EFEITO DA COMPOSIçãO QUíMICA DO BANHO DE ZN NA QUALIDADE SUPERFICIAL DO REVESTIMENTO GALVANIZED (GI) FORMADO EM AçOS AVANçADOS DE ALTA RESISTêNCIA (AHSS)

EFFECT OF CHEMICAL COMPOSITION OF ZN BATH ON THE SURFACE QUALITY OF GALVANIZED (GI) COATING FORMED ON ADVANCED HIGH-STRENGTH STEEL (AHSS)

DOI

10.5151/2594-5297-41245

Downloads

Baixar Artigo 3 Downloads

Resumo

O CONTROLE DA COMPOSIçãO QUíMICA DO BANHO DE ZN EM LINHAS CONTíNUAS DE GALVANIZAçãO POR IMERSãO A QUENTE (CGL) PERMITE MELHORAR A QUALIDADE SUPERFICIAL DE PRODUTOS REVESTIDOS, PRINCIPALMENTE NO CASO DE REVESTIMENTO GALVANIZADO (GI), POR MINIMIZAR A FORMAçãO E PRECIPITAçãO DE PARTíCULAS INTERMETáLICAS FE-ZN, DENOMINADAS “DROSS”, ALéM DE PERMITIR A MELHORA DA EFICIêNCIA OPERACIONAL ATRAVéS DO AUMENTO DE VELOCIDADE DO PROCESSO. A FORMAçãO E PRECIPITAçãO DESSAS PARTíCULAS ESTãO INTRISICAMENTE RELACIONADAS AOS TEORES DE FE E AL PRESENTES NO BANHO DE ZN. ALéM DISSO, O CONTROLE DO TEOR DE AL NO BANHO DE ZN é AINDA MAIS IMPORTANTE DURANTE A GALVANIZAçãO DE AçOS DE ALTA RESISTêNCIA DEVIDO à PRESENçA DE ELEMENTOS DE LIGA NESTES AçOS QUE COMPETEM COM O AL PELA FORMAçãO DE REVESTIMENTOS COM BOA QUALIDADE SUPERFICIAL DURANTE A IMERSãO DAS CHAPAS DE AçO NO BANHO DE ZN. NESTE CONTEXTO, O EFEITO DA COMPOSIçãO QUíMICA DO BANHO DE ZN NA QUALIDADE SUPERFICIAL DO REVESTIMENTO GI DE AçOS AHSS FOI DETERMINADO, EM ESCALA PILOTO, UTILIZANDO UM SIMULADOR DE PROCESSO DE IMERSãO A QUENTE (HDPS). FOI POSSíVEL AVALIAR A INFLUêNCIA DA COMPOSIçãO QUíMICA DO BANHO DE ZN NA FORMAçãO E PRECIPITAçãO DE PARTíCULAS AO LONGO DO TEMPO, E NA FORMAçãO DO REVESTIMENTO, PRINCIPALMENTE NA CAMADA INTERFACIAL, DENOMINADA CAMADA DE INIBIçãO. COM ISSO FOI POSSíVEL OTIMIZAR A COMPOSIçãO QUíMICA DO BANHO DE ZN, PRINCIPALMENTE O TEOR DE AL, PARA PRODUZIR REVESTIMENTOS GI COM BOA QUALIDADE SUPERFICIAL E ADESãO AO SUBSTRATO, ALéM DE PROPORCIONAR CONDIçõES PARA OBTER MAIOR FLEXIBILIDADE OPERACIONAL.

 

THE CHEMICAL COMPOSITION CONTROLLING OF ZN BATH IN CONTINUOUS HOT DIP GALVANIZING LINES (CGL) IS RESPONSIBLE FOR IMPROVING THE SURFACE QUALITY OF COATED PRODUCTS, ESPECIALLY IN THE CASE OF GALVANIZED COATING (GI). THIS CHEMICAL COMPOSITION CONTROLS MINIMIZE THE FORMATION AND PRECIPITATION OF ZN-FE-AL INTERMETALLIC PARTICLES, NAMED DROSS, IN ADDITION TO IMPROVING OPERATIONAL EFFICIENCY AND INCREASING PROCESS LINE SPEED. THE FORMATION AND PRECIPITATION OF THESE PARTICLES ARE CLOSELY RELATED TO THE FE AND AL CONTENTS PRESENT IN THE ZN BATH. FURTHERMORE, AL CONTENT CONTROL IN THE ZN BATH IS EVEN MORE CRITICAL FOR GALVANIZATION OF HIGH-STRENGTH STEELS (AHSS) DUE TO THE HIGH CONTENT OF ALLOYING ELEMENTS IN THESE STEELS, WHICH COMPETE WITH AL IN GI COATINGS. IN THIS CONTEXT, THE EFFECT OF THE CHEMICAL COMPOSITION OF THE ZN BATH ON THE SURFACE QUALITY OF THE GI COATING OF AN AHSS WAS DETERMINED IN THE LABORATORY USING A HOT DIP GALVANIZATION PROCESS SIMULATOR (HDPS). IT WAS POSSIBLE TO EVALUATE THE INFLUENCE OF THE CHEMICAL COMPOSITION OF THE ZN BATH ON THE FORMATION AND PRECIPITATION OF PARTICLES AND ON THE COATING FORMATION, MAINLY IN THE INTERFACIAL LAYER, NAMED THE INHIBITION LAYER. IT WAS POSSIBLE TO OPTIMIZE THE AL CONTENT IN THE ZN BATH, PROVIDING CONDITIONS TO OBTAIN GREATER OPERATIONAL FLEXIBILITY AND GI COATINGS WITH GOOD SURFACE QUALITY AND ADHESION TO THE SUBSTRATE.

Palavras-chave

Revestimento GI; Advanced high strength steel (AHSS); Hot dip galvanizing; Adição de Al

GI coating; Advanced high strength steel (AHSS); Dual phase steel (DP); Hot dip galvanizing (HDG).

Como citar

ELEUTERIO, HENRIQUE LACERDA; PAULA, JULIANA CRISTINA DE. EFEITO DA COMPOSIçãO QUíMICA DO BANHO DE ZN NA QUALIDADE SUPERFICIAL DO REVESTIMENTO GALVANIZED (GI) FORMADO EM AçOS AVANçADOS DE ALTA RESISTêNCIA (AHSS) , p. 560-569. In: 59º Seminário de Laminação, Conformação de Metais e Produtos, São Paulo, Brasil, 2024.