, AND WITH COMPLEX GEOMETRIES. POLYPROPYLENE HAS GOOD MECHANICAL PROPERTIES AND ALLOWS FOR EASY PROCESSING. SILICON CARBIDE HAS HIGH HARDNESS AND GOOD THERMAL STABILITY, THUS BEING A PROMISING MATERIAL TO BE ADDED TO THE MATRIX. IN THE STUDY, TWO SIC PARTICLE SIZES AND FOUR DIFFERENT WEIGHT PERCENTAGES WERE USED, ALONG WITH A SAMPLE OF PURE PP FOR REFERENCE. AFTER PROCESSING THE SAMPLES, THERMAL ANALYSIS, TENSILE TESTS AND HARDNESS MEASUREMENTS WERE PERFORMED, AND THEN IT WAS OBSERVED THAT THE INITIAL DECOMPOSITION TEMPERATURE OF THE COMPOSITE WAS HIGHER BY AN AVERAGE OF 20ºC, AND THAT THE YIELD STRENGTH INCREASED BY AN AVERAGE OF 2.5 MPA AND HARDNESS WAS INCREASED BY AN AVERAGE OF 10 SHORE D.

Palavras-chave

Polipropileno; Carbeto de Sílicio; Compósito; Resistência Mecânica

Polypropylene; Silicon carbide; Composite; Mechanical resistance