DESEMPENHO DE ARGAMASSAS COM ADIÇÃO DE CINZAS CERÂMICAS NO ESTADO ENDURECIDO

PERFORMANCE OF MORTARS WITH THE ADDITION OF CERAMIC ASHES IN THE HARDENED STATE

Autoria

Cruz, Ariana Silva Azeredo; Marvila, Markssuel Teixeira; Azevedo, Afonso Rangel Garcez de; Júnior, José Alexandre Tostes Linhares; Cruz, Lucas Reis; Delaqua, Geovana Carla Girondi; Monteiro, Sergio Neves; Cecchin, Daiane; Alexandre, Jonas; Vieira, Carlos Maurício Fontes

DOI

10.5151/2594-5327-34090

Downloads

Baixar Artigo 36 Downloads

Resumo

EM VIRTUDE DA GRANDE PREOCUPAÇÃO ATUAL ACERCA DOS IMPACTOS AMBIENTAIS CAUSADOS PELA PRODUÇÃO INDUSTRIAL, E TENDO EM VISTA NÃO APENAS O POTENCIAL DA UTILIZAÇÃO DE RESÍDUOS INDUSTRIAIS COMO ADIÇÃO MINERAL EM ARGAMASSAS E CONCRETOS, MAS TAMBÉM OS BENEFÍCIOS CONSEQUENTES DESTA PRÁTICA, ESTE ARTIGO TEVE COMO OBJETIVO AVERIGUAR A VIABILIDADE TÉCNICA DO EMPREGO DE CINZAS RESIDUAIS DA PRODUÇÃO CERÂMICA EM ARGAMASSAS DE ASSENTAMENTO. PARA ISSO, FORAM PRODUZIDOS CORPOS DE PROVA DE ARGAMASSA NO TRAÇO 1:1:6 (CIMENTO: CAL HIDRATADA: AREIA), SENDO UM TRAÇO DE REFERÊNCIA, SEM USO DO RESÍDUO, E DOIS COM 5 E 10% DE RESÍDUO EM SUBSTITUIÇÃO DO CIMENTO PORTLAND, RESPECTIVAMENTE. OS CORPOS DE PROVA FORAM SUBMETIDOS AOS ENSAIOS DE DENSIDADE DE MASSA NO ESTADO ENDURECIDO, ABSORÇÃO DE ÁGUA POR CAPILARIDADE, ABSORÇÃO DE ÁGUA POR IMERSÃO, RESISTÊNCIA A TRAÇÃO NA FLEXÃO E RESISTÊNCIA A COMPRESSÃO. OS RESULTADOS EXPERIMENTADOS DEMONSTRARAM QUE O DESEMPENHO DAS ARGAMASSAS COM O EMPREGO DAS CINZAS CERÂMICAS FOI SUPERIOR AO DA ARGAMASSA DE REFERÊNCIA EM TODOS OS ENSAIOS. DESTA FORMA, FOI POSSÍVEL ASSEGURAR A VIABILIDADE TÉCNICA DO USO DE CINZAS RESIDUAIS DA PRODUÇÃO CERÂMICA EM ARGAMASSAS DE ASSENTAMENTO E TAMBÉM CONCLUIR QUE O TEOR IDEAL DE SUBSTITUIÇÃO PARA O RESÍDUO É O DE 10% EM RELAÇÃO AO CIMENTO PORTLAND.

 

DUE TO THE GREAT CURRENT CONCERN ABOUT THE ENVIRONMENTAL IMPACTS CAUSED BY INDUSTRIAL PRODUCTION, AND CONSIDERING NOT ONLY THE POTENTIAL OF USING INDUSTRIAL WASTE AS A MINERAL ADDITION IN MORTARS AND CONCRETE, BUT ALSO THE CONSEQUENT BENEFITS OF THIS PRACTICE, THIS ARTICLE AIMED TO INVESTIGATE THE TECHNICAL FEASIBILITY OF USING RESIDUAL ASH FROM CERAMIC PRODUCTION IN LAYING MORTARS. FOR THIS, MORTAR SPECIMENS WERE PRODUCED IN THE 1: 1: 6 LINE (CEMENT: HYDRATED LIME: SAND), ONE OF WHICH IS A REFERENCE LINE, WITHOUT USING THE RESIDUE, AND TWO WITH 5 AND 10% OF RESIDUE IN PLACE OF THE CEMENT PORTLAND, RESPECTIVELY. THE SPECIMENS WERE SUBJECTED TO MASS DENSITY TESTS IN THE HARDENED STATE, CAPILLARY WATER ABSORPTION, IMMERSION WATER ABSORPTION (?), FLEXURAL TENSILE AND COMPRESSION RESISTANCE. THE RESULTS SHOWED THAT THE PERFORMANCE OF MORTARS WITH THE USE OF CERAMIC ASH WAS SUPERIOR TO THAT OF REFERENCE MORTAR IN ALL TESTS. IT WAS ALSO POSSIBLE TO CONCLUDE THAT THE IDEAL SUBSTITUTION CONTENT FOR THE RESIDUE IS 10% IN RELATION TO PORTLAND CEMENT.

Palavras-chave

Resíduo; Cinzas Cerâmicas; Argamassa de Assentamento; Cimento Portland

Residue; Ceramic Ashes; Settlement Mortar; Portland Cement