CARACTERIZAÇÃO MICROESTRUTURAL DE MAGNÉSIO PROCESSADO POR ECAE USANDO EBSD: MICROSTRUCTURAL CHARACTERIZATION OF MAGNESIUM PROCESSED BY ECAE USING EBSD

Neto, João Rodrigues de Barros; Saraiva, Breno Rabelo Coutinho; Oliveira Filho, José Amilton Cardoso de; Loureiro, Rodrigo de Carvalho Paes; Silva, Erenilton Pereira da; Leiva, Daniel Rodrigo; Abreu, Hamilton Ferreira Gomes de

doi:10.5151/2594-5297-34882

Anais do Seminário de Laminação, Conformação de Metais e Produtos

ISSN 2594-5297

57° Seminário de Laminação e Conformação de Metais — vol. 57, num.57 (2022)

Título

CARACTERIZAÇÃO MICROESTRUTURAL DE MAGNÉSIO PROCESSADO POR ECAE USANDO EBSD

MICROSTRUCTURAL CHARACTERIZATION OF MAGNESIUM PROCESSED BY ECAE USING EBSD

Autoria

Neto, João Rodrigues de Barros; Saraiva, Breno Rabelo Coutinho; Oliveira Filho, José Amilton Cardoso de; Loureiro, Rodrigo de Carvalho Paes; Silva, Erenilton Pereira da; Leiva, Daniel Rodrigo; Abreu, Hamilton Ferreira Gomes de

DOI

10.5151/2594-5297-34882

Downloads

Baixar Artigo 9 Downloads

Resumo

MAGNÉSIO COMERCIALMENTE PURO (99,8%) FOI PROCESSADO USANDO 4 PASSES DE EXTRUSÃO ANGULAR POR CANAIS IGUAIS (ECAE) A 300 °C E 225 °C AO LONGO DA ROTA BC. AS AMOSTRAS FORAM CARACTERIZADAS UTILIZANDO A DIFRAÇÃO DE ELÉTRON RETROESPALHADOS (EBSD). OS DADOS DE EBSD FORAM ANALISADOS USANDO O SOFTWARE MTEX. ENTÃO, A DISTRIBUIÇÃO DO TAMANHO DO GRÃO, DISTRIBUIÇÃO DO ÂNGULO DE MISORIENTATION, FIGURAS DE POLO INVERSAS, MAPAS KAM E GND FORAM AVALIADOS. OS RESULTADOS MOSTRARAM QUE A RECRISTALIZAÇÃO DINÂMICA OCORRE EM AMBAS AS TEMPERATURAS DE PROCESSAMENTO E ESTÁ ASSOCIADA À PRODUÇÃO DIÂMETRO MÉDIO DE GRÃOS E DESVIO PADRÃO MENORES. A EXTRUSÃO A 225 °C PRODUZIU UMA MELHOR COMBINAÇÃO DE TAMANHO DE GRÃO E TEXTURA CRISTALLOGRÁFICA, COM O OBJETIVO DE MELHORAR AS PROPRIEDADES MECÂNICAS DO MAGNÉSIO.

AS-CAST COMMERCIAL PURITY (99.8%) MAGNESIUM (MG) WAS PROCESSED USING EQUAL CHANNEL ANGULAR EXTRUSION (ECAE) AT 300 °C AND 225 °C ALONG 4 PASS BC ROUTE. THE SAMPLES WERE CHARACTERIZED USING ELECTRON BACKSCATTER DIFFRACTION (EBSD). THIS DATA WAS ANALYZED WITH MTEX SOFTWARE PACKAGE. THEN, GRAIN SIZE DISTRIBUTION, MISORIENTATION ANGLE DISTRIBUTION, INVERSE POLE FIGURES, KAM MAPS, AND GND PLOTS WERE EVALUATED. THE RESULTS SHOWED THAT DYNAMIC RECRYSTALLIZATION OCCURS AT BOTH PROCESSING TEMPERATURES AND IS ASSOCIATED WITH PRODUCTION OF EQUIAXED MICROSTRUCTURE. MOREOVER, THE LOWEST TEMPERATURE WAS ASSOCIATED WITH SMALLER AVERAGE GRAIN DIAMETER AND STANDARD DEVIATION. EXTRUSION AT 225 °C PRODUCED A BETTER COMBINATION OF GRAIN SIZE AND CRYSTALLOGRAPHIC TEXTURE WITH THE SAKE OF IMPROVING MECHANICAL PROPERTIES OF MAGNESIUM.

Palavras-chave

MAGNÉSIO; EXTRUSÃO ANGULAR POR CANAIS IGUAIS (ECAE); RECRISTALIZAÇÃO;EBSD

MAGNESIUM; EQUAL CHANNEL ANGULAR EXTRUSION (ECAE); RECRYSTALLIZATION; EBSD

Como citar

Neto, João Rodrigues de Barros; Saraiva, Breno Rabelo Coutinho; Oliveira Filho, José Amilton Cardoso de; Loureiro, Rodrigo de Carvalho Paes; Silva, Erenilton Pereira da; Leiva, Daniel Rodrigo; Abreu, Hamilton Ferreira Gomes de. CARACTERIZAÇÃO MICROESTRUTURAL DE MAGNÉSIO PROCESSADO POR ECAE USANDO EBSD , p. 372-384. In: 57° Seminário de Laminação e Conformação de Metais, São Paulo, 2022.