EFEITO DA TEMPERATURA DE AUSTENITIZAÇÃO NO TAMANHO DE GRÃO AUSTENÍTICO E NAS TEMPERATURAS DE INÍCIO DE TRANSFORMAÇÃO DE FASES EM UM AÇO DO TIPO TRIP780

EFFECT OF AUSTENITIZING TEMPERATURE ON AUSTENITIC GRAIN SIZE AND START TRANSFORMATION TEMPERATURES IN A TRIP780 TYPE STEEL

Autoria

Magalhaes, Charles Henrique Xavier Morais; Campos, Pablo Henrique Kelly; Faria, Geraldo Lúcio de

DOI

10.5151/2594-5327-34138

Downloads

Baixar Artigo 17 Downloads

Resumo

PARA ATENDER DEMANDAS ATUAIS DA INDÚSTRIA AUTOMOTIVA, UMA TERCEIRA GERAÇÃO DE AHSS VEM SENDO DESENVOLVIDA COMO ALTERNATIVA ÀS GERAÇÕES ANTERIORES. NESSE CENÁRIO, O AÇO DO TIPO TRIP780 É UMA LIGA ATRATIVA, POIS POSSUI COMPOSIÇÃO QUÍMICA FAVORÁVEL PARA O DESENVOLVIMENTO DE TRATAMENTOS TÉRMICOS INOVADORES, COMO OS DE TÊMPERA E PARTIÇÃO. NESSE CONTEXTO, ESTE TRABALHO SE PROPÔS A INVESTIGAR O EFEITO DA TEMPERATURA DE AUSTENITIZAÇÃO SOBRE O TAMANHO DE GRÃO AUSTENÍTICO (TGA) E NAS TEMPERATURAS CRÍTICAS DE DECOMPOSIÇÃO DA AUSTENITA POR MEIO DA EXECUÇÃO DE CICLOS TÉRMICOS DE AUSTENITIZAÇÃO COMPLETA, ENTRE 950°C E 1200°C, SEGUIDOS DE RESFRIAMENTO CONTÍNUO A 15°C/S E 200°C/S, SIMULADOS EM UM DILATÔMETRO DE TÊMPERA. COM O AUXÍLIO DE MO E MEV, AS MICROESTRUTURAS FORAM ANALISADAS E O TGA FOI MEDIDO, APRESENTANDO UMA TENDÊNCIA DE AUMENTO EXPONENCIAL COM A TEMPERATURA. AS CURVAS DILATOMÉTRICAS MOSTRARAM QUE A TEMPERATURA CRÍTICA DE INÍCIO DE DECOMPOSIÇÃO DA AUSTENITA EM FERRITA DIMINUIU À MEDIDA EM QUE SE AUMENTOU O TGA. POR FIM, CONCLUIU-SE QUE O TGA NÃO INFLUENCIOU INTRINSECAMENTE A TEMPERATURA DE INÍCIO DE FORMAÇÃO DE MARTENSITA (MS), MAS SIM EXTRINSECAMENTE, TENDO EM VISTA QUE ESSE PARÂMETRO INFLUENCIOU A FORMAÇÃO DOS CONSTITUINTES DIFUSIONAIS DURANTE O RESFRIAMENTO E, ESSES, POR SUA VEZ INFLUENCIARAM A PARTIÇÃO DE CARBONO PARA A AUSTENITA METAESTÁVEL, MODIFICANDO ASSIM AS TEMPERATURAS MS.

 

TO MEET CURRENT DEMANDS FROM THE AUTOMOTIVE INDUSTRY, A THIRD GENERATION OF AHSS HAS BEEN DEVELOPED AS AN ALTERNATIVE TO PREVIOUS GENERATIONS. IN THIS SCENARIO, TRIP780 STEEL IS AN ATTRACTIVE ALLOY, AS IT HAS A FAVORABLE CHEMICAL COMPOSITION FOR THE DEVELOPMENT OF INNOVATIVE HEAT TREATMENTS, SUCH AS QUENCHING AND PARTITIONING. IN THIS CONTEXT, THIS WORK AIMED TO INVESTIGATE THE EFFECT OF AUSTENITIZING TEMPERATURE ON AUSTENITIC GRAIN SIZE (AGS) AND ON CRITICAL AUSTENITE DECOMPOSITION TEMPERATURES THROUGH THE EXECUTION OF COMPLETE AUSTENITIZING HEAT CYCLES, BETWEEN 950°C AND 1200°C, FOLLOWED BY CONTINUOUS COOLING AT 15°C/S AND 200°C/S, SIMULATED IN A QUENCHING DILATOMETER. WITH THE AID OF OM AND SEM, THE MICROSTRUCTURES WERE ANALYZED AND AGS WAS MEASURED, SHOWING A TENDENCY TO INCREASE EXPONENTIALLY WITH TEMPERATURE INCREASE. THE DILATOMETRIC CURVES SHOWED THAT THE START CRITICAL TEMPERATURE OF AUSTENITE TO FERRITE DECOMPOSITION DECREASED AS THE AGS INCREASED. FINALLY, IT WAS CONCLUDED THAT THE AGS DID NOT INTRINSICALLY INFLUENCE THE MARTENSITE FORMATION START TEMPERATURE (MS), BUT EXTRINSICALLY DID, CONSIDERING THAT THIS PARAMETER INFLUENCED THE FORMATION OF THE DIFFUSIONAL CONSTITUENTS DURING COOLING AND, IN TURN, THESE INFLUENCED THE CARBON PARTITION TO METASTABLE AUSTENITE, THUS MODIFYING MS TEMPERATURES.

Palavras-chave

TRIP780; Tamanho de Grão Austenítico; Transformações de fase; Temperatura Ms

TRIP780; Phase Transformations; Austenitic Grain Size; Ms Temperature