OS AVANçOS NOS SISTEMAS DE BLINDAGEM EM CONFLITOS ARMADOS LEVARAM à INTEGRAçãO DE CERâMICAS AVANçADAS, SUBSTITUINDO AS ARMADURAS METáLICAS TRADICIONAIS E IMPULSIONANDO NOVAS METODOLOGIAS DE DESENVOLVIMENTO DE ARMADURAS BALíSTICAS. O ESTUDO FOCOU EM UM COMPóSITO DE MATRIZ CERâMICA (CMC) FORMADO POR MATRIZ DE CARBETO DE SILíCIO (SIC), ALUMINA (〖AL〗_2 O_3) E íTRIA (Y_2 O_3) REFORçADO COM UMA VITROCERâMICA DO SISTEMA LíTIO-ALUMíNIO-SILíCIO (LAS). OS RESULTADOS INDICARAM QUE AS AMOSTRAS COM ADIçõES MíNIMAS DE LAS APRESENTARAM A MAIOR DUREZA VICKERS, COM UMA MéDIA DE 25 GPA, ALéM DE UMA RESISTêNCIA MAIS ELEVADA AO DESGASTE DURANTE OS TESTES DE SUSCETIBILIDADE AO CORTE. ALéM DISSO, AS AVALIAçõES BALíSTICAS NãO REVELARAM DISPARIDADES ESTATíSTICAS ENTRE OS NíVEIS DE CONCENTRAçãO DE LAS. ESSES RESULTADOS RESSALTAM A IMPORTâNCIA DA OTIMIZAçãO DAS PROPORçõES DE MATERIAIS NA FABRICAçãO DE COMPóSITOS CERâMICOS PARA ALCANçAR DESEMPENHO MECâNICO E BALíSTICO DESEJADO.
ADVANCEMENTS IN ARMOR SYSTEMS IN ARMED CONFLICTS LED TO THE INTEGRATION OF ADVANCED CERAMICS, REPLACING TRADITIONAL METALLIC ARMORS AND DRIVING NEW METHODOLOGIES IN BALLISTIC ARMOR DEVELOPMENT. THE STUDY FOCUSED ON A CERAMIC MATRIX COMPOSITE (CMC) COMPOSED OF SILICON CARBIDE (SIC), ALUMINA (〖AL〗_2 O_3), YTTRIA (Y_2 O_3), AND A LITHIUM-ALUMINUM-SILICON GLASS-CERAMIC SYSTEM (LAS). THE RESULTS INDICATED THAT SAMPLES WITH MINIMAL LAS ADDITIONS EXHIBITED THE HIGHEST VICKERS HARDNESS, AVERAGING 25 GPA, ALONG WITH ENHANCED WEAR RESISTANCE DURING CUTTING SUSCEPTIBILITY TESTS. FURTHERMORE, BALLISTIC EVALUATIONS DID NOT REVEAL STATISTICAL DISPARITIES AMONG LAS CONCENTRATION LEVELS. THESE FINDINGS UNDERSCORE THE IMPORTANCE OF OPTIMIZING MATERIAL PROPORTIONS IN CERAMIC COMPOSITES MANUFACTURING TO ACHIEVE DESIRED MECHANICAL AND BALLISTIC PERFORMANCE.
Palavras-chave
Comportamento balístico; Comportamento tribológico; Carbeto de Silício; Vitrocerâmica
wear behavior, Ballistic behavior, Silicon carbide, Glass-ceramic
Como citar
CARVALHO, MAGNO TORRES;
FIGUEIREDO, ANDRÉ BEN-HUR DA SILVA;
MONTEIRO, SÉRGIO NEVES;
CAMPOS, JOSÉ BRANT DE;
MELO, FRANCISCO CRISTÓVÃO LOURENÇO DE;
LIMA, EDUARDO DE SOUSA.
COMPORTAMENTO BALÍSTICO E TRIBOLÓGICO DE CERÂMICA POROSA SINTERIZADA EM FASE LÍQUIDA COM VITROCERÂMICA DO SISTEMA LAS
,
p. 2031-2044.
In: 77º Congresso Anual da ABM - Internacional,
São Paulo, Brasil,
2024.
ISSN: 2594-5327
, DOI 10.5151/2594-5327-41051