CORRELAÇÃO ENTRE A CARACTERIZAÇÃO MECÂNICA, ELÉTRICA E ESTRUTURAL DA LIGA AL-0,9%SI MODIFICADA COM (0,05 E 0,2)%TI: CORRELATION BETWEEN THE MECHANICAL CHARACTERIZATION, ELECTRICAL AND STRUCTURAL LEAGUE AL-0, MODIFIED WITH 9% SI (0,05 AND 0,2)% TI

Freitas, Emmanuelle Sá; Farias, Luciana Bezerra; Santos, Washington Luiz Reis; Machado, Paulo Cordeiro; Quaresma, José Maria do Vale

doi:10.5151/2594-5327-15008

Anais do Congresso Anual da ABM

ISSN 2594-5327

64º Congresso Anual da ABM — vol. 64, num.64 (2009)

Título

CORRELAÇÃO ENTRE A CARACTERIZAÇÃO MECÂNICA, ELÉTRICA E ESTRUTURAL DA LIGA AL-0,9%SI MODIFICADA COM (0,05 E 0,2)%TI

CORRELATION BETWEEN THE MECHANICAL CHARACTERIZATION, ELECTRICAL AND STRUCTURAL LEAGUE AL-0, MODIFIED WITH 9% SI (0,05 AND 0,2)% TI

Autoria

Freitas, Emmanuelle Sá; Farias, Luciana Bezerra; Santos, Washington Luiz Reis; Machado, Paulo Cordeiro; Quaresma, José Maria do Vale

10.5151/2594-5327-15008

Downloads

Baixar Artigo 72 Downloads

Resumo

Neste trabalho foi analisada a variação do teor de Titânio e sua influência na condutividade elétrica, no limite de resistência a tração e na trabalhabilidade da liga. As ligas estudadas Al-0,9%Si-(0,05 e 0,2)%Ti, foram vazadas em lingoteiras de aço SAE 1010. Os corpos de prova foram usinados para um diâmetro de 9,5mm e, desta forma um primeiro conjunto destes foram avaliados mecânica e estruturalmente. Um segundo conjunto de corpos de prova usinado foi laminado a frio até o diâmetro de 3,98mm e, desta forma caracterizados mecânica, estrutural e eletricamente. Os resultados destes ensaios associam a presença das Linhas de Ferro, com o teor e distribuição do Titânio ao comportamento mecânico e elétrico da liga Al-Si modificada.

In this work, the Titanium variation content was analyzed and its influence in alloy’s electrical conductivity, tensile strength, and workability. The studied Al-0.9%Si-(0.05 e 0,2)%Ti alloys were poured in a SAE 1010 steel ingot mold. The test specimen were machined to 9.5 mm diameter. By this way, a primary group was mechanical and structural evaluated. A second group of machined tests specimen was cold- rolled until 3.98 mm diameter and mechanical, structural and electrical characterized. The results of these tests associate Iron Lines’ presence with Titanium distribution and content to mechanical and electrical behavior of Al-Si modified alloy.

Palavras-chave

Liga Al-Si; Propriedades mecânicas; Condutividade elétrica; Caracterização estrutural.

Al-Si alloy; Mechanical properties; Electrical conductivity; Structural characterization.

Como citar

Freitas, Emmanuelle Sá; Farias, Luciana Bezerra; Santos, Washington Luiz Reis; Machado, Paulo Cordeiro; Quaresma, José Maria do Vale. CORRELAÇÃO ENTRE A CARACTERIZAÇÃO MECÂNICA, ELÉTRICA E ESTRUTURAL DA LIGA AL-0,9%SI MODIFICADA COM (0,05 E 0,2)%TI , p. 2200-2207. In: 64º Congresso Anual da ABM, Belo Horizonte, 2009.