DURABILIDADE DE ARGAMASSAS COM FIBRAS DE COCO

DURABILITY OF MORTARS WITH COCONUT FIBERS

Autoria

Marvila, Markssuel Teixeira; Azevedo, Afonso Rangel Garcez de; Cecchin, Daiane; Zanelato, Euzébio Bernabé; Barbosa, Victor de Souza; Lima, Thuany Espirito Santo; Monteiro, Sergio Neves; Xavier, Gustavo Castro; Aguiar, Niander Cerqueira; Vieira, Carlos Maurício Fontes

DOI

10.5151/2594-5327-34040

Downloads

Baixar Artigo 10 Downloads

Resumo

A APLICAÇÃO DE FIBRAS NATURAIS, COMO É O CASO DA FIBRA DE COCO, É CADA VEZ MAIS COMUM EM MATERIAIS CIMENTÍCIOS, COMO CONCRETOS E ARGAMASSAS. PORÉM, AINDA CARECE DE ESTUDOS MAIS APROFUNDADOS SOBRE A DURABILIDADE DESSAS ARGAMASSAS. ASSIM, O OBJETIVO DESSE TRABALHO É ESTUDAR A DURABILIDADE DE ARGAMASSAS 1:1:6:1,5 (CIMENTO: CAL HIDRATADA: AREIA: ÁGUA), CONTENDO DIFERENTES PORCENTAGENS DE FIBRA DE COCO (0%, 1,5% E 3,0%). ESSAS ARGAMASSAS FORAM ENSAIADAS À COMPRESSÃO, ONDE DETECTOU-SE QUE A UTILIZAÇÃO DAS FIBRAS AUMENTA DE MANEIRA SIGNIFICA A RESISTÊNCIA DA ARGAMASSA, SENDO NA SEQUÊNCIA ENSAIADA EM CICLOS DE MOLHAGEM E SECAGEM E CICLOS DE DEGRADAÇÃO EM NÉVOA SALINA, SENDO VERIFICADAS AS PERDAS DE MASSA DO MATERIAL E A QUEDA DE RESISTÊNCIA À COMPRESSÃO APÓS A REALIZAÇÃO DOS CICLOS. VERIFICOU-SE QUE AS ARGAMASSAS CONTENDO FIBRAS DE COCO APRESENTARAM UM DESEMPENHO SUPERIOR A ARGAMASSA DE REFERÊNCIA NOS CICLOS DE MOLHAGEM E SECAGEM, MAS QUE HOUVE UMA QUEDA DE PROPRIEDADES PARA A ARGAMASSA CONTENDO 3,0% DE FIBRA NOS CICLOS DE DEGRADAÇÃO EM NÉVOA SALINA DEVIDO AO APODRECIMENTO DAS FIBRAS. PORÉM AS ARGAMASSAS CONTENDO 1,5% DE FIBRA DE COCO APRESENTARAM DESEMPENHO SUPERIOR EM TODAS AS SITUAÇÕES, COMPROVANDO QUE A INCORPORAÇÃO DAS FIBRAS DE COCO EM 1,5% É BENÉFICA AS PROPRIEDADES DAS ARGAMASSAS.

 

THE APPLICATION OF NATURAL FIBERS, SUCH AS COCONUT FIBER, IS INCREASINGLY COMMON IN CEMENTITIOUS MATERIALS, SUCH AS CONCRETE AND MORTAR. HOWEVER, THERE IS STILL A NEED FOR MORE IN-DEPTH STUDIES ON THE DURABILITY OF THESE MORTARS. THUS, THE OBJECTIVE OF THIS WORK IS TO STUDY THE DURABILITY OF MORTARS 1: 1: 6: 1.5 (CEMENT: HYDRATED LIME: SAND: WATER), CONTAINING DIFFERENT PERCENTAGES OF COCONUT FIBER (0%, 1.5% AND 3, 0%). THESE MORTARS WERE TESTED FOR COMPRESSION, WHERE IT WAS FOUND THAT THE USE OF THE FIBERS SIGNIFICANTLY INCREASES THE STRENGTH OF THE MORTAR, BEING SUBSEQUENTLY TESTED IN WETTING AND DRYING CYCLES AND DEGRADATION CYCLES IN SALT SPRAY, CHECKING THE MASS LOSSES OF THE MATERIAL AND THE DROP IN COMPRESSIVE STRENGTH AFTER THE CYCLES. IT WAS FOUND THAT THE MORTARS CONTAINING COCONUT FIBERS PERFORMED BETTER THAN THE REFERENCE MORTAR IN THE WETTING AND DRYING CYCLES, BUT THAT THERE WAS A DECREASE IN PROPERTIES FOR THE MORTAR CONTAINING 3.0% FIBER IN THE SALT FOG DEGRADATION CYCLES DUE TO FIBER ROT. HOWEVER, MORTARS CONTAINING 1.5% COCONUT FIBER SHOWED SUPERIOR PERFORMANCE IN ALL SITUATIONS, PROVING THAT THE INCORPORATION OF COCONUT FIBERS IN 1.5% IS BENEFICIAL TO THE PROPERTIES OF MORTARS

Palavras-chave

Fibra de coco; Durabilidade; Argamassa

Coconut fiber; Durability; Mortar