NA CONSTRUçãO CIVIL, OS COMPóSITOS REFORçADOS COM FIBRAS SURGEM COMO INOVAçãO PROMISSORA PARA MELHORAR PROPRIEDADES MECâNICAS DE MATERIAIS COMO ARGAMASSA E CONCRETO, REDUZINDO IMPACTOS AMBIENTAIS E OTIMIZANDO RECURSOS. O USO DE FIBRAS RESIDUAIS VISA APRIMORAR AS PROPRIEDADES E CONTROLAR FISSURAS, DESTACANDO-SE COMO SOLUçãO SUSTENTáVEL. ESTE ARTIGO INVESTIGA O EFEITO DA ADIçãO DE FIBRAS DE POLIéSTER EM DIFERENTES TEORES (0%, 0,15% E 0,30%) NA RESISTêNCIA à COMPRESSãO DE ARGAMASSAS. OS MATERIAIS UTILIZADOS INCLUíRAM CIMENTO PORTLAND DE ALTA RESISTêNCIA INICIAL, AREIA COMERCIAL E FIBRAS DE POLIéSTER RECICLADAS PROVENIENTES DE RESíDUOS DE PNEUS, REFLETINDO UMA ABORDAGEM SUSTENTáVEL NA CONSTRUçãO CIVIL. OS RESULTADOS DOS ENSAIOS DEMONSTRAM QUE A RESISTêNCIA à COMPRESSãO AUMENTOU COM O ACRéSCIMO DE FIBRAS: 14,5 MPA PARA 0%, 15,2 MPA PARA 0,15% E 16,1 MPA PARA 0,30%. ALéM DISSO, A ANáLISE POR MICROSCOPIA óPTICA EVIDENCIOU MUDANçAS NA TEXTURA DAS ARGAMASSAS COM O AUMENTO DAS FIBRAS, INDICANDO MAIOR COESãO E ADERêNCIA. ESSES RESULTADOS SUGEREM QUE A INCORPORAçãO DE FIBRAS DE POLIéSTER PODE MELHORAR SIGNIFICATIVAMENTE A RESISTêNCIA à COMPRESSãO DAS ARGAMASSAS, CONTRIBUINDO PARA O DESENVOLVIMENTO DE MATERIAIS DE CONSTRUçãO MAIS EFICIENTES E SUSTENTáVEIS. ESTE ESTUDO DESTACA A VIABILIDADE E O POTENCIAL DE APLICAçãO DESSES COMPóSITOS REFORçADOS COM FIBRAS NA INDúSTRIA DA CONSTRUçãO CIVIL.
IN CIVIL ENGINEERING, FIBER-REINFORCED COMPOSITES EMERGE AS A PROMISING INNOVATION TO ENHANCE MECHANICAL PROPERTIES OF MATERIALS LIKE MORTAR AND CONCRETE, REDUCING ENVIRONMENTAL IMPACTS AND OPTIMIZING RESOURCES. THE USE OF RESIDUAL FIBERS AIMS TO IMPROVE PROPERTIES AND CONTROL FISSURES, STANDING OUT AS A SUSTAINABLE SOLUTION. THIS ARTICLE INVESTIGATES THE EFFECT OF ADDING POLYESTER FIBERS AT DIFFERENT PROPORTIONS (0%, 0.15%, AND 0.30%) ON MORTAR COMPRESSION STRENGTH. MATERIALS INCLUDED HIGH INITIAL STRENGTH PORTLAND CEMENT, COMMERCIAL SAND, AND RECYCLED POLYESTER FIBERS FROM TIRE WASTE, REFLECTING A SUSTAINABLE APPROACH IN CIVIL CONSTRUCTION. TEST RESULTS SHOW INCREASED COMPRESSION STRENGTH WITH FIBER ADDITION: 14.5 MPA FOR 0%, 15.2 MPA FOR 0.15%, AND 16.1 MPA FOR 0.30%. ADDITIONALLY, OPTICAL MICROSCOPY ANALYSIS REVEALED TEXTURE CHANGES IN MORTARS WITH INCREASED FIBERS, INDICATING GREATER COHESION AND ADHESION. THESE FINDINGS SUGGEST THAT INCORPORATING POLYESTER FIBERS CAN SIGNIFICANTLY ENHANCE MORTAR COMPRESSION STRENGTH, CONTRIBUTING TO THE DEVELOPMENT OF MORE EFFICIENT AND SUSTAINABLE CONSTRUCTION MATERIALS. THIS STUDY HIGHLIGHTS THE FEASIBILITY AND POTENTIAL APPLICATION OF THESE FIBER-REINFORCED COMPOSITES IN THE CIVIL CONSTRUCTION INDUSTRY.
Palavras-chave
Construção Civil; Fibras residuais; Argamassa; Compósitos.
Civil Construction; Residual Fibers; Mortar; Composites.
Como citar
SANTANA, RAYANNE OLIVEIRA LEAO;
FERREIRA, PAULO ANDERSON ARANHA;
FRANÇA, GIOVANA ZAGALO DE;
BOTELHO, EMILY DE FÁTIMA PINHEIRO;
SANTANA, VITOR LEÃO;
SILVA, ALISSON CLAY RIOS DA;
CANDIDO, VERÔNICA SCARPINI.
DESEMPENHO MECÂNICO DE ARGAMASSAS REFORÇADAS COM FIBRAS DE RESÍDUO TÊXTIL DA INDUSTRIA DE PNEUS
,
p. 3127-3134.
In: 77º Congresso Anual da ABM - Internacional,
São Paulo, Brasil,
2024.
ISSN: 2594-5327
, DOI 10.5151/2594-5327-41356