DESENVOLVIMENTO DE AÇO SAE 1012 EM NOVAS ESPESSURAS DE 1,8 MM E 1,9 MM PARA O MERCADO: DEVELOPMENT OF SAE 1012 STEEL IN NEW THICKNESSES OF 1.8 MM AND 1.9 MM TO THE MARKET

SAE 1012 É UM AÇO CARBONO (NÃO LIGADO). É UM AÇO FACILMENTE TRABALHÁVEL DEVIDO À SUA RESISTÊNCIA MECÂNICA, TENACIDADE, DUCTILIDADE, SOLDABILIDADE E USINABILIDADE. POR ESTES MOTIVOS, É UTILIZADO EM MÚLTIPLAS APLICAÇÕES FINAIS, PRINCIPALMENTE EM PERFIS METÁLICOS E TUBOS. EM 2019, HOUVE UMA DEGRADAÇÃO DO MERCADO NACIONAL DE CARBONO E AÇO LIGADO, COM PERDA DE RENTABILIDADE, DEVIDO AO AUMENTO DO CUSTO DAS MATÉRIAS-PRIMAS, PRINCIPALMENTE MINÉRIO DE FERRO. UTILIZANDO AS FERRAMENTAS BRAINSTORMING, MATRIZ ESFORÇO X IMPACTO E 5W2H, UMA NOVA OPORTUNIDADE FOI VISLUMBRADA E PRIORIZADA PELA EQUIPE. O DESAFIO ERA PRODUZIR BOBINAS A QUENTE DE 1,8 MM E 1,9 MM DE ESPESSURA COM BOA QUALIDADE, RENDIMENTO E PRODUTIVIDADE. A ESPESSURA ALMEJADA FICOU ABAIXO DA ESPECIFICAÇÃO NOMINAL DE STECKEL DA APERAM TIMÓTEO. PADRÕES ROBUSTOS DE PROCESSO A QUENTE FORAM DESENVOLVIDOS COM ÊNFASE NO CICLO TERMOMECÂNICO EM LAMINADORES ROUGHER E STECKEL COM BASE NO USO DE CILINDROS DE ALTO DESEMPENHO (HSS). COM A MAIOR AGILIDADE DE PROJETO, APÓS APENAS 3 MESES, O PORTFÓLIO DE PRODUTOS DA APERAM FOI ATUALIZADO, INCLUINDO O MARCO DE PROTOTIPAGEM. UM IMPORTANTE VOLUME DE PEDIDOS DE LAMINADOS A QUENTE GRAU SAE 1012 FOI ADICIONADO AO PORTFÓLIO DE NEGÓCIOS, QUE ERA O PILAR DA MANUTENÇÃO DOS NÍVEIS DE PRODUÇÃO NO CIRCUITO QUENTE DA PLANTA. COM BASE NO ENTENDIMENTO DOS FUNDAMENTOS DA METALURGIA FÍSICA DA DEFORMAÇÃO A QUENTE, PRINCIPALMENTE SIMULAÇÃO MATEMÁTICA A QUENTE, UMA NOVA FASE DE DESENVOLVIMENTO ESTÁ EM ANDAMENTO COM O OBJETIVO DE EXPANDIR AINDA MAIS O PORTFÓLIO ATUAL, PRINCIPALMENTE NOVAS ESPESSURAS E NOVAS LARGURAS NA JANELA DE PRODUTOS DO LAMINADOR STECKEL

SAE 1012 IS A CARBON (NON-ALLOY) STEEL. IT IS EASILY WORKABLE STEEL DUE TO ITS MECHANICAL STRENGTH, TOUGHNESS, DUCTILITY, WELDABILITY, AND MACHINABILITY. FOR THESE REASONS, IT IS USED IN FINAL MULTIPLE APPLICATIONS, MAINLY FOR METAL PROFILES AND TUBES. IN 2019, THERE WAS A DEGRADATION OF THE NATIONAL CARBON AND ALLOYED STEEL MARKET, WITH LOSSES IN PROFITABILITY, DUE TO THE INCREASE IN THE COST OF RAW MATERIALS, MAINLY IRON ORE. USING THE TOOLS BRAINSTORMING, MATRIX EFFORT X IMPACT, AND 5W2H, A NEW OPPORTUNITY WAS ENVISIONED AND PRIORITIZED BY THE TEAM. THE CHALLENGE WAS TO PRODUCE HOT COILS OF 1.8 MM AND 1.9 MM THICKNESS WITH GOOD QUALITY, YIELD, AND PRODUCTIVITY. THE THICKNESS AIMED WAS BELOW STECKEL'S NOMINAL SPECIFICATION OF APERAM TIMóTEO. ROBUST HOT PROCESS STANDARDS HAVE BEEN DEVELOPED WITH AN EMPHASIS ON THE THERMOMECHANICAL CYCLE IN ROUGHER AND STECKEL ROLLING MILLS BASED ON HIGH-PERFORMANCE CYLINDERS (HSS) USE. WITH THE GREATEST PROJECT AGILITY, AFTER 3 MONTHS ONLY, THE PRODUCT PORTFóLIO OF APERAM WAS UPGRADED, INCLUDING THE PROTOTYPING MILESTONE. AN IMPORTANT ORDER VOLUME OF HOT ROLLED SAE 1012 GRADE WAS ADDED TO THE BUSINESS PORTFOLIO, WHICH WAS THE PILLAR OF MAINTENANCE OF PRODUCTION LEVELS IN THE PLANT'S HOT CIRCUIT. BASED ON THE UNDERSTANDING OF THE FUNDAMENTALS OF THE PHYSICAL METALLURGY OF HOT DEFORMATION, MAINLY HOT MATHEMATICAL SIMULATION, A NEW PHASE OF THE DEVELOPMENT IS ONGOING AIMING TO EXPAND THE CURRENT PORTFOLIO, EVEN MORE, MAINLY NEW THICKNESS AND NEW WIDTH IN THE STECKEL MILL PRODUCT WINDOW

Palavras-chave

Aço SAE 1012; Espessura de 1, 8 mm; laminados a quente

SAE 1012 steel; 1.8 mm thickness; hot rolled

Como citar

Toledo Jr, Francisco Geraldo; Riechelmann, Celso Custodio; Castro, Geovane Martis; Ferreira, Keyferson Gonçalves; Fernandes, Marcio Aurélio Gomes; Montes, Rafael Rezende; Rocha, Thiago Silva. DESENVOLVIMENTO DE AÇO SAE 1012 EM NOVAS ESPESSURAS DE 1,8 MM E 1,9 MM PARA O MERCADO , p. 313-322. In: 57° Seminário de Laminação e Conformação de Metais, São Paulo, 2022.
ISSN: 2594-5297 , DOI 10.5151/2594-5297-34696