COMPÓSITOS DE MATRIZ POLIESTER ISOFTÁLICO COM CARGA DE RESÍDUO INDUSTRIAL E REFORÇO DE FIBRAS NATURAIS CURTAS

ISOFTÁLICOS POLYESTER MATRIX COMPOSITIONS WITH INDUSTRIAL WASTE LOADING AND STRENGTHENING OF SHORT NATURAL FIBERS

DOI

10.5151/1516-392X-31787

Downloads

Baixar Artigo 75 Downloads

Resumo

Em busca de um desenvolvimento sustentável pesquisadores têm procurado componentes como as fibras vegetais e resíduos industriais que possuem descartes muitas vezes inadequados para fabricação de materiais compósitos. Foram produzidos materiais compósitos de matriz polimérica com inserção de fibras vegetais de bambu no comprimento de 15 mm, compósitos com carga de resíduo industrial de caulim flint com granulometria de 100 mesh e compósitos híbridos resíduo/fibra utilizando o método hand lay-up. Para cada série foram produzidos 6 (seis) corpos de prova. A matriz polimérica apresentou proporções de: catalisador 1% e acelerador 1,5%. As fibras inseridas tiveram valores de fração mássica de: 1, 2 e 3%, o resíduo industrial de caulim nas frações de: 10, 20, 30 e 40% e os compósitos híbridos tiveram valores de: fibras 3% e variação de resíduo nas proporções de 10, 20 e 30%. Foram realizados ensaios de tração dos compósitos pela norma ASTM D-3039. Os melhores resultados de limite de resistência foram: 35,84 MPa para fibras de bambu na proporção de 1%; 25,76 MPa para resíduo de caulim na proporção de 30% e 22,17 MPa para compósitos híbridos 20% de resíduo + 3% de fibras.

 

In search of sustainable development researchers have sought components such as vegetable fibers and industrial waste that have discards often unsuitable for manufacturing composite materials. Polymer matrix composite materials with bamboo plant fiber insertion of 15 mm length were produced, composites with industrial kaolin flint load with 100 mesh granulometry and hybrid composites residue / fiber using the hand lay-up method. For each series, 6 (six) specimens were produced. The polymer matrix showed proportions of: catalyst 1% and accelerator 1.5%. The fibers presented values of: 1, 2 and 3%, the industrial kaolin residue in the fractions of: 10, 20, 30 and 40% and the hybrid composites had values of: 3% fiber and residue variation in proportions of 10, 20 and 30%. Traction tests of the composites were performed according to ASTM D-3039. The best resistance limit results were: 35.84 MPa for bamboo fibers in the 1% ratio; 25.76 MPa for kaolin residue at the ratio of 30% and 22.17 MPa for hybrid composites 20% residue + 3% fibers.

Palavras-chave

Desenvolvimento Sustentável; Matriz Poliéster; Fibras Vegetais; Resíduo de Caulim.

Sustainable development; Polyester Matrix; Plant Fibers; Kaolin Residue

Como citar

Barbosa, Karla Suellen Lino; Mendes, Bruno Henrique Alves; Santos, Alessandro José Gomes dos; Costa, Deibson Silva da; Souza, Jose Antonio da Silva. COMPÓSITOS DE MATRIZ POLIESTER ISOFTÁLICO COM CARGA DE RESÍDUO INDUSTRIAL E REFORÇO DE FIBRAS NATURAIS CURTAS , p. 1868-1878. In: 73º Congresso Anual da ABM, São Paulo, 2018.