ESTE ESTUDO INVESTIGOU A INFLUêNCIA DO TIPO DE CURA NA RESISTêNCIA à COMPRESSãO DE ARGAMASSAS A BASE DE CIMENTO PORTLAND COM ADIçãO DE SUBPRODUTO DE GESSO, OBTIDO DURANTE A PRODUçãO DO áCIDO LáTICO. ARGAMASSAS FORAM FEITAS COM ADIçãO DE SUBPRODUTO DE GESSO, MOíDO POR 30 MINUTOS NO MOINHO DE BOLAS, NAS PROPORçõES DE 0%, 2,5%, 5% E 7,5% EM RELAçãO à MASSA DO CIMENTO E CURADAS EM TEMPERATURA AMBIENTE E SUBMERSA EM áGUA SATURADA COM CAL. FOI AVALIADA A RESISTêNCIA à COMPRESSãO DAS ARGAMASSAS NOS DOIS TIPOS DE CURA, BEM COMO A ANáLISE MICROESTRUTURAL POR DIFRAçãO DE RAIOS-X. OS RESULTADOS MOSTRARAM QUE AS AMOSTRAS SUBMETIDAS à CURA AMBIENTE APRESENTARAM MAIOR RESISTêNCIA COMPARADA AS SUBMETIDAS à CURA IMERSA EM áGUA SATURADA DE CAL. NO ENTANTO, AS ARGAMASSAS COM ADIçãO DE SULFATO DE CáLCIO ATé 5% E CURA IMERSA APRESENTARAM RESISTêNCIA à COMPRESSãO SIGNIFICATIVAMENTE MAIOR DO QUE A ARGAMASSA DE REFERêNCIA. ENQUANTO, NA CURA AO AR A RESISTêNCIA EXIBIU TENDêNCIA DECRESCENTE COM A ADIçãO DO GESSO. ISTO INDICA QUE O REGIME DE CURA TEM UM IMPACTO SIGNIFICATIVO NA RESISTêNCIA à COMPRESSãO, MAS NãO ALTERARAM O TIPO DE PRODUTOS DE HIDRATAçãO.
THIS STUDY INVESTIGATED THE INFLUENCE OF THE TYPE OF CURING ON THE COMPRESSIVE STRENGTH OF MORTARS BASED ON PORTLAND CEMENT WITH THE ADDITION OF GYPSUM BY-PRODUCT, OBTAINED DURING THE PRODUCTION OF LACTIC ACID. MORTARS WERE MADE WITH THE ADDITION OF GYPSUM BY-PRODUCT, GROUND FOR 30 MINUTES IN A BALL MILL, IN PROPORTIONS OF 0%, 2.5%, 5% AND 7.5% IN RELATION TO THE CEMENT MASS AND CURED AT ROOM TEMPERATURE AND SUBMERGED. IN WATER SATURATED WITH LIME. THE COMPRESSIVE STRENGTH OF THE MORTARS IN BOTH TYPES OF CURING WAS EVALUATED, AS WELL AS MICROSTRUCTURAL ANALYSIS BY X-RAY DIFFRACTION. THE RESULTS SHOWED THAT SAMPLES SUBJECTED TO AMBIENT CURING PRESENTED GREATER RESISTANCE COMPARED TO THOSE SUBJECTED TO CURING IMMERSED IN LIME-SATURATED WATER. HOWEVER, MORTARS WITH THE ADDITION OF CALCIUM SULFATE UP TO 5% AND IMMERSED CURING SHOWED SIGNIFICANTLY HIGHER COMPRESSIVE STRENGTH THAN THE REFERENCE MORTAR. WHILE, IN AIR CURING, THE RESISTANCE SHOWED A DECREASING TREND WITH THE ADDITION OF GYPSUM. THIS INDICATES THAT THE CURING REGIME HAS A SIGNIFICANT IMPACT ON COMPRESSIVE STRENGTH, BUT DOES NOT ALTER THE TYPE OF HYDRATION PRODUCTS.
Palavras-chave
Argamassa; Subproduto de gesso; Resistência à compressão; Cura.
Mortar; Gypsum by-product; Compressive strength; Cure.
Como citar
BARROSO, LAIMARA DA SILVA;
TAVARES, KARINE MIRANDA DE SOUZA;
CHERENE, MARIANA GOMES PINTO;
BASTOS, WALQUÍRIA LEONARDO;
RIBEIRO, CAROLINA GOMES DIAS;
XAVIER, GUSTAVO DE CASTRO;
VIEIRA, CARLOS MAURÍCIO FONTES;
AZEVEDO, AFONSO RANGEL GARCEZ DE;
MONTEIRO, SÉRGIO NEVES.
EFEITO DA CURA NA RESISTÊNCIA À COMPRESSÃO DE ARGAMASSAS COM INCORPORAÇÃO DE GESSO
,
p. 1744-1751.
In: 77º Congresso Anual da ABM - Internacional,
São Paulo, Brasil,
2024.
ISSN: 2594-5327
, DOI 10.5151/2594-5327-40926